Fire retardant nonwoven material and process for manufacture
View Patent ↗An improved acoustically and thermally insulating fire-retardant composite material suitable for use in structures such as buildings, appliances, and the interior passenger compartments and exterior components of automotive vehicles is provided. The material is comprised of at least one airlaid fibrous layer of controlled density and composition and incorporating suitable binding agents and additives as needed to meet expectations for noise abatement, fire-retardancy, and mildew resistance. Separately, an airlaid structure which provides a reduced, controlled airflow therethrough useful for acoustic insulation is provided, and which includes a woven or nonwoven scrim. A process for the production of the fire retardant nonwoven material is also provided.
1. A fire-retardant nonwoven material, comprising:
(A) a nonwoven substrate comprising matrix fibers including individualized cellulosic fibers;
(B) a binder; and
(C) a fire retardant,
wherein the fire-retardant nonwoven material has a Burn Through Time in a fire barrier screening test of about 1 minute or greater.
2. The fire-retardant nonwoven material of claim 1 , wherein the Burn Through Time in the Fire Barrier Test is about 15 minutes or greater.
3. The fire-retardant nonwoven material of claim 1 , wherein matrix fibers further comprise synthetic fibers.
4. The fire-retardant nonwoven material of claim 3 , wherein the matrix fibers are present in amounts ranging from about 30 weight percent to about 95 weight percent based on the total weight of the nonwoven material.
5. The fire-retardant nonwoven material of claim 4 , wherein the matrix fibers are present in amounts ranging from about 60 weight percent to about 80 weight percent based on the total weight of the nonwoven material.
6. The fire-retardant nonwoven material of claim 1 , wherein the binder is a bicomponent fiber binder, a latex binder, a thermoplastic material, or a mixture thereof.
7. The fire-retardant nonwoven material of claim 6 , wherein the binder is present in amounts ranging from about 5 weight percent to about 70 weight percent core binder.
8. The fire-retardant nonwoven material of claim 7 , wherein the binder is present in amounts ranging from about 20 weight percent to about 40 weight percent core binder.
9. The fire-retardant nonwoven material of claim 1 , wherein the nonwoven substrate has a basis weight of from about 200 gram per square meter (gsm) to about 3000 gsm.
10. The fire-retardant nonwoven material of claim 9 , wherein the basis weight of the nonwoven material substrate is from about 200 gsm to about 1500 gsm.
11. The fire-retardant nonwoven material of claim 9 , wherein the basis weight of the nonwoven material substrate is from about 1500 gsm to about 3000 gsm.
12. The fire-retardant nonwoven material of claim 1 , wherein the basis weight of the nonwoven material substrate is from about 10 gsm to about 2000 gsm.
13. The fire-retardant nonwoven material of claim 12 , wherein the basis weight of the nonwoven material substrate is from about 10 gsm to about 150 gsm.
14. The fire-retardant nonwoven material of claim 1 , wherein the nonwoven material has a caliper thickness of from about 1.0 mm to about 60 mm.
15. The fire-retardant nonwoven material of claim 14 , wherein the nonwoven material has a caliper thickness of from about 1.0 mm to about 3 mm.
16. The fire-retardant nonwoven material of claim 1 , wherein the fire retardant is present in an amount of from about 3 gsm to about 100 gsm.
17. The fire-retardant nonwoven material of claim 16 , wherein the fire retardant is present in an amount of from about 3 gsm to about 15 gsm.
18. The fire-retardant nonwoven material of claim 16 , wherein the fire retardant is present in an amount of from about 15 gsm to about 50 gsm.
19. The fire-retardant nonwoven material of claim 16 , wherein the fire retardant is present in an amount of from about 50 gsm to about 100 gsm.
20. The fire-retardant nonwoven material of claim 1 , wherein the fire-retardant nonwoven material further comprises an anti-leachant which is present in an amount of from about 5 gsm to about 50 gsm.
21. The fire-retardant nonwoven material of claim 1 , wherein the nonwoven material is an airlaid nonwoven, spunbonded nonwoven, a meltblown nonwoven, a spunlaced nonwoven, or a combination thereof.
22. The fire-retardant nonwoven material of claim 21 , wherein the nonwoven material is an airlaid nonwoven substrate.
23. The fire-retardant nonwoven material of claim 1 , wherein the nonwoven substrate has a density of from about 0.015 g/cc to about 0.10 g/cc.
24. The fire-retardant nonwoven material of claim 23 , wherein the nonwoven substrate has a density of from about 0.017 g/cc to about 0.045 g/cc.
25. The fire-retardant nonwoven material of claim 1 , wherein the nonwoven material has sound transmission reduction of 5 decibel or greater in an LSTT sound transmission test.
26. The fire-retardant nonwoven material of claim 25 , wherein the nonwoven material has sound transmission reduction of 11 decibel or greater in an LSTT sound transmission test.
27. The fire-retardant nonwoven material of claim 1 , further comprising a carrier having a basis weight of from about 8 gsm to about 2000 gsm which is integral with a surface of the core.
