Pre-impregnated composite materials with improved performance
View Patent ↗Pre-impregnated composite material (prepreg) is provided that can be molded to form composite parts that have high levels of both strength and damage tolerance without causing any substantial negative impact upon the physical or chemical characteristics of the uncured prepreg or cured part. This is achieved by including in the matrix resin a substantial amount of a multifunctional aromatic epoxy resin that has at least one phenyl group that is meta-substituted.
1. A pre-impregnated composite material comprising:
A) reinforcing fibers; and
B) a matrix comprising:
a) a from 10 to 40 weight percent of dysfunctional epoxy resin;
b) from 15 to 45 weight percent of a trifunctional epoxy resin comprising triglycidyl meta-aminophenol;
c) from 1 to 35 weight percent insoluble thermoplastic particles;
d) from 5 to 45 weight percent thermoplastic toughening agent; and
e) from 10 to 30 weight percent curing agent.
2. A pre-impregnated composite material according to claim 1 wherein the amount of said matrix in said pre-impregnated composite material is between about 25 weight percent and 45 weight percent.
3. A pre-impregnated composite material according to claim 1 wherein said reinforcing fibers are selected from the group consisting of glass, carbon and aramid.
4. A pre-impregnated composite material according to claim 2 wherein said reinforcing fibers are in the form of woven fabric, unidirectional fibers, randomly oriented fibers or quasi-isotropic chopped unidirectional fiber tape.
5. A pre-impregnated composite material according to claim 1 wherein said dysfunctional epoxy resin is selected from the group consisting of diglycidyl ether of bisphenol F, diglycidyl ether of bisphenol A, diglycidyl dihydroxy naphthalene and combinations thereof.
6. A pre-impregnated composite material according to claim 1 wherein said matrix further comprises N,N,N′,N′-tetraglycidyl-m-xylenediamine or N,N,N′,N′-tetraglycidyl-4,4′-diaminodiphenyl methane.
7. A pre-impregnated composite material according to claim 1 wherein said insoluble thermoplastic particles comprise polyamide particles.
8. A pre-impregnated composite material according to claim 1 wherein said toughening agent is selected from the group consisting of polyether sulfone, polyether ethersulfone, polyphenyl sulphone, polysulfone, polyimide, polyetherimide, aramid, polyester, polyketone, polyetheretherketone, polyurethane, polyurea, polyarylether, polyarylsulphide, polycarbonate and polyphenylene oxide.
9. A pre-impregnated composite material according to claim 1 wherein said curing agent is an aromatic amine.
10. A pre-impregnated composite material according to claim 1 wherein said matrix comprises:
15 to 35 weight percent of said dysfunctional epoxy resin;
20-40 weight percent of said trifunctional epoxy resin;
10-20 weight percent of said insoluble thermoplastic particles;
10-20 weight percent of said thermoplastic toughening agent; and
15-25 weight percent of said curing agent.
11. A pre-impregnated composite material according to claim 10 wherein said dysfunctional epoxy resin is diglycidyl ether of bisphenol F.
12. A pre-impregnated composite material according to claim 11 wherein said insoluble thermoplastic particles comprises polyamide particles.
13. A pre-impregnated composite material according to claim 12 wherein said polyamide particles comprise both low melting and high melting polyamide particles.
14. A pre-impregnated composite material according to claim 12 wherein said thermoplastic toughening agent is polyether sulfone.
15. A pre-impregnated composite material according to claim 14 wherein said curing agent is 4,4-diaminodiphenylsulfone.
16. A pre-impregnated composite material according to claim 15 wherein said matrix comprises:
22 to 25 weight percent of said diglycidyl ether of bisphenol F;
25 to 30 weight percent of said trifunctional epoxy resin;
10 to 15 weight percent of said polyamide particles;
13 to 17 weight percent of said polyether sulfone; and
17 to 21 weight percent of said 4,4-diaminodiphenylsulfone.
17. A composite part that comprises a pre-impregnated composite material according to claim 1 wherein said matrix has been cured.
18. A method for making a composite part comprising the step of curing a pre-impregnated composite material according to claim 1 .
19. A pre-impregnated composite material according to claim 1 wherein said matrix further comprises conducting particles.
20. A pre-impregnated composite material according to claim 19 wherein said conducting particles are selected from the group of particles consisting of silver, gold, copper, aluminum, nickel, conducting grades of carbon, buckminsterfullerene, carbon nanotubes, carbon nanofibers, nickel coated carbon particles, silver coated silica particles and copper coated silica particles.
21. A pre-impregnated composite material according to claim 20 wherein said conducting particles comprise conducting grades of carbon.
22. A method for making a pre-impregnated composite material comprising the steps of:
A) providing a reinforcing fiber; and
B) impregnating said reinforcing fiber with a matrix wherein said matrix comprises:
a) a from 10 to 40 weight percent of dysfunctional epoxy resin;
b) from 15 to 45 weight percent of a trifunctional epoxy resin comprising triglycidyl meta-aminophenol;
c) from 1 to 35 weight percent insoluble thermoplastic particles;
d) from 5 to 45 weight percent thermoplastic toughening agent; and
e) from 10 to 30 weight percent curing agent.