Process for Producing Permanent Magnet for Use in Automotive Ipm Motor
[Problem] To provide a process for producing a permanent magnet for use in an automotive IPM motor, which excels in all of corrosion resistance, abrasion resistance, and impact resistance. [Means for Resolution] The production process characterized in that it comprises forming on the surface of an R—Fe—B based permanent magnet a 3 to 15 μm thick Ni film as a first layer by electroplating method, followed by a 3 to 15 μm thick Cu or Sn film as a second layer by electroplating method, and a 4 to 7 μm thick Ni—P alloy film as a third layer by electroless plating method, provided that the third layer has a Vicker's hardness of 2.5 to 4.5 with respect to the Vicker's hardness of the Cu or Sn electroplated film provided as the second layer taken as 1.
1 . A process for producing a permanent magnet which is used by inserting it into the slot inside a rotor yoke of an automotive IPM motor, characterized by a production process comprising forming on the surface of an R—Fe—B based permanent magnet a 3 to 15 μm thick Ni film as a first layer by electroplating method, followed by a 3 to 15 μm thick Cu or Sn film as a second layer by electroplating method, and a 4 to 7 μm thick Ni—P alloy film as a third layer by electroless plating method, provided that the third layer has a Vicker's hardness of 2.5 to 4.5 with respect to the Vicker's hardness of the Cu or Sn electroplated film provided as the second layer taken as 1.
2 . The production process as claimed in claim 1 , wherein the film provided as the first layer is formed by using a Ni-plating bath, the pH of which is adjusted to a range of 6.0 to 8.0.
3 . The production process as claimed in claim 1 , wherein the Vicker's hardness value of the film provided as the third layer is in a range of 400 to 700.
4 . The production process as claimed in claim 1 , wherein the film provided as the third layer contains 5 to 12% by weight of P.
5 . The production process as claimed in claim 1 , wherein the total film thickness of the films provided as the first layer to the third layer is in a range of 15 to 25 μm.
6 . A permanent magnet which is used by inserting it into the slot inside a rotor yoke of an automotive IPM motor, characterized by laminating a 3 to 15 μm thick Cu or Sn electroplated film on the surface of an R—Fe—B based permanent magnet with a 3 to 15 μm thick Ni electroplated film interposed, and a 4 to 7 μum thick Ni—P alloy electroless plating film having a Vicker's hardness of 2.5 to 4.5 with respect to the Vicker's hardness of the Cu or Sn electroplated film taken as 1.