28. The fire-retardant nonwoven material of claim 27 , further comprising a carrier having a basis weight of from about 8 gsm to about 25 gsm which is integral with a surface of the core.
29. The fire-retardant nonwoven material of claim 1 , further comprising a carrier having a basis weight of from about 10 gsm to about 2000 gsm which is integral with a surface of the core.
30. The fire retardant, nonwoven material of claim 1 , further comprising an auxiliary layer containing plastic material with a basis weight of from about 300 gsm to about 700 gsm on the nonwoven material.
31. The fire retardant, nonwoven material of claim 1 , further comprising an auxiliary layer with a basis weight of from about 50 gsm to about 400 gsm on the nonwoven material.
32. The fire retardant, nonwoven material of claim 31 , wherein the auxiliary layer has a basis weight of from about 150 gsm to about 400 gsm.
33. The fire-retardant, nonwoven material of claim 1 , wherein the nonwoven material has a sound absorption coefficient (α) as determined by ASTM E1050-98 at 1000 Hz of about 0.5 or greater.
34. The fire-retardant, nonwoven material of claim 33 , wherein the nonwoven material has a sound absorption coefficient (a) as determined by ASTM E1050-98 at 1000 Hz of about 0.7 or greater.
35. The fire-retardant, nonwoven material of claim 1 , wherein the nonwoven material has a sound absorption coefficient (a) as determined by ASTM E1050-98 at 2500 Hz of about 0.9 or greater.
36. The fire-retardant, nonwoven material of claim 1 , wherein the nonwoven material has a SAMI of about 3 δdB/kgsm or greater.
37. The fire-retardant, nonwoven material of claim 36 , wherein the nonwoven material has a SAMI of about 8 δdB/kgsm or greater.
38. The fire-retardant, nonwoven material of claim 1 , further comprising a waterproofing, anti-leaching agent.
39. The fire-retardant, nonwoven material of claim 38 , wherein the anti-leaching agent is present in an amount of from about 5 gsm to about 50 gsm.
40. The fire-retardant nonwoven material of claim 3 , wherein the matrix fibers include inherently fire-retardant fibers.
41. The fire-retardant nonwoven material of claim 40 , wherein the fire retardant fibers comprise ammonium polyphosphate, melamine, sodium tetraborate decahydrate, or combinations thereof.
42. The fire-retardant nonwoven material of claim 1 , wherein the nonwoven structure has an airflow resistance of from about 500 to about 10,000 Rayls (NS/m 3 ).
43. The fire-retardant nonwoven material of claim 42 , wherein the nonwoven structure has an airflow resistance of from about 500 to about 3,000 Rayls (NS/m 3 ).
44. The fire-retardant, nonwoven material of claim 1 , wherein the nonwoven material is fabricated as a panel having an area of 50 m 2 or less.
45. The fire-retardant, nonwoven material of claim 44 , wherein the panel has been molded with an application of heat and pressure into a shape which is retained.
46. The fire-retardant, nonwoven material of claim 44 , wherein the panel has an area of 10 meters square or less.
47. The fire-retardant, nonwoven material of claim 1 , wherein the nonwoven material is attached to a panel of upholstery material or carpeting.
48. The fire-retardant, nonwoven material of claim 1 , wherein the nonwoven material is attached to a panel of an automobile.
49. The fire-retardant, nonwoven material of claim 1 , wherein the nonwoven material is attached to a wall or structural member of a building.
50. A sound attenuating laminate comprising the nonwoven material of claim 1 and attached or applied thereto or otherwise in contact therewith upholstery material, carpeting or a structural member or surface.
51. A mattress, futon or other bedding product, furniture cushion or covering incorporating the fire-retardant nonwoven material of claim 1 .
52. A fire retardant, nonwoven material comprising a core, containing:
(A) from about 30 weight percent to about 95 weight percent matrix fibers, the matrix fibers comprising individualized cellulosic fibers;
(B) from about 60 weight percent to about 5 weight percent core binder, where weight percentages in the core are based on the total weight of the core;
(C) a fire retardant, where the fire-retardant nonwoven material has a Burn Through Time in a fire barrier screening test of about 1 minute or greater; and where
(D) the core has a basis weight of from about 200 g/m 2 to about 3000 g/cm 2 ,
(E) the core has a density of from about 0.015 g/cc to about 0.10 glee, and
(F) the nonwoven material has sound transmission reduction of 5 decibel or greater in an LSTT sound transmission test.
53. A fire retardant, nonwoven material, comprising:
(a) a scrim with an interior surface and an outer surface, the scrim having a basis weight of from about 8 gsm to about 200 gsm;
(b) a nonwoven material having an interior surface and an outer surface, wherein the interior surface of the nonwoven material is in contact with the interior surface of the scrim, the nonwoven material having a basis weight of from about 10 g/m2 to about 2000 g/m2 which contains from about 30 weight percent to about 95 weight percent matrix fibers, wherein the matrix fibers comprise individualized cellulosic fibers, and from about 5 weight percent to about 70 weight percent of a binder where the weight percentages are based on the total weight of the nonwoven material; and
(c) the nonwoven material having been treated with a fire retardant.
