Stabilizers for improved open time of aqueous coatings
A stabilizer composition comprising an AB type polymer for use in increasing Open Time of aqueous coating compositions is disclosed. The stabilizers compositions are of utility in many aqueous compositions including paints, stains, varnishes, adhesives and inks. Of particular interest is the use of the stabilizer compositions for in increasing the Open Time of latex paints as well as alkyd emulsion paints.
1. A stabilizer composition for use in increasing Open Time of an aqueous coating composition comprising an AB type polymer, wherein B comprises a water-soluble/water dispersible oligomer or polymer and wherein A, covalently connected to B, comprises a structure that has the following formula:
wherein R comprises a C 1 to C 30 hydrocarbon, which is linear or branched, aliphatic or aromatic, or combinations thereof;
R 1 comprises H, CH 3 , or C 2 H 5 ;
R 2 comprises CH 2 O, CO 2 , CONH, or CH 2 and wherein R 2 can be the same or different;
R 3 comprises H or OH;
n is an integer from 2 to 100; and
m is either 0 or 1;
wherein “A” is made from a monomer selected from the group consisting of polyphenoxy glycidyl ether, methylphenyl glycidyl ether, ethylhexylglycidyl ether, phenyl glycidyl ether, and alkali glycidyl ether, and wherein “B” comprises polyacetalpolyether (PAPE); and
wherein the addition of at least 0.5 wt % of the AB type polymer to an aqueous coating composition increases the Open Time of the aqueous coating composition by at least 10% Open Time, as measured by at least one of Open Time X-test A&D and Open Time X-test RC.
2. The stabilizer composition of claim 1 , wherein “A” is made from methylphenyl glycidyl ether.
3. The stabilizer composition of claim 1 , wherein “A” is made from ethylhexylglycidylether.
4. An aqueous coating composition comprising:
a film-forming polymer, and
a stabilizer composition comprising an AB type polymer, wherein B comprises a water-soluble/water dispersible oligomer or polymer and wherein A, covalently connected to B, comprises a structure that has the following formula:
wherein R comprises a C 1 to C 30 hydrocarbon, which is linear or branched, aliphatic or aromatic or combinations thereof:
R 1 comprises H, CH 3 , or C 2 H 5 ;
R 2 comprises CH 2 O, CO 2 , CONH, or CH 2 and wherein R 2 can be the same or different;
R 3 comprises H or OH;
n is an integer from 2 to 100; and
m is either 0 or 1;
wherein “A” is made from a monomer selected from the group consisting of polyphenoxy glycidyl ether, methylphenyl glycidyl ether, ethylhexylglycidyl ether, phenyl glycidyl ether, and alkali glycidyl ether, and wherein “B” comprises polyacetalpolyether (PAPE); and
wherein the addition of at least 0.5 wt % of the AB type polymer to an aqueous coating composition increases the Open Time of the aqueous coating composition by at least 10% Open Time, as measured by at least one of Open Time X-test A&D and Open Time X-test RC.
5. The aqueous coating composition of claim 4 , wherein the film-forming polymer comprises a latex.
6. The aqueous coating composition of claim 5 , wherein the film-forming polymer may be selected from the group consisting of alkyl acrylates, alkoxy acrylates, alkyl methacrylates, alkoxy methacrylates, vinyl esters of saturated carboxylic acids monoolefins and conjugated dienes.
7. The aqueous coating composition of claim 4 further comprising one or more of an additional component selected from the group consisting of pigments, fillers, thickeners, biocides, mildewcides, surfactants, dispersants and defoamers.
8. The aqueous coating composition of claim 4 , wherein the stabilizer composition comprises about 0.1 to about 10 wt % of the aqueous coating composition.
9. The aqueous coating composition of claim 8 , wherein the stabilizer composition comprises about 0.1 to about 3 wt % of the aqueous coating composition.
10. The aqueous coating composition of claim 8 , wherein the stabilizer composition comprises about 0.5 to about 1 wt % of the aqueous coating composition.
11. The aqueous coating composition of claim 4 , wherein “A” comprises methylphenyl glycidyl ether.
12. The aqueous coating composition of claim 4 , wherein “A” comprises ethylhexylglycidylether.
13. The aqueous coating composition of claim 4 , wherein the aqueous coating composition is selected from the group consisting of paints, stains, varnishes, adhesives and inks.
14. The aqueous coating composition of claim 13 , wherein the aqueous coating composition comprises a paint.
15. A method of producing an aqueous coating composition having increased Open Time comprising the steps of:
dispersing or emulsifying a film-forming polymer in an aqueous solution, and
adding an amount of a stabilizer composition to the aqueous solution to form the aqueous composition having increased Open Time, wherein the stabilizer composition comprises an AB type polymer, wherein B comprises a water-soluble/water dispersible oligomer or polymer and wherein A, covalently connected to B, comprises a structure that has the following formula:
wherein R comprises a C 1 to C 30 hydrocarbon, which is linear or branched, aliphatic or aromatic or combinations thereof:
R 1 comprises H, CH 3 , or C 2 H 5 ;
R 2 comprises CH 2 O, CO 2 , CONH or CH 2 and wherein R 2 can be the same or different;
R 3 comprises H or OH;
n is an integer from 2 to 100; and
m is either 0 or 1;
wherein “A” is made from a monomer selected from the group consisting of polyphenoxy glycidyl ether, methylphenyl glycidyl ether, ethylhexylglycidyl ether, phenyl glycidyl ether, and alkali glycidyl ether, and wherein “B” comprises polyacetalpolyether (PAPE); and
wherein the addition of at least 0.5 wt % of the AB type polymer to an aqueous coating composition increase the Open Time of the aqueous coating composition by at least 10% Open Time, as measured by at least one of Open Time X-test A&D and Open Time X-test RC.
16. The method of claim 15 , wherein stabilizer composition is added to the aqueous solution before the film-forming polymer is dispersed or emulsified in the aqueous solution.
17. The method of claim 15 , wherein stabilizer composition is added to the aqueous solution after the film-forming polymer is dispersed or emulsified in the aqueous solution.
18. The method of claim 15 , wherein stabilizer is added to the aqueous solution at the same time the film-forming polymer is dispersed or emulsified in the aqueous solution.
19. A stabilizer composition for use in increasing Open Time of an aqueous coating composition comprising a latex thickener and an AB type polymer, wherein B comprises a water-soluble/water dispersible oligomer or polymer and wherein A, covalently connected to B, comprises a structure that has the following formula:
wherein R comprises a C 1 to C 30 hydrocarbon, which is linear or branched, aliphatic or aromatic, or combinations thereof;
R 1 comprises H, CH 3 , or C 2 H 5 ;
R 2 comprises CH 2 O, CO 2 , CONH, or CH 2 , and wherein R 2 can be the same or different;
R 3 comprises H or OH;
n is an integer from 2 to 100; and
m is either 0 or 1;
wherein “A” is made from a monomer selected from the group consisting of polyphenoxy glycidyl ether, methylphenyl glycidyl ether, ethylhexylglycidyl ether, phenyl glycidyl ether, and alkali glycidyl ether, and wherein “B” comprises polyacetalpolyether (PAPE); and wherein the addition of at least 0.5 wt % of the AB type polymer to an aqueous coating composition comprising a latex thickener increases the Open Time of the aqueous coating composition by at least 30% Open Time, as measured by at least one of Open Time X-test A&D and Open Time X-test RC.