Method of preparing wetting-resistant surfaces and articles incorporating the same
View Patent ↗The present invention provides methods for manufacturing an article having a wetting-resistant surface. The method includes providing a mixture comprising a plurality of micron-sized first particles and a plurality of nano-sized second particles, and a binder; depositing the mixture onto a substrate to form a wetting-resistant surface via a thermal spray process. The mixture is deposited without substantial melting of the first and second particles. The wetting-resistant surface has wettability sufficient to generate, with a reference fluid, a static contact angle of greater than about 90 degrees.
1. A method for manufacturing an article having a wetting-resistant surface comprising:
providing a mixture comprising a plurality of micron-sized first particles and a plurality of nano-sized second particles, and a binder; wherein the micron-sized first particles have a median particle size in the range from about 1 micrometer to about 100 micrometers; and wherein the nano-sized second particles have a median particle size in the range from about 10 nanometers to about 500 nanometers;
depositing the mixture onto a substrate to form a wetting-resistant surface via a thermal spray process, wherein the mixture is deposited without substantial melting of the first and second particles, wherein the binder gets deformed and binds the particles to the surface of the substrate during deposition, and binds the nano-sized particles to the micron-sized particles;
wherein the wetting-resistant surface has a wettability sufficient to generate, with a reference fluid of water or alcohol, a static contact angle of greater than about 90 degrees; and wherein the wetting-resistant surface has a texture comprising a plurality of micron-sized features provided by the micron-sized particles, and wherein the plurality of features further comprises a plurality of nano-scale features provided by the nano-sized particles, and wherein the plurality of nanoscale features are disposed onto the plurality of micron-sized features.
2. The method of claim 1 , wherein the micron-sized first particles comprise a material selected from the group consisting of a metal, a ceramic, a cermet, and an intermetallic material.
3. The method of claim 2 , wherein the micron-sized first particles comprise the metal, and the metal is at least one selected from the group consisting of steel, stainless steel, nickel, titanium, aluminum, any alloys thereof.
4. The method of claim 2 , wherein the micron-sized first particles comprise the ceramic, and the ceramic is at least one selected from the group consisting of an oxide, a mixed oxide, a nitride, a boride, a carbide, a carbonitride, a borocarbide, an oxynitride, and combinations thereof.
5. The method of claim 4 , wherein the ceramic is at least one selected from the group consisting of carbides of silicon or tungsten; nitrides of boron, titanium, silicon, or titanium; stibinite (SbS 2 ), titanium oxynitride, and combinations thereof.
6. The method of claim 1 , wherein the nano-sized second particles comprise a material selected from the group consisting of a ceramic, a cermet, and combinations thereof.
7. The method of claim 6 , wherein the nano-sized second particles comprise the ceramic, and the ceramic is at least one selected from the group consisting of an oxide, a mixed oxide, a carbide, a nitride, a boride, a carbonitride, a borocarbide, an oxynitride, and combinations thereof.
8. The method of claim 7 , wherein the ceramic comprises the oxide, and the oxide is at least one selected from the group consisting of alumina, zirconia, yttria, tantalum oxide, and lanthanoid oxide.
9. The method of claim 7 , wherein the ceramic comprises the nitride, and the nitride is at least one selected from the group consisting of boron nitride and carbon nitride.
10. The method of claim 1 , wherein the binder comprises a material selected from the group consisting of CoCr, Co, Ni, NiCr, and FeCr.
11. The method of claim 10 , wherein the binder comprises CoCr.
12. The method of claim 1 , wherein the nano-sized second particles are present in the mixture in a range from about 0.1 r/R weight percent to about 1 r/R weight percent, wherein r is the mean diameter of the nano-sized second particle and R is the mean diameter of the micron-sized first particle.
13. The method of claim 12 , wherein the nano-sized second particles are present in the mixture in a range from about 0.5 r/R weight percent to about 1 r/R weight percent, wherein r is the mean diameter of the nano-sized second particle and R is the mean diameter of the micron-sized first particle.
14. The method of claim 1 , wherein thermal spraying the mixture comprises accelerating the mixture in a carrier gas to a mass flow rate in a range from about 3 pounds/hour to about 5 pounds/hour.
15. The method of claim 1 , wherein thermal spraying the mixture comprises accelerating the mixture in a carrier gas to a velocity in a range from about 500 meters/second to about 700 meters/second.
16. The method of claim 1 , wherein the wetting-resistant surface has a wettability sufficient to generate, with the reference fluid, a static contact angle of greater than about 120 degrees.
17. The method of claim 1 , wherein the wetting-resistant surface has a surface enhancement factor of greater than about 1.2.
18. The method of claim 1 , further comprising modifying the wetting-resistant surface by applying a top coat comprising diamond-like carbon, titanium oxide, tantalum oxide, titanium nitride, titanium carbonitride, chromium nitride, chromium carbide, boron nitride, zirconium nitride, titanium carbide, tungsten carbide, molybdenum carbide, molybdenum boride, tridecafluoro 1,1,2,2-tetrahydroflouro octyl trichlorosilane, or tungsten boride.
19. The method of claim 1 , wherein the wear-resistant surface forms a part of an aircraft.
20. The method of claim 1 , wherein the wear-resistant surface forms a part of a turbine assembly.
21. A method for manufacturing an article having a wetting-resistant surface comprising:
providing a mixture comprising a plurality of micron-sized first particles and a plurality of nano-sized second particles, and a binder; wherein the micron-sized first particles have a median particle size in the range from about 1 micrometer to about 100 micrometers; and wherein the nano-sized second particles have a median particle size in the range from about 10 nanometers to about 500 nanometers;
thermal spraying the mixture at a temperature low enough to prevent substantial melting of the first and second particles; wherein the binder gets deformed and binds the particles to the surface of the substrate during deposition, and binds the nano-sized particles to the micron-sized particles;
depositing the mixture onto a substrate to form a coating; and
depositing a low surface energy layer onto the coating to create a wetting-resistant surface; wherein the low surface energy layer comprises diamond-like carbon, titanium oxide, tantalum oxide, titanium nitride, titanium carbonitride, chromium nitride, chromium carbide, boron nitride, zirconium nitride, titanium carbide, tungsten carbide, molybdenum carbide, molybdenum boride, tridecafluoro 1,1,2,2-tetrahydroflouro octyl trichlorosilane, or tungsten boride;
wherein the wetting-resistant surface has a wettability sufficient to generate, with a reference fluid of water or alcohol, a static contact angle of greater than about 90 degrees; and wherein the coating has a texture comprising a plurality of micron-sized features provided by the micron-sized particles, and wherein the plurality of features further comprises a plurality of nano-scale features provided by the nano-sized particles, and wherein the plurality of nanoscale features are disposed onto the plurality of micron-sized features.