Solvent free aqueous polyurethane dispersions and adhesive films therefrom for stretch fabrics
View Patent ↗Novel aqueous polyurethane dispersions and adhesive films formed therefrom are provided. The aqueous polyurethane dispersions are provided in solvent-free systems of a prepolymer comprising at least one polyether or polyester polyol, a mixture of MDI isomers, and a diol. The adhesive films from such dispersions can be heat-activated for bonding, lamination, and adhesion of textile fabrics, including stretch fabrics.
1. An aqueous polyurethane dispersion, comprising:
a prepolymer, which comprises:
a) at least one polyether or polyester polyol, wherein said polyether or polyester polyol has a number average molecular weight of about 600 to about 3,500;
b) a mixture of 4,4′- and 2,4′-methylene bis(phenyl isocyanate) (MDI) isomers, wherein the ratio of 4,4′-MDI to 2,4′-MDI isomers ranges from about 65:35 to about 35:65; and
c) at least one diol compound comprising: (i) hydroxy groups capable of reacting with the mixture of MDI isomers of component b) and (ii) at least one carboxylic acid group capable of forming a salt upon neutralization, wherein said at least one carboxylic acid group is incapable of reacting with the mixture of MDI isomers of component b); wherein the aqueous polyurethane dispersion is a substantially solvent-free system that further comprises:
d) at least one neutralizing agent to form an ionic salt with the at least one diol compound; and
e) at least one monofunctional dialkyl amine compound as a blocking agent for isocyanate groups; and
further comprising at least one surface active agent; at least one antifoam agent at least one rheological modifier; at least one diamine chain extension component, and
at least one polymeric component selected from the group consisting of polyethylenimine dendrimers, poly(vinylamine) dendrimers, poly(allylamine) dendrimers, and poly(amidoamine) dendrimers, with at least three or more primary and/or secondary amino groups per mole of the polymer.
2. The aqueous polyurethane dispersion of claim 1 , wherein the at least one diamine chain extension component is selected from the group consisting of 1,2-ethylenediamine, 1,4-butanediamine, 1,6-hexamethylenediamine, 1,12-dodecanediamine, 1,2-propanediamine, 2-methyl-1,5-pentanediamine, 1,2-cyclohexanediamine, 1,4-cyclohexanediamine, 4,4′-methylene-bis(cyclohexylamine), isophorone diamine, 2,2-dimethyl-1,3-propanediamine, and metatetramethylxylenediamine.
3. The aqueous polyurethane dispersion of claim 1 , further comprising at least one additional component selected from the group consisting of anti-oxidants, UV stabilizers, colorants, pigments, crosslinking agents, phase change materials, antimicrobials, minerals, microencapsulated well-being additives, nanoparticles, calcium carbonate, flame retardants, antitack additives, chlorine degradation additives, and dye-assist agents.
4. An adhesive film or tape, comprising:
a substantially solvent-free aqueous polyurethane dispersion of:
(1) a prepolymer, which comprises:
a) at least one polyether or polyester polyol, wherein said polyether or polyester polyol has a number average molecular weight of about 600 to about 3,500;
b) a mixture of 4,4′- and 2,4′-methylene bis(phenyl isocyanate) (MDI) isomers, wherein the ratio of 4,4′-MDI to 2,4′-MDI isomers ranges from about 65:35 to about 35:65; and
c) at least one diol compound comprising: (i) hydroxy groups capable of reacting with the mixture of MDI isomers of component b) and (ii) at least one carboxylic acid group capable of forming a salt upon neutralization, wherein said at least one carboxylic acid group is incapable of reacting with the mixture of MDI isomers of component b);
(2) at least one neutralizing agent to form an ionic salt with the at least one diol compound: and
(3) at least one monofunctional dialkyl amine compound as a blocking agent for isocyanate groups;
wherein the substantially solvent-free aqueous polyurethane dispersion further comprises at least one surface active agent, at least one antifoam agent; at least one rheological modifier; at least one diamine chain extension component, and at least one polymeric component selected from the group consisting of polyethylenimine dendrimers, poly(vinylamine) dendrimers, poly(allylamine) dendrimers, and poly(amidoamine) dendrimers, with at least three or more primary and/or secondary amino groups per mole of the polymer.
5. The adhesive film or tape of claim 4 , wherein the at least one diamine chain extension component is selected from the group consisting of 1,2-ethylenediamine, 1,4-butanediamine, 1,6-hexamethylenediamine, 1,12-dodecanediamine, 1,2-propanediamine, 2-methyl-1,5-pentanediamine, 1,2-cyclohexanediamine, 1,4-cyclohexanediamine, 4,4′-methylene-bis(cyclohexylamine), isophorone diamine, 2,2-dimethyl-1,3-propanediamine, and metatetramethylxylenediamine.
6. The adhesive film or tape of claim 4 , wherein the substantially solvent-free aqueous polyurethane dispersion further comprises at least one additional component selected from the group consisting of anti-oxidants, UV stabilizers, colorants, pigments, cross linking agents, phase change materials, antimicrobials, minerals, microencapsulated well-being additives, nanoparticles, calcium carbonate, flame retardants, antitack additives, chlorine degradation additives, and dye-assist agents.