Antimicrobial cementitious composition, method and article

1. A pre-cured antimicrobial cementitious composition, comprising:

a cement-based compound; and

a first antimicrobial agent consisting essentially of a salt of an imazalil agent present in an amount of from about 250 ppm to about 4000 ppm based on the weight of the cement-based compound.

2. The composition of claim 1 wherein the first antimicrobial agent is present in an amount from about 750 ppm to about 3000 ppm based on the weight of the cement-based compound.

3. The composition of claim 1 wherein the pre-cured composition is a cement premix, concrete premix, mortar premix, grout premix, or stucco premix.

4. The composition of claim 1 wherein the antimicrobial cementitious composition further includes a second antimicrobial agent selected from the group consisting of an orthophenyl phenol, an an orthophenyl phenol salt, a tolyl diiodomethyl sulfone, a zinc pyrithione, an oxathiazine, an azole, a chlorothalonil, and a triazine diamine.

5. A method of making a pre-cured antimicrobial cementitious composition, comprising:

combining a quantity of a first antimicrobial agent consisting essentially of a salt of an imazalil agent with a quantity of a pre-cured cement-based compound to form a pre-cured cementitious composition;

wherein the weight concentration of first antimicrobial agent in the cementitious composition is from at least about 250 ppm to about 4000 ppm based upon the weight of the pre-cured cement-based compound.

6. The method of claim 5 wherein the first antimicrobial agent is combined in an amount from 500 ppm.

7. The method of claim 5 wherein the pre-cured antimicrobial cementitious composition is a cement mix, a concrete mix, a mortar mix, a grout mix, or a stucco mix.

8. The method of claim 5 , further comprising:

combining with a quantity of a pre-cured cement-based compound a second antimicrobial agent selected from the group consisting of an orthophenyl phenol, an an orthophenyl phenol salt, a tolyl diiodomethyl sulfone, a zinc pyrithione, an oxathiazine, an azole, a chlorothalonil, and a triazine diamine.

9. A method for making a cured antimicrobial cementitious article, comprising:

affixing a pre-cured antimicrobial cementitious composition to a substrate, wherein the pre-cured antimicrobial cementitious composition includes:

a cement-based compound, and

first antimicrobial agent consisting essentially of a salt of an imazalil agent,

wherein the first antimicrobial agent is present in the pre-cured antimicrobial cementitious composition at a concentration of at least about 250 ppm to about 4000 ppm based on the weight of the cement-based compound; and

curing the affixed antimicrobial cementitious composition.

10. The method of claim 9 wherein the first antimicrobial agent is present in an amount from 500 ppm.

11. The method of claim 9 wherein the pre-cured antimicrobial cementitious composition is a cement mix, a concrete mix, a mortar mix, a grout mix, or a stucco mix.

12. The method of claim 9 wherein the antimicrobial cementitious composition further includes a second antimicrobial agent selected from the group consisting of an orthophenyl phenol, an an orthophenyl phenol salt, a tolyl diiodomethyl sulfone, a zinc pyrithione, an oxathiazine, an azole, a chlorothalonil, and a triazine diamine.

13. A method for making an antimicrobial solid cementitious article, comprising:

affixing an antimicrobial cementitious composition to a substrate, said antimicrobial cementitious composition including a salt of an imazalil agent present in an amount of from at least about 500 ppm to about 4000 ppm based on the weight of the cementitious composition; and

dehydrating said affixed composition.

14. The method of claim 13 wherein the salt of an imazalil agent is present in an amount from about 750 ppm to about 2000 ppm based on the weight of the cement-based compound.

15. The method of claim 13 wherein the cementitious composition is stucco.

16. The method of claim 13 wherein the antimicrobial cementitious composition further includes an antimicrobial agent selected from the group consisting of a tolyl diiodomethyl sulfone, a zinc pyrithione, an oxathiazine, a chlorothalonil, and a triazine diamine.

17. The method of claim 13 wherein the antimicrobial cementitious composition is selected from the group consisting of a concrete composition, a mortar composition, a grout composition, and a stucco composition.

18. The method of claim 13 wherein the antimicrobial cementitious composition is in a liquid state.

19. The method of claim 13 wherein the substrate is a substantially vertically oriented substrate.