Ni-base wear and corrosion resistant alloy
View Patent ↗Nickel base alloys for use in applications for highly corrosive and abrasive environments. The alloys contain a large volume fraction of metallic carbide particles that provide wear and abrasion resistance. The alloys are produced by induction melting and gas atomization to form alloy powder particles. The particles are consolidated by hot isostatic pressing to form a solid article.
1. A nickel based wear and corrosion resistant alloy consisting essentially of in weight percent:
carbon—2%-5.5%; chromium—16%-22.5%; vanadium—10%-20%; molybdenum—8%-13%; cobalt—6%-12%; titanium—2.5%-5%; aluminum—1%-2.5%; zirconium—up to 1.5%; silicon—up to 0.5%; and balance essentially nickel and incidental impurities.
2. A nickel based wear and corrosion resistant alloy consisting essentially of in weight percent:
carbon—4%-5%; chromium—20%-23%; vanadium—12%-15%; molybdenum—10%-12.5%; cobalt—6.5%-8.0%; titanium—4%-6%; aluminum—1.5%-2.5%; zirconium—up to 1.2%; silicon—up to 0.5%; and balance essentially nickel and incidental impurities.
3. A nickel based wear and corrosion resistant alloy consisting essentially of in weight percent:
carbon—5%-6%; chromium—19%-21%; vanadium—18%-20%; molybdenum—8.5%-10.5%; cobalt—6%-8%; titanium—4%-5%; aluminum—1.5%-2.5%; zirconium—up to 2%; silicon—up to 0.5%; and balance essentially nickel and incidental impurities.
4. A nickel based wear and corrosion resistant alloy consisting essentially of in weight percent:
carbon—2%-3%; chromium—17%-19%; vanadium—11%-13%; molybdenum—8%-10%; cobalt—9%-11%; titanium—2.5%-4%; aluminum—1%-2%; zirconium—up to 0.5%; silicon—up to 0.5%; and balance essentially nickel and incidental impurities.
5. A nickel based wear and corrosion resistant alloy consisting essentially of in weight percent:
carbon—2.5%-3.5%; chromium—15.5%-18%; vanadium—14%-16%; molybdenum—8%-10%; cobalt—8%-10%; titanium—2.5%-4%; aluminum—1%-2%; zirconium—up to 0.5%; silicon—up to 0.5%; and balance essentially nickel and incidental impurities.
6. A nickel based wear and corrosion resistant alloy consisting essentially of in weight percent:
carbon—3.25%-4.25%; chromium—21%-23%; vanadium—14%-16%; molybdenum—11%-13%; cobalt—7%-9%; titanium—3%-4%; aluminum—1%-2%; zirconium—up to 0.5%; silicon—up to 0.5%; and balance essentially nickel and incidental impurities.
7. A nickel based wear and corrosion resistant alloy consisting essentially of in weight percent:
carbon—2%-3%; chromium—19%-21%; vanadium—11%-13%; molybdenum—11%-12%; cobalt—10%-12%; titanium—2.5%-4%; aluminum—1%-2%; zirconium—up to 0.5%; silicon—up to 0.5%; and balance essentially nickel and incidental impurities.
8. A nickel based wear and corrosion resistant alloy consisting essentially of in weight percent:
carbon—2.25%-3.25%; chromium—19%-21%; vanadium—12%-14%; molybdenum—11%-13%; cobalt—9%-11%; titanium—3%-4.5%; aluminum—1%-2%; zirconium—up to 0.5%; silicon—up to 0.5%; and balance essentially nickel and incidental impurities.