Surface-treated microporous membrane and electrochemical device prepared thereby
View Patent ↗Disclosed is a porous film comprising: (a) a porous substrate having pores; and (b) a coating layer formed on at least one region selected from the group consisting of a surface of the substrate and a part of the pores present in the substrate, wherein the coating layer comprises styrene-butadiene rubber. An electrochemical device using the porous film as a separator is also disclosed. The porous film is coated with a styrene-butadiene polymer, whose rubbery characteristics can be controlled, and thus provides improved scratch resistance and adhesion to other substrates. When the porous film is used as a separator for an electrochemical device, it is possible to improve the safety of the electrochemical device and to prevent degradation in the quality of the electrochemical device.
1. A battery separator, comprising:
(a) a porous substrate having pores; and
(b) a styrene-butadiene layer formed on at least one region selected from the group consisting of a surface of the substrate and a part of the pores present in the substrate, wherein the styrene-butadiene layer comprises styrene-butadiene rubber;
wherein the porous substrate having pores is selected from the group consisting of:
(i) an organic/inorganic composite porous film, which comprises a porous film having pores, coated with a coating layer comprising a mixture of inorganic particles with a binder polymer, on a surface of the porous film and on a part of the pores present in the porous film, the inorganic particles linked and fixed among themselves by the binder polymer, and having a pore structure formed by interstitial volumes of the inorganic particles throughout the coating layer, wherein the coating layer restrains the thermal shrinkage of the porous film; and
(ii) an organic/inorganic composite porous free-standing film comprising inorganic particles and a binder polymer, the inorganic particles linked and fixed among themselves by the binder polymer, and having a pore structure formed by interstitial volumes of the inorganic particles throughout the organic/inorganic composite porous free-standing film;
wherein the inorganic particles are present in an amount of 50-99 wt % based on 100 wt % of the mixture of the inorganic particles and the binder polymer.
2. The battery separator according to claim 1 , which has a pore size of between 0.001 and 10 μm and a porosity of 10˜99%.
3. The battery separator according to claim 1 , wherein the inorganic particles further comprise inorganic particles having a dielectric constant of 5 or more.
4. The battery separator according to claim 3 , wherein the inorganic particles having a dielectric constant of 5 or more are BaTiO 3 , SrTiO 3 , SnO 2 , CeO 2 , MgO, NiO, CaO, ZnO, ZrO 2 , Y 2 O 3 , Al 2 O 3 or TiO 2 .
5. The battery separator according to claim 1 , wherein the binder polymer has a solubility parameter of between 15 and 45 MPa 1/2 .
6. The battery separator according to claim 1 , wherein the binder polymer is at least one selected from the group consisting of polyvinylidene fluoride-co-hexafluoro propylene, polyvinylidene fluoride-co-trichloroethylene, polymethylmethacrylate, polyacrylonitrile, polyvinyl pyrrolidone, polyvinyl acetate, polyethylene-co-vinyl acetate, polyethylene oxide, cellulose acetate, cellulose acetate butyrate, cellulose acetate propionate, cyanoethylpullulan, cyanoethyl polyvinyl alcohol, cyanoethylcellulose, cyanoethylsucrose, pullulan, and carboxymetyl cellulose.
7. The battery separator according to claim 1 , wherein the styrene-butadiene rubber contains a hydrophilic functional group.
8. The battery separator according to claim 3 , wherein the hydrophilic functional group forms a hydrogen bond with other substrates.
9. The battery separator according to claim 1 , wherein the styrene-butadiene rubber is obtained by polymerization of: (a) a butadiene group-containing monomer and a styrene group-containing monomer; or (b) a butadiene group-containing monomer, a styrene group-containing monomer and a hydrophilic group-containing monomer having at least one hydrophilic functional group selected from the group consisting of maleic acid, acrylic acid, acrylate, carboxylic acid, nitrile, hydroxyl, acetate, mercapto, ether, ester, amide, amine groups, and halogen atoms.
10. The battery separator according to claim 1 , wherein the styrene-butadiene rubber has an average molecular weight of 10,000˜1,000,000.
11. The battery separator according to claim 1 , wherein the styrene-butadiene layer has a thickness of 0.001˜10 μm.
12. The separator according to claim 1 , wherein the porous substrate having pores is (i) the organic/inorganic composite porous film, which comprises the porous film having pores, coated with the coating layer comprising a mixture of inorganic particles with the binder polymer, on the surface of the porous film and/or on part of the pores present in the porous film.
13. The battery separator according to claim 1 , wherein the porous substrate comprises at least one material selected from the group consisting of polyethylene terephthalate, polybutylene terephthalate, polyester, polyacetal, polyamide, polycarbonate, polyimide, polyetherether ketone, polyether sulfone, polyphenylene oxide, polyphenylene sulfidro, polyethylene naphthalene, polyethylene, polypropylene, and polyolefin.
14. The separator according to claim 1 , wherein the porous substrate having pores is (ii) the organic/inorganic composite porous free-standing film comprising inorganic particles and the binder polymer.
15. An electrochemical device comprising a cathode, an anode, a separator according to claim 1 and an electrolyte.
16. The electrochemical device according to claim 15 , which is a lithium secondary battery.