Aluminum alloy products having improved property combinations and method for artificially aging same
View Patent ↗Aluminum alloy products about 4 inches thick or less that possesses the ability to achieve, when solution heat treated, quenched, and artificially aged, and in parts made from the products, an improved combination of strength, fracture toughness and corrosion resistance, the alloy consisting essentially of: about 6.8 to about 8.5 wt. % Zn, about 1.5 to about 2.00 wt. % Mg, about 1.75 to about 2.3 wt. % Cu; about 0.05 to about 0.3 wt. % Zr, less than about 0.1 wt. % Mn, less than about 0.05 wt. % Cr, the balance Al, incidental elements and impurities and a method for making same. The invention alloy is useful in making structural members for commercial airplanes including, but not limited to, upper wing skins and stringers, spar caps, spar webs and ribs of either built-up or integral construction. The invention alloy may be aged by 2 or 3 step practices while exceeding the SCC requirements for applications for which the invention alloy is primarily intended. The flexibility of the invention in this regard is useful for its application in multi-alloy or multi-material systems joined by welding or bonding and subsequently aged.
1. An aluminum alloy plate product having a thickness of less than about 2.5 inches, the alloy consisting essentially of from 7.64 to 7.7 wt. % Zn, from 1.62 to 1.65 wt. % Mg, from 1.81 to 2.15 wt. % Cu; from 0.05 to 0.3 wt. % Zr, less than 0.1 wt. % Mn, less than 0.05 wt. % Cr, the balance being aluminum, incidental elements and impurities;
wherein the plate realizes a combination of strength and toughness that satisfies the expression FT≧4.0*(TYS)+453;
where TYS is the longitudinal tensile yield strength in ksi as measured in accordance with ASTM E8 and ASTM B557; and
where FT is the LT plane stress fracture toughness (K app ) of the plate in ksi√in, where FT is measured in accordance with ASTM Standard E561 and B646 on a center-cracked aluminum alloy specimen taken from the T/2 location of an aluminum alloy plate, where the specimen has a width of 16 inches, a thickness of 0.25 inch and a initial fatigue pre-crack length of 4 inches.
2. The alloy product of claim 1 , having an EXCO corrosion resistance rating of “EB” or better.
3. The alloy product of claim 1 , wherein the product is an aerospace structural component.
4. The alloy product of claim 1 , wherein the alloy product is a fuselage component.
5. The alloy product of claim 1 , wherein the alloy product is an armor component.
6. The alloy product of claim 2 , wherein the plate realizes a FT of at least about 100 ksi√inch and a TYS of at least about 80 ksi.
7. The alloy product of claim 6 , wherein the plate has a thickness of about 1 inch.