Interlayers for laminated safety glass with superior de-airing and laminating properties and process for making the same
View Patent ↗This invention relates to thermoplastic interlayer sheets or films for laminated safety glass with superior vacuum de-airing at elevated temperatures and superior tacking and edge sealing properties. The sheeting has an embossed surface pattern on at least one of the surfaces, which provides relatively uninterrupted channels for de-airing in at least two non-parallel directions, wherein the channels are spaced about 0.1 to about 1 mm apart and have a depth of less than about 25 μm and a width of about 30 to about 300 μm.
1. A thermoplastic interlayer sheet or film comprising an unplasticized polymer selected from the group consisting of ethylene acid copolymers and ionomers derived therefrom having at least one embossed surface having a surface pattern that provides relatively uninterrupted channels for de-airing in at least two non-parallel directions that are spaced about 0.1 to about 1 mm apart and have a depth of about 2 to less than 20 μm and a width of about 30 to about 300 μm.
2. The thermoplastic interlayer sheet or film of claim 1 , wherein the unplasticized polymer is the ethylene acid copolymer.
3. The thermoplastic interlayer sheet or film of claim 1 , wherein the unplasticized polymer is the ionomer.
4. The thermoplastic interlayer sheet or film of claim 3 , wherein the depth of the channels is about 14 to less than 20 μm.
5. The thermoplastic interlayer sheet or film of claim 4 , wherein the width of the channels is about 40 to about 250 μm.
6. The thermoplastic interlayer sheet or film of claim 3 , wherein the width of the channels is about 40 to about 250 μm.
7. The thermoplastic interlayer sheet or film of claim 1 , wherein the at least one embossed surface has a total area roughness, AR t , of less than 32 μm, a ratio of area peak height (AR p )/AR t of between 0.42 and 0.62, and an area kurtosis, AKu, of less than about 5.
8. The thermoplastic interlayer sheet or film of claim 7 , wherein the ratio of AR p /AR t is between 0.52 and 0.62.
9. The thermoplastic interlayer sheet or film of claim 7 , wherein the area kurtosis, AKu, is less than about 2.5.
10. The thermoplastic interlayer sheet or film of claim 9 , wherein the film is a film consisting essentially of ethylene acid copolymer.
11. The thermoplastic interlayer sheet or film of claim 9 , wherein the film is a film consisting essentially of ionomer.
12. The thermoplastic interlayer sheet or film of claim 11 , wherein the depth of the channels is about 14 to less than 20 μm and the width of the channels is about 40 to about 250 μm.
13. A pre-laminate comprising the thermoplastic interlayer sheet or film of claim 12 and two layers of glass on opposite sides of the thermoplastic interlayer sheet or film.
14. A process of preparing a glass laminate comprising (i) providing the pre-laminate of claim 13 ; and (ii) subjecting the pre-laminate structure to heat to bind the thermoplastic interlayer sheet to the glass layer.
15. The thermoplastic interlayer sheet or film of claim 7 , wherein the film is a film consisting essentially of ethylene acid copolymer.
16. The thermoplastic interlayer sheet or film of claim 7 , wherein the film is a film consisting essentially of ionomer.
17. The thermoplastic interlayer sheet or film of claim 1 , wherein both surfaces of the thermoplastic interlayer sheet or film comprises an embossed surface pattern that provides relatively uninterrupted channels for de-airing in at least two non-parallel directions and wherein the channels are spaced about 0.1 to 1 mm apart and have a depth of about 2 to less than 20 μm and a width of about 30 to 300 μm.
18. A pre-laminate comprising the thermoplastic interlayer sheet or film of claim 1 and a glass layer.
19. The pre-laminate of claim 18 , which comprises two layers of glass on opposite sides of the thermoplastic interlayer sheet or film.
20. A process of preparing a glass laminate comprising (i) providing the pre-laminate of claim 18 ; and (ii) subjecting the pre-laminate structure to heat to bind the thermoplastic interlayer sheet to the glass layer.
21. The process of claim 20 , wherein the film is a film consisting essentially of ionomer and the ionomer is derived from an ethylene-methacrylic acid copolymer.
22. The thermoplastic interlayer sheet or film of claim 1 , wherein the film is a film consisting essentially of ionomer and the ionomer is derived from an ethylene-methacrylic acid copolymer.