Spark plug with an improved seal
View Patent ↗A spark plug having a glass seal formed from a first glass material and a second glass material. The first glass material has a glass transition temperature/softening point that is greater than the glass transition temperature/softening point of the second glass material. The first glass material and second glass material form a matrix and when combined with a filler have thermal expansion rates and properties the approximate leaded glass.
1. A spark plug comprising:
an insulator having a central bore;
a feed-through wire disposed in said central bore;
a non-conductive glass seal between the insulator and the feed-through, wherein said glass seal has a vesicular structure and is a fused or sintered glass matrix of substantially lead free first and second glass materials;
said first glass material including, in % by weight relative to the total weight of the first glass material, 19% to 24.5% SiO 2 , 35% to 41% B 2 O 3 , and 19% to 24% Al 2 O 3 ;
said second glass material including, in % by weight relative to the total weight of the second glass material, 40% to 55% Bi 2 O 3 , 0.5% to 10% SiO 2 , 20% to 35% B 2 O 3 , and 23% to 33% ZnO;
said first glass material having a first glass transition temperature and said second glass material having a second glass transition temperature, wherein the first glass transition temperature is 10 to 50 degrees Celsius apart from the second glass transition temperature.
2. The spark plug of claim 1 wherein said first glass material has a glass transition temperature of approximately 505-535 degrees Celsius.
3. The spark plug of claim 1 wherein said first glass material has a thermal expansion coefficient of approximately 6.2 ppm per degree Celsius, measured with the temperature being in the range of approximately 25-260 degrees Celsius.
4. The spark plug of claim 1 wherein each of said first and second glass materials have a particle size of less than 200 Mesh (US Standard Sieve) for approximately 95% by weight of each of said first and second glass powders, respectively.
5. The spark plug of claim 1 wherein said first glass material includes less than approximately 2% by weight Na 2 O.
6. The spark plug of claim 1 wherein said first glass material includes less than approximately 0.8% by weight K 2 O.
7. The spark plug of claim 1 wherein said first glass material includes approximately 4% to 7% by weight Li 2 O.
8. The spark plug of claim 1 wherein said first glass material includes less than approximately 0.8% by weight CaO.
9. The spark plug of claim 1 wherein said first glass material powder includes less than approximately 0.8% by weight BaO.
10. The spark plug of claim 1 wherein said first glass material includes 0.1% to 1.3% TiO2.
11. The spark plug of claim 1 wherein the glass seal further includes clay mineral binder.
12. The spark plug of claim 1 wherein said first and second glass materials each include individually less than 100 ppm of Lead, Mercury, Chromium, and less than 70 ppm Cadmium.
13. The spark plug of claim 1 wherein said matrix occurs upon heating said glass powders to a temperature of less than 750 degrees Celsius.
14. The spark plug of claim 1 wherein said glass seal further includes up to 5% by weight bentonite.
15. The spark plug of claim 1 wherein said first glass material includes approximately 5% to 17% by weight SrO.
16. The spark plug of claim 1 wherein said second glass material includes less than 1% by weight Al 2 O 3 .
17. The spark plug of claim 1 wherein said first glass material has a transition temperature within 50 degrees Celsius of the glass transition temperature of said second glass material.
18. The spark plug of claim 1 wherein said second glass material has a transition temperature of at least 10 degrees Celsius greater than the glass transition temperature of said second glass material.
19. The spark plug of claim 1 wherein said second glass material has a transition temperature of approximately 475 degrees Celsius to about 505 degrees Celsius.
20. The spark plug of claim 1 wherein said second glass material has a thermal expansion coefficient of approximately 6.4 ppm per degree Celsius, measured with the temperature being in the range of in the range of approximately 25 degrees to 260 degrees Celsius.
21. A spark plug comprising:
an insulator having a central bore; and
a non-conductive glass seal disposed in said bore and having a vesicular structure and formed from a first glass material and a second glass material;
said first glass material including, in % by weight relative to the total weight of the first glass material, 19% to 24.5% SiO 2 , 35% to 41% B 2 O 3 , and 19% to 24% A 1 2 O 3 ;
said second glass material including, in % by weight relative to the total weight of the second glass material, 40% to 55% Bi 2 O 3 , 0.5% to 10% SiO 2 , 20% to 35% B 2 O 3 , and 23% to 33% ZnO;
said first glass material having a first glass transition temperature and said second glass material having a second glass transition temperature, wherein said first glass transition temperature is at least 10 degrees Celsius greater than said second glass transition temperature.
22. The spark plug of claim 21 wherein said first glass transition temperature is no more than 50 degrees Celsius greater than said second glass transition temperature.
23. The spark plug of claim 21 wherein said first glass transition temperature is from 10-50 degrees Celsius greater than the second glass transition temperature.
24. The spark plug of claim 21 wherein said glass seal includes more of said first glass material than said second glass material by weight.
25. The spark plug of claim 21 wherein said glass seal includes at least 10 percent more of said first glass material than said second glass material by weight.
26. The spark plug of claim 21 wherein said first glass material is approximately 35% to 65% by weight and said second glass material is approximately 10-35% by weight.
27. The spark plug of claim 21 wherein said glass seal further includes a filler, said filler being approximately 15% to 26% by weight.
28. The spark plug of claim 27 wherein said filler is approximately 20% to 23% by weight.
29. The spark plug of claim 21 wherein said first glass material is approximately 45% to 55% by weight.
30. The spark plug of claim 21 wherein said second glass material is approximately 22% to 30% by weight.
31. The spark plug of claim 21 wherein said first glass material is approximately 48% to 50% by weight and said second glass material is approximately 26% to 28% by weight.
32. The spark plug of claim 21 wherein said glass seal further includes lithium carbonate.
33. The spark plug of claim 27 wherein said filler is an inorganic filler with a thermal expansion rate that is approximately less than or equal to the thermal expansion rate of either the first glass material or the second glass material.