Acrylic matt thermoplastic resin films and process for producing the same
View Patent ↗Acrylic matt thermoplastic resin films having excellent printability, flex whitening resistance, impact resistance and solvent resistance, and a process for the preparation thereof are provided. The films made of a thermoplastic resin composition comprising 100 parts by weight of an acrylic resin (A) and 0.5 to 20 parts by weight of a crosslinked acrylic polymer (B) as a matting agent are prepared by a process wherein the resin composition is kneaded and formed into a film, and the both surfaces of the film are simultaneously brought into contact with rolls between them, one roll being kept at a temperature of not less than the glass transition temperature Tg of the resin composition and the other roll being kept at a temperature of less than the Tg, whereby the film surface contacted with the roll having a temperature of Tg or higher is converted into a mirror surface and the film surface contacted with the roll having a temperature lower than Tg is converted into a matt surface.
1. A process for producing an acrylic matt thermoplastic resin film having a thickness of 10 to 300 μm by applying a high stretching processing via two rolls simultaneous contacting the film, the process comprising
kneading a thermoplastic resin composition (I) comprising (A) an acrylic resin and (B) 0.5 to 20 parts by weight of a crosslinked acrylic polymer as a matting agent based on 100 parts by weight of said acrylic resin (A),
forming said composition into a film, and
stretching the film,
bringing the both surfaces of said film into contact with rolls simultaneously between said rolls, the film temperature being not less than Tg of the thermoplastic resin (I) in the high stretching processing, wherein
one surface of said film is brought into contact with a roll kept at a temperature of not less than the glass transition temperature Tg of said resin composition (I) to thereby convert said surface into a mirror surface, and the other surface of said film is brought into contact with a roll kept at a temperature of less than the Tg to thereby convert said other surface into a matt surface,
wherein said acrylic resin (A) is an acrylic graft copolymer comprising (a-1) 5 to 85 parts by weight of an elastomeric polymer composed of 50 to 99.9% by weight of an alkyl acrylate, 0 to 49.9% by weight of other copolymerizable vinyl monomer and 0.1 to 10% by weight of a copolymerizable polyfunctional monomer having at least two non-conjugated double bonds per a molecule, and (a-2) 95 to 15 parts by weight of a graft component composed of 50 to 100% by weight of an alkyl methacrylate and 0 to 50% by weight of other vinyl monomer copolymerizable therewith which have been graft-polymerized onto said elastomeric polymer (a-1), in which said elastomeric polymer (a-1) has a particle size of 50 to 400 nm,
wherein said crosslinked acrylic polymer (B) is a graft copolymer comprising (b-1) 40 to 100 parts by weight of a crosslinked acrylic ester polymer prepared by polymerizing 100 to 90% by weight of an acrylic monomer composed of 40 to 90% by weight of an alkyl acrylate and 60 to 10% by weight of an alkyl methacrylate with 0 to 10% by weight of at least one other copolymerizable vinyl monomer and 0.1 to 20 parts by weight of a copolymerizable polyfunctional monomer having at least two non-conjugated double bonds per a molecule based on 100 parts by weight of the total of said acrylic monomer and said other vinyl monomer, and (b-2) 60 to 0 part by weight of a graft component composed of 60 to 100% by weight of an alkyl methacrylate, 0 to 40% by weight of an alkyl acrylate and 0 to 10% by weight of other copolymerizable vinyl monomer which have been graft-polymerized onto said crosslinked acrylic ester polymer (b-1).
2. The process of claim 1 , wherein said crosslinked acrylic polymer (B) has a weight average particle size of 0.5 to 15 μm.
3. A process for producing an acrylic matt thermoplastic resin film comprising kneading a thermoplastic resin composition (I) essentially consisting of (A) an acrylic resin and (B) 0.5 to 20 parts by weight of a crosslinked acrylic polymer as a matting agent based on 100 parts by weight of said acrylic resin (A),
forming said composition into a film, and
bringing the both surfaces of said film into contact with rolls simultaneously between said rolls, wherein one surface of said film is brought into contact with a roll kept at a temperature of not less than the glass transition temperature Tg of said resin composition (I) to thereby convert said surface into a mirror surface and the other surface of said film is brought into contact with a roll kept at a temperature of less than the Tg to thereby convert said other surface into a matt surface,
wherein said acrylic resin (A) is an acrylic graft copolymer comprising (a-1) 5 to 85 parts by weight of an elastomeric polymer composed of 50 to 99.9% by weight of an alkyl acrylate, 0 to 49.9% by weight of other copolymerizable vinyl monomer and 0.1 to 10% by weight of a copolymerizable polyfunctional monomer having at least two non-conjugated double bonds per a molecule, and (a-2) 95 to 15 parts by weight of a graft component composed of 50 to 100% by weight of an alkyl methacrylate and 0 to 50% by weight of other vinyl monomer copolymerizable therewith which have been graft-polymerized onto said elastomeric polymer (a-1), in which said elastomeric polymer (a-1) has a particle size of 50 to 400 nm
wherein said crosslinked acrylic polymer (B) is a graft copolymer comprising (b-1) 40 to 100 parts by weight of a crosslinked acrylic ester polymer prepared by polymerizing 100 to 90% by weight of an acrylic monomer composed of 40 to 90% by weight of an alkyl acrylate and 60 to 10% by weight of an alkyl methacrylate with 0 to 10% by weight of at least one other copolymerizable vinyl monomer and 0.1 to 20 parts by weight of a copolymerizable polyfunctional monomer having at least two non-conjugated double bonds per a molecule based on 100 parts by weight of the total of said acrylic monomer and said other vinyl monomer, and (b-2) 60 to 0 part by weight of a graft component composed of 60 to 100% by weight of an alkyl methacrylate, 0 to 40% by weight of an alkyl acrylate and 0 to 10% by weight of other copolymerizable vinyl monomer which have been graft-polymerized onto said crosslinked acrylic ester polymer (b-1).