Slip-cling stretch film
View Patent ↗A multilayer stretch film having a high slip surface and an aggressive cling surface for wrapping items or loads for ease of transport is disclosed. In one embodiment, there is disclosed a multilayer film comprises a first surface having a coefficient of friction at least less than about 0.9, comprising at least polypropylene and high density polyethylene, a second surface having a cling force to the first surface at least greater than about 5 g/in, comprising at least ethylene methyl acrylate copolymer and a tackifier resin, and a core layer, positioned between the first surface and the second surface, comprising at least linear low density polyethylene or its blend.
1. A multilayer film comprising:
a slip layer comprising at least polypropylene and high density polyethylene blend;
a cling layer comprising at least ethylene methyl acrylate copolymer and a tackifier; and an intermediary layer comprising at least linear low density polyethylene resin or its blend
wherein the intermediary layer comprises about 68% by weight linear low density polyethylene, about 30% by weight metallocene polyethylene resin, and about 2% by weight titanium dioxide.
2. The multilayer film of claim 1 , wherein the slip comprises about 5% to about 20% by weight, the cling layer comprises about 5% to about 20% by weight, and the intermediary layer comprises about 60% to about 90% by weight.
3. The multilayer film of claim 2 , wherein the slip layer comprises about 15% by weight, the cling layer comprises about 10% by weight, and the intermediary layer comprises about 75% by weight.
4. The multilayer film of claim 1 , wherein the slip layer has a coefficient of friction between about 0.3 to about 0.9, and wherein the cling layer has a cling force to the slip layer between about 5 g/in to about 80 g/in.
5. The multilayer film of claim 4 , wherein the slip layer has a coefficient of friction of about 0.5, and wherein the cling layer has a cling force to the slip layer of about 40 g/in.
6. The multilayer film of claim 1 , wherein the slip layer comprises between about 80% and about 99% by weight polypropylene and between about 1% to about 20% by weight high density polyethylene.
7. The multilayer film of claim 6 , wherein slip layer comprises about 90% by weight polypropylene and about 10% by weight high density polyethylene.
8. The multilayer film of claim 1 , wherein the cling layer comprises between about 80% and 99% by weight ethylene methyl acrylate copolymer and between about 1% to about 20% by weight tackifier resin.
9. The multilayer film of claim 8 , wherein the cling layer comprises about 95% by weight ethylene methyl acrylate and about 5% by weight tackifier resin.
10. The multilayer film of claim 1 , wherein the multilayer film can withstand a force stretch of the film to about 600% at about 5000 psi.
11. The multilayer film of claim 1 , wherein the overall multilayer film thickness is between about 0.012 mm to about 0.125 mm.
12. The multilayer film of claim 11 , wherein the overall multilayer film thickness is about 0.025 mm.
13. A multilayer film comprising:
a first surface layer having a coefficient of friction less than about 0.9, comprising at least polypropylene and high density polyethylene;
a second surface layer having a cling force to the first surface greater than about 5 g/in, comprising at least ethylene methyl acrylate copolymer and a tackifier resin; and
a core layer, positioned between the first surface and the second surface, comprising at least linear low density polyethylene resin
wherein the core layer comprises about 68% by weight linear low density polyethylene resin, about 30% by weight a metallocene polyethylene resin, and about 2% by weight titanium dioxide.
14. The multilayer film of claim 13 , wherein the coefficient of friction of the first surface layer is about 0.5, and wherein the cling force of the second surface layer to the first surface layer is about 40 g/in.
15. The multilayer film of claim 13 , wherein the first surface layer comprises between about 5% to about 20% by weight, the second surface layer comprises between about 5% to about 20% by weight, and the core layer comprises between about 60% to about 90% by weight.
16. The multilayer film of claim 15 , wherein the first surface layer comprises about 15% by weight, the second surface layer comprises about 10% by weight, and the core layer comprises about 75% by weight.
17. The multilayer film of claim 13 , wherein the first surface layer comprises between about 80% and about 99% by weight polypropylene and between about 1% to about 20% by weight high density polyethylene.
18. The multilayer film of claim 17 , wherein first surface layer comprises about 90% by weight polypropylene and about 10% by weight high density polyethylene.
19. The multilayer film of claim 13 , wherein the second surface layer comprises between about 80% and 99% by weight ethylene methyl acrylate copolymer and between about 1% to about 20% by weight tackifier resin.
