MONITORING A COATING APPLIED TO A METAL SURFACE
A method of monitoring a coating applied to a metal surface is disclosed. Specifically, the method comprises the following: applying a sol composition to a metal surface, wherein said composition contains one or more alkoxysilyl group containing compounds, a fluorophore, and a solvent; forming a gelled coating on said surface from said composition; measuring the fluorescence of said coating with a fluorometer, wherein said fluorometer is capable of measuring reflective fluorescence emission measurements; correlating the fluorescence of said coating with the thickness or weight of said coating, and/or with the concentration of alkoxysilyl group containing compound in the coating composition; and optionally applying an additional coating to said metal surface when the thickness of the coating is less than a desired amount or adjusting the concentration of the alkoxysilyl group containing compound applied to said surface.
1 . A method of monitoring a coating applied to a metal surface comprising:
a. applying a sol composition to a metal surface, wherein said composition contains one or more alkoxysilyl group containing compounds, a fluorophore, and a solvent;
b. forming a gelled coating on said surface from said composition;
c. measuring the fluorescence of said coating with a fluorometer, wherein said fluorometer is capable of measuring reflective fluorescence emission measurements;
d. correlating the fluorescence of said coating with the thickness or weight of said coating, and/or with the concentration of alkoxysilyl group containing compound in the coating composition; and
e. optionally applying an additional coating to said metal surface when the thickness of the coating is less than a desired amount or adjusting the concentration of the alkoxysilyl group containing compound applied to said surface.
2 . The method of claim 1 wherein said composition contains at least 0.1% by weight of said alkoxysilyl group containing compound relative to the composition.
3 . The method of claim 1 wherein said composition contains from about 20 ppb to 20,000 ppm of said fluorophore, relative to alkoxysilyl group containing compound by weight
4 . The method of claim 1 wherein said composition contains from about 10 ppm to about 1000 ppm of said fluorophore, relative to the alkoxylsilyl group containing compound by weight.
5 . The method of claim 1 wherein said metal contains at least one of the following: aluminum, tin, steel, zinc, titanium, nickel, copper, alloys thereof, and a combination thereof.
6 . The method of claim 1 wherein said alkoxysilyl group compound comprises a monfunctional silane or multifunctional silane.
7 . The method of claim 6 wherein said compound is monomeric or polymeric.
8 . The method of claim 6 wherein said compound is hydrolyzed or unhydrolyzed.
9 . The method of claim 1 wherein said fluorophore is selected from the group consisting of: pyrenetetrasulfonate, fluorescein, rhodamine, and derivatives thereof.