METHOD OF SEPARATING A POLYMER FROM A SOLVENT
The present invention provides a method of separating a polymer from a solvent comprising introducing a superheated polymer-solvent mixture into an extruder, and isolating a polymer product, said extruder being equipped with at least one vent operated at subatmospheric pressure and at least one vent operated at about atmospheric pressure, said extruder having a screw diameter D, said extruder being operated at a feed rate FR and at a screw speed RPM such that a devolatilization performance ratio (DPR) given by Equation (I) DPR=FR /RPM Equation (I) is selected from a predetermined set of devolatilization performance ratios which correlate with a target characteristic of the polymer product.
1 . A method of separating a polymer from a solvent, said method comprising:
introducing a superheated polymer-solvent mixture into an extruder, and isolating a polymer product, said extruder being equipped with at least one vent operated at subatmospheric pressure and at least one vent operated at about atmospheric pressure, said extruder having a screw diameter D, said extruder being operated at a feed rate FR and at a screw speed RPM such that a devolatilization performance ratio (DPR) given by Equation (I)
DPR=FR /RPM Equation (I)
is selected from a predetermined set of devolatilization performance ratios which correlate with a target characteristic of the polymer product.
2 . The method according to claim 1 , wherein the characteristic of the polymer product is a concentration of residual solvent.
3 . The method according to claim 1 , wherein the characteristic of the polymer product is a concentration of residual monomer.
4 . The method according to claim 1 , wherein the characteristic of the polymer product is a molecular weight.
5 . The method according to claim 1 , wherein the polymer product is selected from the group consisting of polyetherimides, polyethersulfones, polycarbonates, and mixtures of two or more of the foregoing polymers.
6 . The method according to claim 1 , wherein the polymer product is a polyetherimide, the characteristic of the polymer product is a concentration of residual orthodichlorobenzene solvent, D is from about 10 to 30 millimeters.
7 . The method according to claim 1 , wherein the polymer product is a polyetherimide, the characteristic of the polymer product is a concentration of residual orthodichlorobenzene solvent, D is in a range from about 30 millimeters to about 60 millimeters.
8 . The method according to claim 1 , wherein the polymer product is a polyetherimide, the characteristic of the polymer product is a concentration of residual orthodichlorobenzene solvent, D is in a range from about 60 millimeters to about 140 millimeters.
9 . The method according to claim 1 , wherein the polymer product is a polyetherimide, the characteristic of the polymer product is a concentration of residual orthodichlorobenzene solvent, D is from about 140 millimeters to about 380 millimeters.
10 . The method according to claim 1 , wherein the superheated polymer-solvent mixture has a temperature of about 2° C. to about 200° C. higher than the boiling point of the solvent at atmospheric pressure.
11 . The method according to claim 1 , wherein the polymer-solvent mixture comprises less than or equal to about 35 percent by weight polymer based on a total weight of the polymer and the solvent.
12 . The method according to claim 1 , wherein the extruder further comprises at least one side feeder wherein the side feeder comprises a vent operated at about 400 millimeter of mercury of absolute pressure or greater.
13 . The method according to claim 1 , wherein the extruder is a twin-screw counter-rotating extruder, a twin-screw co-rotating extruder, a single-screw extruder, or a single-screw reciprocating extruder.
14 . The method according to claim 1 , wherein the extruder is a twin-screw, co-rotating intermeshing extruder.
15 . The method according to claim 1 , wherein the solvent is a halogenated aromatic solvent, a halogenated aliphatic solvent, a non-halogenated aromatic solvent, a non-halogenated aliphatic solvent, or a mixture containing at least two of the foregoing solvents.
16 . A method of separating a polyetherimide from a solvent, said method comprising:
introducing a superheated polymer-solvent mixture comprising a polyetherimide and a solvent into an extruder, and isolating a polyetherimide product, said solvent comprising at least 25 percent by weight of the polymer-solvent mixture, said extruder being equipped with at least one vent operated at subatmospheric pressure and at least one vent operated at about atmospheric pressure, said extruder having a screw diameter D, said extruder being operated at a feed rate FR and at a screw speed RPM such that a devolatilization performance ratio (DPR) given by Equation (I)
DPR=FR /RPM Equation (I)
is selected from a predetermined set of devolatilization performance ratios which correlate with a characteristic of the polyetherimide product, wherein said characteristic of the polyetherimide product is a concentration of solvent of less than 20 parts per million.
17 . The method according to claim 16 , wherein said polyetherimide product comprises less than 200 parts per million residual monomer.
18 . The method according to claim 16 , wherein said product polyetherimide has a number average molecular weight of at least 10,000 grams per mole.
19 . A method of separating a polymer from a solvent, said method comprising:
introducing a superheated polymer-solvent mixture into an extruder, and isolating a polymer product, said extruder being equipped with at least one vent operated at subatmospheric pressure and at least one vent operated at about atmospheric pressure, said extruder having a screw diameter D in a range from about 130 to about 380 millimeters, said extruder being operated at a feed rate FR and at a screw speed RPM such that a devolatilization performance ratio (DPR) given by Equation (I)
DPR=FR /RPM Equation (I)
is selected from a predetermined set of devolatilization performance ratios which correlate with a characteristic of the polymer product.
20 . The method according to claim 1 , wherein said polymer product is a polyetherimide having a number average molecular weight of at least 10,000 grams per mole.