20. The multilayer film of claim 19 , wherein the second surface layer comprises about 95% by weight ethylene methyl acrylate and about 5% by weight tackifier resin.
21. A multilayer film comprising:
a slip layer comprising at least polypropylene and high density polyethylene blend;
a cling layer comprising at least ethylene methyl acrylate copolymer and a tackifier; and
an intermediary layer comprising between about 65% and about 70% by weight linear low density polyethylene resin, about 30% by weight metallocene polyethylene resin, and 0% to about 5% by weight titanium dioxide.
22. A multilayer film comprising:
a slip layer comprising at least polypropylene and high density polyethylene blend;
a cling layer comprising at least ethylene methyl acrylate copolymer and a tackifier; and
an intermediary layer comprising between about 65% and about 95% by weight linear low density polyethylene resin and between about 5% and about 35% by weight metallocene polyethylene resin.
23. The multilayer film of claim 22 , wherein the intermediary layer further comprises titanium dioxide.
24. The multilayer film of claim 22 , wherein the slip layer comprises about 5% to about 20% by weight, the cling layer comprises about 5% to about 20% by weight, and the intermediary layer comprises about 60% to about 90% by weight.
25. The multilayer film of claim 22 , wherein the slip layer comprises about 15% by weight, the cling layer comprises about 10% by weight, and the intermediary layer comprises about 75% by weight.
26. The multilayer film of claim 22 , wherein the slip layer has a coefficient of friction between about 0.3 to about 0.9, and wherein the cling layer has a cling force to the slip layer between about 5 g/in to about 80 g/in.
27. The multilayer film of claim 22 , wherein the slip layer has a coefficient of friction of about 0.5, and wherein the cling layer has a cling force to the slip layer of about 40 g/in.
28. The multilayer film of claim 22 , wherein the slip layer comprises between about 80% and about 99% by weight polypropylene and between about 1% to about 20% by weight high density polyethylene.
29. The multilayer film of claim 22 , wherein slip layer comprises about 90% by weight polypropylene and about 10% by weight high density polyethylene.
30. The multilayer film of claim 22 , wherein the cling layer comprises between about 80% and 99% by weight ethylene methyl acrylate copolymer and between about 1% to about 20% by weight tackifier resin.
31. The multilayer film of claim 22 , wherein the cling layer comprises about 95% by weight ethylene methyl acrylate and about 5% by weight tackifier resin.
32. The multilayer film of claim 22 , wherein the overall multilayer film thickness is between about 0.012 mm to about 0.125 mm.
33. A multilayer film comprising:
a slip layer comprising at least polypropylene and high density polyethylene blend;
a cling layer comprising at least ethylene methyl acrylate copolymer and a tackifier; and
an intermediary layer comprising linear low density polyethylene resin and between about 5% and about 35% by weight metallocene polyethylene resin.
34. The multilayer film of claim 33 , wherein the coefficient of friction of the slip layer is about 0.5, and wherein the cling force of the cling layer to the slip layer is about 40 g/in.
35. The multilayer film of claim 33 , wherein the slip layer comprises between about 5% to about 20% by weight, the cling layer comprises between about 5% to about 20% by weight, and the intermediary layer comprises between about 60% to about 90% by weight.
36. The multilayer film of claim 35 , wherein the slip layer comprises about 15% by weight, the cling layer comprises about 10 % by weight, and the intermediary layer comprises about 75% by weight.
37. The multilayer film of claim 33 , wherein the slip layer comprises between about 80% and about 99% by weight polypropylene and between about 1% to about 20% by weight high density polyethylene.
38. The multilayer film of claim 37 , wherein slip layer comprises about 90% by weight polypropylene and about 10% by weight high density polyethylene.
39. The multilayer film of claim 33 , wherein the cling layer comprises between about 80% and 99% by weight ethylene methyl acrylate copolymer and between about 1% to about 20% by weight tackifier resin.
40. The multilayer film of claim 39 , wherein the cling layer comprises about 95% by weight ethylene methyl acrylate and about 5% by weight tackifier resin.
41. The multilayer film of claim 33 , wherein the multilayer film can withstand a force stretch of the film to about 600% at about 5000 psi.
42. The multilayer film of claim 33 , wherein the overall multilayer film thickness is between about 0.012 mm to about 0.125 mm.
43. The multilayer film of claim 33 , wherein the overall multilayer film thickness is about 0.025 mm.