Flameproofed impact-strength-modified poly(ester)carbonate compositions

1. A process for producing a three-dimensional article comprising

A) melt-blending a thermoplastic composition that contains

i. 40-95 parts by weight of branched aromatic poly(ester)carbonate,

ii. 1-25 parts by weight of a graft polymer including at least one graft base selected from the group consisting of silicone rubber and silicone-acrylate rubber,

iii. 9-18 parts by weight of talc,

iv. 0.4-20 parts by weight of phosphorus-containing flameproofing agent,

v. 1-6 parts by weight of at least one inorganic boron compound selected from the group consisting of Zn 4 B 2 O 7 .H 2 O, Zn 2 B 6 O 11 .3.5H 2 O and ZnB 4 O 7 .4H 2 O, and

vi. 0-3 parts by weight of an anti-dripping agent to obtain a molten blend,

B) cooling and granulating said molten blend to obtain a plurality of granules

C) extruding said granules to produce a sheet and

D) shaping said sheet into a three-dimensional article.

2. The process according to claim 1 wherein said shaping is carried out by at least one thermoforming method selected from the group consisting of hot forming, draw forming, deep drawing and vacuum forming.

3. The process according to claim 2 wherein said shaping is carried out by deep drawing.

4. The process according to claim 1 wherein the branched poly(ester)carbonate contains at least one residue having at least one amine functionality.

5. The process according to claim 1 wherein the phosphorus-containing flameproofing agent conforms to formula (VIII)

in which

R 1 , R 2 , R 3 and R 4 independently of one another denote C 1 to C 8 alkyl, C 5 to C 6 cycloalkyl, C 6 to C 20 aryl or C 7 to C 12 aralkyl,

n independently of one another denote 0 or 1,

q is 0 to 30 and

X is a residue of an aromatic compound having 6 to 30 C atoms, or of a linear or branched aliphatic compound having 2 to 30 C atoms.

6. The process according to claim 1 wherein the thermoplastic composition contains neither thermoplastic vinyl (co)polymer nor polyalkylene terephthalate.

7. The process according to claim 1 wherein in the thermoplastic composition further contains at least one member selected from the group consisting of lubricant, mold-release agent, nucleating agent, antistatic agent, stabilizer, dyestuff, pigment, filler, and reinforcing material different from talc.

8. The three-dimensional article prepared by the process of claim 1 .

9. The composition according to claim 1 , wherein the inorganic boron compound is present in 2-4 parts by weight.

10. The composition according to claim 1 , wherein the inorganic boron compound is Zn 2 B 6 O 11 .3.5H 2 O.

11. The composition according to claim 9 , wherein the inorganic boron compound is Zn 2 B 6 O 11 .3.5H 2 O.