Phosphor and method for producing same, and light-emitting device using same and method for manufacturing such device
View Patent ↗When a phosphor for ultraviolet excitation or visible light excitation is excited by light having wavelengths in a range of 100 to 500 nm and emission colors of the phosphor are represented by xy coordinates, the phosphor has a difference between a maximum value and a minimum value of x coordinates and a difference between a maximum value and a minimum value of y coordinates which are respectively 0.020 or less. A light-emitting device includes a light-emitting part which contains at least such a phosphor. The light-emitting part emits visible light when irradiated with ultraviolet or visible light emitted from an excitation source.
1. A testing method, comprising:
exciting a phosphor at each of the following wavelengths: 100 nm, 150 nm, 200 nm, 250 nm, 300 nm, 350 nm, 400 nm and 500 nm;
measuring emission colors of the phosphor excited at the individual wavelengths wherein the emission colors are represented by xy coordinates; and
selecting a phosphor based on the measured emission colors having a difference between a maximum value and a minimum value of the x coordinates and a difference between a maximum value and a minimum value of the y coordinates which are respectively 0.020 or less as a phosphor for use in a light-emitting device.
2. A light-emitting device, comprising:
an excitation source which emits ultraviolet or visible light; and
a light-emitting part which is excited by the ultraviolet or visible light emitted from the excitation source to emit visible light and comprising at least the phosphor selected for use in a light-emitting device by the testing method according to claim 1 .
3. The light-emitting device according to claim 2 , wherein the light-emitting part comprises the selected phosphor in a range of 70 mass% or more of all phosphors.
4. The light-emitting device according to claim 2 , wherein the light-emitting device is one selected from a fluorescent lamp, a cold cathode discharge lamp, a plasma display and an LED lamp.
5. The light-emitting device according to claim 2 , wherein the light-emitting device is a white light-emitting LED lamp.
6. The testing method according to claim 1 , wherein the phosphor is a europium-activated rare-earth oxide phosphor, a europium-activated rare-earth oxysulfide phosphor, a europium-activated rare-earth borate phosphor, a europium-activated aluminate phosphor, a europium-activated halophosphate phosphor, a manganese-activated zinc silicate phosphor, a europium and manganese-activated aluminate phosphor, a europium-activated alkaline-earth silicate phosphor, a terbium-activated rare-earth silicate phosphor, a terbium-activated rare-earth borate phosphor, or a terbium-activated rare-earth phosphate phosphor.
7. The testing method according to claim 1 , comprising:
selecting a phosphor based on the measured emission colors having a difference between a maximum value and a minimum value of the x coordinates and a difference between a maximum value and a minimum value of the y coordinates which are respectively 0.015 or less as a phosphor for use in a light-emitting device.
8. A light-emitting device, comprising:
an excitation source which emits ultraviolet or visible light; and
a light-emitting part which is excited by the ultraviolet or visible light emitted from the excitation source to emit visible light and comprising at least the phosphor selected for use in a light-emitting device by the testing method according to claim 7 .
9. A method for producing a light-emitting device, comprising:
exciting a phosphor at each of the following wavelengths: 100 nm, 150 nm, 200 nm, 250 nm, 300 nm, 350 nm, 400 nm and 500 nm;
measuring emission colors of the phosphor excited at the individual wavelengths, wherein the emission colors are represented by xy coordinates; and
based on the measured emission colors, if the phosphor has a difference between a maximum value and a minimum value of the x coordinates and a difference between a maximum value and a minimum value of the y coordinates which are respectively 0.020 or less; then
producing a light-emitting part which is excited by ultraviolet or visible light emitted from an excitation source to emit visible light using the phosphor.
10. The method for producing the light-emitting device according to claim 9 ,
wherein the light-emitting part contains the phosphor in 70 mass% or more of all phosphors.
11. The method for producing the light-emitting device according to claim 9 ,
wherein the light-emitting device is one selected from a fluorescent lamp, a cold cathode discharge lamp, a plasma display and an LED lamp.
12. The method for producing the light-emitting device according to claim 9 , wherein the light-emitting device is a white light-emitting LED lamp.
13. The method for producing the light-emitting device according to claim 9 ,
wherein the phosphor is a europium-activated rare-earth oxide phosphor, a europium-activated rare-earth oxysulfide phosphor, a europium-activated rare-earth borate phosphor, a europium-activated aluminate phosphor, a europium-activated halophosphate phosphor, a manganese-activated zinc silicate phosphor, a europium and manganese-activated aluminate phosphor, a europium-activated alkaline-earth silicate phosphor, a terbium-activated rare-earth silicate phosphor, a terbium-activated rare-earth borate phosphor, or a terbium-activated rare-earth phosphate phosphor.