Method for joining ceramic components

1. A method for joining multiple ceramic components together, the method comprising:

providing a first ceramic component having a first mating surface and a second ceramic component having a second mating surface adapted to mate with the first mating surface;

applying a slip to at least one of the first and second mating surfaces, the slip comprising a mixture of alumina powder and a phosphate-containing reagent to react with the alumina powder, the alumina powder having a mean particle size of less than 1 micron, wherein the molar ratio of total aluminum from the alumina powder to total phosphorus from the phosphate-containing reagent is between 8 and about 65;

joining the first and second mating surfaces together; and

sintering the slip to react the mixture and thereby generate a bond between the first and second ceramic components.

2. The method of claim 1 , wherein at least one of the first and second ceramic components is a ceramic monolith.

3. The method of claim 1 , wherein at least one of the first and second ceramic components is a fiber-based ceramic material.

4. The method of claim 1 , wherein the phosphate-containing reagent is phosphoric acid.

5. The method of claim 1 , wherein at least one of the first and second ceramic components contains at least fifty percent of one of the following materials: alumina, mullite, cordierite, magnesia, iron oxide, barium oxide, zinc oxide, copper oxide, tungsten oxide, samaria, ruthenium oxide, silicon carbide, silicon nitride, ceria, yttria, silica, calcia, titania, and zirconia.

6. The method of claim 1 , wherein at least one of the first and second ceramic components is selected from the group consisting of a green ceramic component, a pre-sintered ceramic component, and a sintered ceramic component.

7. The method of claim 1 , wherein sintering comprises sintering at a temperature less than 1000° C.

8. The method of claim 1 , wherein sintering comprises sintering at a temperature less than 1600° C.

9. A method for joining multiple ceramic components together, the method comprising:

providing a first ceramic component having a first mating surface and a second ceramic component having a second mating surface adapted to mate with the first mating surface;

applying a slip to at least one of the first and second mating surfaces, the slip comprising a mixture of alumina powder and a phosphate-containing reagent to react with the alumina powder, the alumina powder having a mean particle size of less than 10 microns, the mixture having a molar ratio of total aluminum from the alumina powder to total phosphorus from the phosphate-containing reagent is between 8 and about 65;

joining the first and second mating surfaces together; and

sintering the slip to react the mixture and thereby generate a bond between the first and second ceramic components.

10. The method of claim 9 , wherein at least one of the first and second ceramic components is a ceramic monolith.

11. The method of claim 9 , wherein at least one of the first and second ceramic components is a fiber-based ceramic material.

12. The method of claim 9 , wherein the phosphate-containing reagent is phosphoric acid.

13. The method of claim 9 , wherein at least one of the first and second ceramic components is selected from the group consisting of a green ceramic component, a pre-sintered ceramic component, and a sintered ceramic component.

14. The method of claim 9 , wherein sintering comprises sintering at a temperature less than 1000° C.

15. The method of claim 9 , wherein sintering comprises sintering at a temperature less than 1600° C.

16. A method for joining multiple ceramic components together, the method comprising:

providing a first ceramic component having a first mating surface and a second ceramic component having a second mating surface adapted to mate with the first mating surface, wherein at least one of the first and second ceramic components is produced by casting a first slip comprising a mixture of alumina powder and a phosphate-containing reagent to react with the alumina powder;

applying a second slip to at least one of the first and second mating surfaces, the second slip comprising a mixture of alumina powder and a phosphate-containing reagent to react with the alumina powder, wherein the molar ratio of total aluminum from the alumina powder (in both the first slip and the second slip) to total phosphorus from the phosphate-containing reagent (in both the first slip and the second slip) is between 8 and about 65;

joining the first and second mating surfaces together; and

sintering the second slip to react the mixture and thereby generate a bond between the first and second ceramic components.

17. The method of claim 16 , wherein the first slip comprises substantially the same materials as the second slip.

18. The method of claim 16 , wherein the phosphate-containing reagent of the first slip and the phosphate-containing reagent of the second slip are both phosphoric acid.

19. The method of claim 16 , wherein at least one of the first and second ceramic components is selected from the group consisting of a green ceramic component, a pre-sintered ceramic component, and a sintered ceramic component.

20. The method of claim 16 , wherein, after sintering, the first and second slips have substantially the same coefficients of thermal expansion.

21. The method of claim 16 , wherein at least one of the first and second ceramic components contains at least fifty percent of one of the following materials: alumina, mullite, cordierite, magnesia, iron oxide, barium oxide, zinc oxide, copper oxide, tungsten oxide, samaria, ruthenium oxide, silicon carbide, silicon nitride, ceria, yttria, silica, calcia, titania, and zirconia.

22. A method for joining multiple ceramic components together, the method comprising:

providing a ceramic monolith having a first mating surface and a fiber-based ceramic component having a second mating surface adapted to mate with the first mating surface;

applying a slip to at least one of the first and second mating surfaces, the slip comprising a mixture of alumina powder and a phosphate-containing reagent to react with the alumina powder, the alumina powder having a mean particle size of less than 10 microns, wherein the molar ratio of total aluminum from the alumina powder to total phosphorus from the phosphate-containing reagent is between 8 and about 65;

joining the first and second mating surfaces together; and

sintering the slip to react the mixture and thereby generate a bond between the ceramic monolith and the fiber-based ceramic component.

23. The method of claim 22 , wherein the phosphate-containing reagent is phosphoric acid.

24. The method of claim 22 , wherein the ceramic monolith is selected from the group consisting of a green ceramic component, a pre-sintered ceramic component, and a sintered ceramic component.

25. The method of claim 22 , wherein the ceramic monolith is produced by casting a slip comprising a mixture of alumina powder and a phosphate-containing reagent to react with the alumina powder.

26. A method for joining multiple ceramic components together, the method comprising:

providing a fiber-based ceramic component;

forming a ceramic monolith by casting a slip, the slip comprising a mixture of alumina powder and a phosphate-containing reagent to react with the alumina powder, the alumina powder having a mean particle size of less than 10 microns, wherein the molar ratio of total aluminum from the alumina powder to total phosphorus from the phosphate-containing reagent is between 8 and about 65;

dipping the fiber-based ceramic component into the slip; and

sintering the slip to react the mixture and thereby generate a bond between the ceramic monolith and the fiber-based ceramic component.