Monofilament suture and preparation method thereof
The present invention relates to a monofilament suture and a preparation method thereof, more specifically, to a novel monofilament suture wherein two polymers having identical inherent properties are spun to have a cross-sectional structure of conjugated filaments, and said cross-section has interfaces between the spun polymers. The interfaces form a discontinuous cross-section along the radial direction and are distributed continuously along the fiber axis direction, thereby offering improved knot security and applicability to a variety of medical materials, and a preparation method thereof.
1. A method for improving knot security of a monofilament suture, comprising separately melting a first polymer and a second polymer having identical chemical composition and identical inherent properties selected from melting point, density, and modulus of elasticity and spinning them into a monofilament having a cross-sectional structure of conjugated filaments, and the first polymer and the second polymer are different in melt viscosity,
wherein both the first and second polymers are bioabsorbable or non-bioabsorbable,
wherein the cross-section has a sea/islands type structure, and
wherein the difference of the melt viscosity of the first polymer and the second polymer is at least 10%.
2. The method according to claim 1 , wherein the ratio between the first polymer and the second polymer is 5:95 to 95:5 by volume.
3. The method according to claim 1 , wherein the ratio between the first polymer and the second polymer is 20:80 to 80:20 by volume.
4. The method as set forth in claim 1 , wherein the bioabsorbable polymer is a homopolymer or a copolymer comprising one or more selected from the group consisting of glycolide, glycolic acid, lactide, lactic acid, caprolactone, dioxanone, trimethylene carbonate, polyethylene glycol, polyanhydride, and polyhydroxyalkanoate.
5. The method as set forth in claim 1 , wherein the non-bioabsorbable polymer is a homopolymer or a copolymer comprising one or more selected from the group consisting of polyolefin, polyamide, polyurethane and polyvinylidene fluoride.
6. The method according to claim 1 , wherein a dye is added in the amount of 0.5 parts by weight or less on the basis of 100 parts by weight of the polymer.
7. The method according to claim 1 , wherein a dye is added in the amount of 0.5 parts by weight or less on the basis of 100 parts by weight of the polymer, the pigment content being expressed by the following equation:
0
≤
Dye
content
in
the
Sea
Dye
content
in
the
Islands
<
1.
8. The method according to claim 7 , wherein the pigment is added only to the polymer forming the islands of the sea/islands type structure.
9. The method according to claim 1 , wherein the first and second polymers are both non-bioabsorbable.