Elastomeric emulsion polymers for masonry coatings
View Patent ↗Acrylate latexes are described which provide properties of good balance of moderate elongation, low dirt pick up, alkaline resistance, UV light resistance, and efflorescence resistance for masonry coatings. These latexes have a large portion of repeating units from C8-C12 alcohol esters of acrylic acid and/or vinyl versatates along with 5-15 weight percent of repeating units from acrylonitrile. They have a glass transition temperature of −50 to +10° C.
1. A coated masonry object comprising:
a) a masonry substrate; and
b) an elastomeric coating comprising a polymer from the polymerization of about 30 to 85 weight percent repeating units selected from C8 to C12 alkyl acrylate or vinyl esters of C10-C12 versatic acid monomers, from about 5 to 15 weight percent repeating units from acrylonitrile, less than 5 weight percent repeating units having mono or polycarboxylic acids, and from 0 to 65 weight percent repeating units from other copolymerizable monomers, wherein said polymer has a glass transition temperature of from −40 to about +10° C.
2. A coated masonry object according to claim 1 , where said 30 to 85 weight percent repeating units are from C8-C12 alkyl acrylates.
3. A coated masonry object according to claim 1 , wherein said elastomeric coating further comprises a UV activated species that promotes crosslinking of said elastomeric coating after film formation.
4. A coated masonry object according to claim 3 , wherein said UV activated species comprises a photosensitive benzophenone group in an amount from about 0.01 to 2.0 wt.%.
5. A coated masonry object according to claim 1 , wherein said elastomeric coating further comprises a silane coupling agent.
6. A coated masonry object according to claim 5 , wherein said silane coupling agent includes at least one hydroxyl group or hydrolyzable alkoxy group and at least one group with a carbon to carbon double bond.
7. A coated masonry object according to claim 1 , wherein said polymer comprises less than 5 weight percent styrene and other aromatic group containing monomers.
8. A coated masonry object according to claim 1 , wherein said polymer comprises about 7 to 13 weight percent acrylonitrile.
9. A coated masonry object according to claim 1 , wherein said polymer has a glass transition temperature from about −40 to 0° C.
10. A coated masonry object according to claim 1 , wherein said polymer comprises at least 80 weight percent of the total binder in said elastomeric coating.