Water-in-oil emulsion composition for forming silicone elastomer porous material

1. A method of preparing a silicone elastomer porous material, comprising:

providing a water-in-oil emulsion comprising a liquid silicone rubber material which forms a silicone elastomer upon curing, a silicone oil material which has a surface activation function, and water droplets dispersed in the liquid silicone rubber material;

subjecting the emulsion to a primary heating, thereby curing the liquid silicone rubber material to form a silicone elastomer and confining the water droplets within the silicone elastomer substantially as they are present in the emulsion; and

subjecting the silicone elastomer confining the water droplets therein to a secondary heating, thereby evaporating and removing the water droplets from the silicone elastomer, thereby forming the silicone elastomer porous material;

wherein the silicone oil material has a hydrophilic group; and

wherein the silicone oil material comprises a mixture of a first ether-modified silicone oil and a second ether-modified silicone oil, and a difference in HLB value between the first ether-modified silicone oil and the second ether-modified silicone oil is at least 3.

2. The method according to claim 1 , wherein the primary heating is carried out at 80 to 130° C. for about 5 to 60 minutes.

3. The method according to claim 2 , wherein the secondary heating is carried out at 70 to 300° C. for about 1 to 24 hours.

4. The method according to claim 1 , wherein the liquid silicone rubber material is an addition reaction curing one.

5. The method according to claim 4 , wherein the liquid silicone rubber material includes a polysiloxane having an unsaturated aliphatic group and a polysiloxane having active hydrogen.

6. The method according to claim 5 , wherein the unsaturated aliphatic group is a vinyl group.

7. The method according to claim 1 , wherein the first ether-modified silicone oil has an HLB value of 7 to 11 and the second ether-modified silicone oil has an HLB value of 4 to 7.

8. The method according to claim 1 , wherein the emulsion composition comprises 100 parts by weight of the liquid silicone rubber material, 0.2 to 5.5 parts by weight of the silicone oil material, and 10 to 250 parts by weight of the water droplets.

9. The method according to claim 1 , wherein the emulsion composition comprises 100 parts by weight of the liquid silicone rubber material, 0.15 to 3.5 parts by weight of the first silicone oil, 0.05 to 2 parts by weight of the second silicone oil, and 10 to 250 parts by weight of the water droplets.

10. The method according to claim 1 , comprising 100 parts by weight of the liquid silicone rubber material, 0.15 to 3.5 parts by weight of the first ether-modified silicone oil, 0.05 to 2 parts by weight of the second ether-modified silicone oil, and 10 to 250 parts by weight of the water droplets.

11. The method according to claim 1 , wherein the water droplets has an average diameter of 1 to 50 μm.