Flex crack resistant low density polyethylene films
View Patent ↗This invention relates to film used to manufacture pouches and bags for containing flowable material. The film is made of low density polyethylene and can be formed into a monofilm or a multi-layer film that can be used to produce packages that exhibit improved flex crack resistance.
1. A sealant film for use in a film structure for the manufacture of pouches and bags for containing flowable materials, said sealant film comprising:
(a) from about 2.0 wt % to about 9.5 wt %, based on 100 wt % total composition, of an ethylene C 4 -C 10 -alpha-olefin interpolymer;
wherein said ethylene C 4 -C 10 -alpha-olefin interpolymer is present in an amount that optimizes flex crack resistance as measured using a Gelbo Flex tester set up to test in accordance with ASTM F392;
wherein said ethylene C 4 -C 10 -alpha-olefin interpolymer is present in an amount that minimizes reduction of thermal resistance, as measured using DSC (ASTM E794/E793) Differential Scanning Calorimetry (DSC), which determines temperature and heat flow associated with material transitions as a function of time and temperature;
wherein said ethylene C 4 -C 10 -alpha-olefin interpolymer is present in an amount that maximizes stiffness of said sealant film layer as measured using Tensile Modulus of said polyethylene films measured in accordance with ASTM Method D882; and
wherein said ethylene C 4 -C 10 -alpha-olefin interpolymer is manufactured in a polymerization process using a single-site or metallocene catalyst and has a density of from 0.850 to 0.890 g/cc and a melt index of 0.3 to 5 g/10 min,
(b) from about 70.5 wt % to about 98.0 wt %, based on 100 wt % total composition, of one or more polymers selected from ethylene homopolymers and ethylene C 4 -C 10 -alpha-olefin interpolymers, having a density between 0.915 g/cc and 0.935 g/cc and a melt index of 0.2 g/10 min to 2 g/10 min, and
(c) from about 0 wt % to about 20.0 wt %, based on 100 wt % total composition, of processing additives selected from slip agents, antiblock agents, colorants and processing aids, and
wherein said sealant film has a thickness of from about 2 μm to about 60 μm.
2. A sealant film as recited in claim 1 , wherein said ethylene C 4 -C 10 -alpha-olefin interpolymer in (a) and (b) are each ethylene-octene interpolymers.
3. A sealant film as recited in claim 1 , wherein component (c) is present in an amount of from about 3 wt % to about 5 wt % based on 100 wt % total composition.
4. A monofilm comprising a film structure that comprises said sealant film as recited in claim 1 .
5. A pouch for containing flowable material made from a monofilm as recited in claim 4 .
6. A multi-layer film structure comprising at least one sealant layer as recited in claim 1 .
7. A pouch for containing flowable material made from a multi-layer film structure as recited in claim 6 .
8. A multi-layer film structure as recited in claim 6 , wherein one or both outer layers is a sealant layer.
9. A pouch for containing flowable material made from a multi-layer film structure recited in claim 8 .
10. A multi-ply film structure comprising at least one intermediate or inner ply of said sealant layer as recited in claim 1 .
11. A bag for containing flowable material made from a multi-ply film structure as recited in claim 10 .
12. A sealant film for use in a film structure for containing flowable materials, said sealant film comprising:
(a) from about 2.0 wt % to about 9.5 wt %, based on 100 wt % total composition, of an ethylene C 4 -C 10 -alpha-olefin interpolymer;
wherein said ethylene C 4 -C 10 -alpha-olefin interpolymer is present in an amount such that the film structure develops 10 or less pinholes per 300 cm 2 in 20,000 cycles of Gelbo Flex testing, as measured using a Gelbo Flex tester set up to test in accordance with ASTM F392;
wherein said ethylene C 4 -C 10 -alpha-olefin interpolymer is present in an amount such that said film structure has a thermal resistance at temperatures just above 100° C., as measured using DSC (ASTM E794/E793) Differential Scanning calorimetry (DSC), which determines temperature and heat flow associated with material transitions as a function of time and temperature;
wherein said ethylene C 4 -C 10 -alpha-olefin interpolymer is present in an amount such that the film structure has a minimum tensile modulus of 20,000 psi as measured using Tensile Modulus of the polyethylene films measured in accordance with ASTM Method D882;
wherein said ethylene C 4 -C 10 -alpha-olefin interpolymer is manufactured in a polymerization process using a single-site or metallocene catalyst and has a density of from 0.850 g/cc to 0.890 g/cc and a melt index of 0.3 g/10 min to 5 g/10 min,
(b) from about 70.5 wt % to about 98.0 wt %, based on 100 wt % total composition, of one or more polymers selected from ethylene homopolymers and ethylene C 4 -C 10 -alpha-olefin interpolymers having a density between 0.915 g/cc and 0.935 g/cc and a melt index of 0.2 g/10 min to 2 g/10 min, and
(c) from about 0 wt % to about 20.0 wt %, based on 100 wt % total composition, of processing additives selected from slip agents, antiblock agents, colorants, and processing aids, and
wherein said sealant film has a thickness of from about 2 μm to about 60 μm.
13. A monofilm comprising a film structure that comprises said sealant film as recited in claim 12 .
14. A pouch for containing flowable material made from a monofilm as recited in claim 13 .
15. A multi-layer film structure comprising at least one sealant layer as recited in claim 12 .
16. A pouch for containing flowable material made from a multi-layer film structure as recited in claim 15 .
17. A multi-layer film structure as recited in claim 15 , wherein one or both outer layers is a sealant layer.
18. A pouch for containing flowable material made from a multi-layer film structure as recited in claim 17 .
19. A multi-ply film structure comprising at least one intermediate or inner ply of said sealant layer as recited in claim 12 .
20. A bag for containing flowable material made from a multi-ply film structure as recited in claim 19 .
21. A sealant film for use in a film structure for the manufacture of pouches and bags for containing flowable materials, said sealant film comprising:
(a) from about 2.0 wt % to about 9.5 wt %, based on 100 wt % total composition, of an ethylene C 4 -C 10 -alpha-olefin interpolymer;
wherein said ethylene C 4 -C 10 -alpha-olefin interpolymer is present in an amount that optimizes flex crack resistance as measured using a Gelbo Flex tester set up to test in accordance with ASTM F392;
wherein said ethylene C 4 -C 10 -alpha-olefin interpolymer is manufactured in a polymerization process using a single-site or metallocene catalyst and has a density of from 0.850 to 0.890 g/cc and a melt index of 0.3 to 5 g/10 min,
(b) from about 70.5 wt % to about 98.0 wt %, based on 100 wt % total composition, of one or more polymers selected from ethylene homopolymers and ethylene C 4 -C 10 -alpha-olefin interpolymers, having a density between 0.915 g/cc and 0.935 g/cc and a melt index of 0.2 g/10 min to 2 g/10 min, and
(c) from about 0 wt % to about 20.0 wt %, based on 100 wt % total composition, of processing additives selected from slip agents, antiblock agents, colorants and processing aids, and
wherein said sealant film has a thickness of from about 2 μm to about 60 μm.