54. The fire retardant, nonwoven material of claim 53 , further comprising:
(d) deposited on the outer surface of the scrim from about 1 g/m 2 to about 40 g/m 2 of a polymeric coating; and, optionally,
(e) deposited on the outer surface of the nonwoven material from about 1 g/m 2 to about 40 g/m 2 of a second polymeric coating; and
wherein the nonwoven structure has a Burn Through Time in a fire barrier screening test of about 1 minute or greater.
55. A process for the production of a fire-retardant nonwoven material, comprising:
(A) providing a comminution sheet of cellulosic fibers,
(B) comminuting the sheet into individualized cellulosic fibers,
(C) providing binder fibers,
(D) air conveying the individualized cellulosic fibers and binder fibers to form a mixture of matrix fibers,
(E) air laying the matrix fibers on a forming wire to form an airlaid nonwoven material,
(F) optionally, depositing a latex binder on the airlaid nonwoven material,
(G) heating the nonwoven material to cure the binder fibers,
(H) depositing a fire retardant on the nonwoven material, and
(I) optionally, depositing an anti-leachant on the nonwoven material.
56. A process for the production of a fire-retardant, nonwoven material comprising:
(1a) on a moving foraminous wire from one or more forming heads, depositing a mixture comprising:
(A) from about 95 weight percent to about 40 weight percent matrix fibers, wherein the matrix fibers comprise individualized cellulosic fibers,
(B) from about 60 weight percent to about 5 weight percent core binder, to form a core of the nonwoven material, where weight percentages in the core are based on the total weight of the core, and
(C) a fire retardant, followed by
(2a) heating the nonwoven material to consolidate the mixture of matrix fibers and binder, or,
(1b) deposition on a moving foraminous wire of
(A) a woven or nonwoven carrier with a basis weight of from about 10 gsm to about 2000 gsm; followed by
(2b) deposition on the carrier from one or more forming heads of a mixture containing
(B) from about 95 weight percent to about 40 weight percent matrix fibers, wherein the matrix fibers comprise individualized cellulosic fibers,
(C) a fire retardant, and
(D) from about 60 weight percent to about 5 weight percent core binder,
to form a core of the nonwoven material, where weight percentages in the core are based on the total weight of the core, and so that the carrier is integral with a surface of the core, followed by
(3) heating the nonwoven material to consolidate the mixture of matrix fibers and binder, wherein
(E) the core has a basis weight of from about 200 gsm to about 3000 gsm, and
(F) the core has a density of from about 0.015 g/cc to about 0.10 g/cc.
57. A process for the production of a nonwoven structure, comprising;
(1) providing a scrim with an interior surface and an outer surface, the scrim having a basis weight of from about 8 g/m 2 to about 200 g/m 2 ;
(2) airlaying a nonwoven material on the interior surface of the scrim, the nonwoven material having a basis weight of from about 10 g/m 2 to about 2000 g/m 2 which contains from about 30 weight percent to about 95 weight percent matrix fibers, wherein the matrix fibers comprise individualized cellulosic fibers, and from about 5 weight percent to about 70 weight percent of a binder where the weight percentages are based on the total weight of the nonwoven material;
(3) depositing on the outer surface of the scrim from about 1 g/m 2 to about 40 g/m 2 of a polymeric coating;
(4) depositing a fire retardant material onto an outer surface of either the nonwoven structure or the scrim so that the nonwoven structure has a Burn Through Time in a fire barrier screening test of about 1 minute or greater; and, optionally,
(5) depositing on the outer surface of the nonwoven material from about 1 g/m 2 to about 40 g/m 2 of a second polymeric coating.
58. A process for the production of a fire-retardant nonwoven material comprising:
(A) depositing a fire retardant on a comminution sheet of cellulosic fibers,
(B) comminuting the sheet into individualized cellulosic fibers,
(C) providing binder fibers,
(D) air conveying the individualized cellulosic fibers and binder fibers to form a mixture of matrix fibers,
(E) air laying the matrix fibers on a forming wire to form an airlaid nonwoven material,
(F) optionally, depositing a latex binder on the airlaid nonwoven material,
(G) heating the nonwoven material to cure the binder, and
(H) optionally, depositing an anti-leachant on the comminution sheet or on the nonwoven material.
59. A process for the production of a nonwoven material comprising:
(A) providing a comminution sheet of cellulosic fibers,
(B) treating the comminution sheet with a substance by spraying or dousing the comminution sheet;
(C) comminuting the sheet into individualized cellulosic fibers,
(C) providing binder fibers,
(D) air conveying the individualized cellulosic fibers and binder fibers to form a mixture of matrix fibers,
(E) air laying the matrix fibers on a forming wire to form an airlaid nonwoven material, and
(F) heating the nonwoven material to cure the binder fibers.
60. The process of claim 59 , wherein the substance applied to the comminution sheet is a fire retardant, waterproofing agent, pigment, adhesive, biocide, antileachant, polymer, antimicrobicide, or a combination thereof.