View Patent ↗A method of casting a multi-layered metal ingot including the steps of delivering a metallic divider member into a direct chill mold, pouring a first molten metal into the mold on one side of the divider member, and pouring a second molten metal into the mold on the other side of the divider member, and allowing the first molten metal and the second molten metal solidify to form a metal ingot which includes the divider metal layer disposed there between.
1. A brazing sheet comprising:
a first aluminum metal layer; and
a second aluminum metal layer connected to the first aluminum metal layer, wherein the second aluminum metal layer has a different composition than the first aluminum metal layer;
wherein the brazing sheet is produced by a process comprising:
(A) direct chill casting a multi-layered slab, the direct chill casting process comprising:
(1) flowing a first molten aluminum alloy in a direct chill casting apparatus;
(2) providing a barrier layer;
(3) flowing a second molten aluminum alloy into a direct chill casting apparatus,
(4) wherein the second molten aluminum alloy has a different composition than the first molten aluminum alloy,
(5) wherein the barrier layer prevents the first molten aluminum alloy from intermixing with the second molten aluminum alloy;
(6) forming the first aluminum layer from the first molten aluminum alloy; and
(7) forming the second distinct aluminum layer from the second molten aluminum alloy; and
(B) rolling the multi-layered slab to form the brazing sheet.
2. The brazing sheet of claim 1 , wherein, after the rolling step (B), the first aluminum metal layer is uniformly thick across the brazing sheet, and the second aluminum metal layer is uniformly thick across the brazing sheet.
3. The brazing sheet of claim 2 , wherein one of the first aluminum metal layer and the second aluminum metal layer is a clad layer of the brazing sheet, and the other of the first aluminum metal layer and the second aluminum metal layer is a core layer of the brazing sheet.
4. The brazing sheet of claim 3 , wherein the clad layer comprises an AA4000 series aluminum alloy.
5. The brazing sheet of claim 3 , wherein the core layer comprises one of an AA1000, 5000, 6000 or 7000 series alloy.