Metal components with silicon-containing protective coatings substantially free of chromium and methods of forming such protective coatings
View Patent ↗A metal component ( 10 ) with a protective coating ( 16 ) containing silicon and a process for forming such protective coatings ( 14 ). The protective coating ( 16 ) is formed by applying a silicon-containing fluid composition to the metal component ( 10 ) as a silicon-containing layer ( 12 ) and heating the silicon-containing layer ( 12 ) to a temperature exceeding 400° F.
1. A coating process for protecting a surface ( 14 ) of a substantially chromium-free metal component ( 10 ), the coating process comprising:
combining a substantially chromium-free silicon-containing fluid composition comprising a silane liquid with a dopant that is dissolvable in the silane liquid and is selected from the group consisting of yttrium, hafnium, and combinations thereof;
applying a layer ( 12 ) of the substantially chromium-free, silicon-containing fluid composition to at least a portion of the surface ( 14 );
curing the substantially chromium-fee, silicon-containing fluid composition after the layer ( 12 ) is applied to the surface ( 14 );
placing the cured substantially chromium-free, silicon-containing fluid composition in layer ( 12 ) in a non-oxidizing atmosphere before heating; and
heating the cured substantially chromium-free, silicon-containing fluid composition in layer ( 12 ) to a temperature of about 70 percent of the melting temperature of the substantially chromium-free component ( 10 ) or to the eutectic temperature of silicon and the metal constituting the substantially chromium-free metal component to form a substantially chromium-free, silicon-containing protective coating ( 16 ) on the surface ( 14 ) that includes silicon from the cured silicon-containing fluid composition and metal from the metal component ( 10 ).
2. The coating process of claim 1 wherein the substantially chromium-free metal component ( 10 ) is composed of iron, aluminum, titanium, copper, nickel, or an alloy of these materials.
3. The coating process of claim 1 wherein silicon from the cured silicon-containing fluid composition diffuses into the surface ( 14 ) to combine with the metal from the metal component ( 10 ) such that the original surface ( 14 ) is present after heating and silicon resides entirely in a diffusion zone ( 22 ).
4. A coating process for protecting a surface ( 14 ) of a substantially chromium-free metal component ( 10 ), the coating process comprising:
combining a substantially chromium-free, silicon-containing fluid composition comprising a silane liquid with a dopant that is dissolvable in the silane liquid and is selected from the group consisting of yttrium, hafnium, and combinations thereof;
applying a layer ( 12 ) of the substantially chromium-free, silicon-containing fluid composition to at least a portion of the surface ( 14 );
curing the substantially chromium-free, silicon-containing fluid composition after the layer ( 12 ) is applied to the surface ( 14 );
placing the substantially chromium-free, silicon-containing fluid composition in layer ( 12 ) in a non-oxidizing atmosphere before heating; and
heating the cured substantially chromium-free, silicon-containing fluid composition in layer ( 12 ) to a temperature greater than 400° F. to form a substantially chromium-free, silicon-containing protective coating ( 16 ) on the surface ( 14 ) that includes silicon from the cured silicon-containing fluid composition and metal from the metal component ( 10 ).
5. The coating process of claim 4 wherein the substantially chromium-free metal component ( 10 ) is composed of iron, aluminum, titanium, copper, nickel, or an alloy of these materials.
6. A coating process for protecting a metal component ( 10 ) having a surface ( 14 ) at least partially covered with hard chromium plating ( 16 ), comprising:
applying a layer ( 12 ) of a substantially chromium-free, silicon-containing fluid composition comprising a silane liquid and a dopant that is dissolvable in the silane liquid and is selected from group consisting of yttrium, hafnium, and combination thereof to at least a portion of the hard chromium plating ( 16 );
curing the substantially chromium-free, silicon-containing fluid composition after the layer ( 12 ) is applied to the hard chromium plating ( 16 ); and
heating the cured substantially chromium-free, silicon-containing fluid composition to a temperature greater than 400° F. to form a protective coating ( 16 ) on the metal component ( 10 ) that includes silicon from the cured silicon-containing fluid composition and at least one of oxygen from an ambient atmosphere communicating with the layer ( 12 ) or chromium from the hard chromium plating ( 16 ).