Composition and method for making a proppant
View Patent ↗The present invention relates to proppants which can be used to prop open subterranean formation fractions. Proppant formulations are further disclosed which use one or more proppants of the present invention. Methods to prop open subterranean formation fractions are further disclosed. In addition, other uses for the proppants of the present invention are further disclosed, as well as methods of making the proppants.
1. A method of forming a proppant, comprising providing a template sphere wherein said template sphere has one or more flaws on the surface of the template sphere;
removing or diminishing said one or more flaws with one or more chemical treatments, one or more mechanical treatments, one or more thermal treatments, one or more spark discharge treatments, or any combination thereof;
providing a shell around the entire outer surface of said template sphere after said removal or diminishing of one or more flaws, and then sintering said shell to form a continuous sintered shell.
2. The method of claim 1 , wherein said chemical treatment is used and comprises treating said template sphere with a chemical that dissolves or otherwise reacts with one or more parts of the surface of the template sphere to remove or reduce said one or more flaws.
3. The method of claim 1 , wherein said chemical treatment is used and comprises the preferential dissolution of one or more species contained in and/or on the template sphere.
4. The method of claim 3 , wherein said one or more species is silica, such that said chemical treatment reduces the overall silica content.
5. The method of claim 2 , wherein said chemical treatment comprises the application of sodium hydroxide, potassium hydroxide, calcium hydroxide, one or more acids, or any combination thereof to the surface of the template sphere.
6. The method of claim 1 , wherein said mechanical treatment is used.
7. The method of claim 6 , wherein said mechanical treatment comprises tumbling, tumbling in the presence of abrasive material, impingement, or any combination thereof.
8. The method of claim 1 , wherein said thermal treatment is used and comprises a furnace, injection into a high temperature plasma flame, or other high temperature flames.
9. The method of claim 8 , wherein said thermal treatment is conducted in the presence of reduced pressure or increased pressure relative to ambient pressure.
10. The method of claim 8 , wherein during said thermal treatment, an active phase is present in order to react with one or more phases in the template sphere.
11. The method of claim 1 , wherein said template sphere after removing or diminishing one or more flaws, has an aspect ratio of 5 or less.
12. The method of claim 1 , wherein said template sphere after removing or diminishing one or more flaws, has an aspect ratio of 0.1 to 4.
13. The method of claim 1 , wherein said template sphere after removing or diminishing one or more flaws, has an aspect ratio of 0.5 to 1.3.
14. The method of claim 1 , wherein after removing or diminishing one or more flaws, the template sphere has a radius of curvature of from 0.5 microns to 100 microns.
15. The method of claim 1 , wherein after removing or diminishing said one or more flaws, the overall surface area of the template sphere is reduced from 1% to 10% compared to the template sphere prior to the surface treatment.
16. A method of forming a proppant comprising providing a template sphere and forming a shell around the entire outer surface of said template sphere by a direct particle deposition from a slurry containing precursor particles that form the shell or coating and then drying or sintering said shell to form a continuous sintered shell.
17. The method of claim 16 , wherein one or more sacrificial monolayers are first applied to the template sphere to induce covalent bonding or other attachment mechanisms between the surface of the template and the particles in suspension that form said shell.
18. A method of forming a proppant comprising providing a template sphere and forming a shell around the entire outer surface of said template sphere by direct nucleation and deposition of species onto the template sphere.
19. The method of claim 18 , wherein said direct nucleation and deposition comprises a precipitation reaction.
20. The method of claim 19 , wherein said precipitation reaction used to form said shell is accomplished through the adjustment of the pH of a solution that contains said template sphere, adjustment of temperature, adjustment of pressure, or any combination thereof.