Non-aqueous electrolyte secondary battery with high capacity and good life characteristics
View Patent ↗Disclosed is a non-aqueous electrolyte secondary battery comprising a positive electrode containing a nickel-containing lithium composite oxide, a negative electrode containing graphite, and a non-aqueous electrolyte. The cut-off voltage of charge of this non-aqueous electrolyte secondary battery is 4.25 to 4.6 V. The negative electrode contains an additive that reacts with lithium at a potential higher than the potential of graphite. The ratio A/B of a positive electrode capacity A based on the weight of the nickel-containing lithium composite oxide and the cut-off voltage of charge relative to a weight B of the graphite contained in a portion of a negative electrode material mixture layer opposing to a positive electrode material mixture layer is 300 to 340 mAh/g, and the irreversible capacity C of the positive electrode and the irreversible capacity D of the negative electrode in the portion opposing to the positive electrode satisfies C≧D.
1. A non-aqueous electrolyte secondary battery comprising:
a positive electrode comprising a positive electrode material mixture layer including a nickel-containing lithium composite oxide,
a negative electrode comprising a negative electrode material mixture layer including graphite, said negative electrode including an additive that reacts with the lithium at a potential higher than a maximum potential of said graphite during charge and discharge, and
a non-aqueous electrolyte,
wherein:
said battery has a cut-off voltage of charge of 4.25 to 4.6 V,
a ratio A/B of a positive electrode capacity A based on a weight of said nickel-containing lithium composite oxide and said cut-off voltage of charge relative to a weight B of said graphite in a portion of said negative electrode material mixture layer opposing to said positive electrode material mixture layer is 300 to 340 mAh/g,
an irreversible capacity C of said positive electrode and an irreversible capacity D in the portion of said negative electrode material mixture layer opposite said positive electrode material mixture layer satisfies a relation of C>D,
an amount of said additive is 0.5 to 2.9 parts by weight per 100 parts by weight of said graphite, and
said additive is at least one selected from the group consisting of SiO and SiO n (0<n≦1.5).
2. The non-aqueous electrolyte secondary battery in accordance with claim 1 , wherein said additive is included in said negative electrode material mixture layer.
3. The non-aqueous electrolyte secondary battery in accordance with claim 1 , further comprising a separator interposed between said positive electrode and said negative electrode and a layer including said additive laminated on said negative electrode material mixture layer, said layer including said additive being disposed between said negative electrode material mixture layer and said separator.
4. The non-aqueous electrolyte secondary battery in accordance with claim 1 , wherein an amount of said additive is 0.5 to 1.5 parts by weight per 100 parts by weight of said graphite.
5. The non-aqueous electrolyte secondary battery in accordance with claim 1 , wherein said nickel-containing lithium composite oxide is represented by the general formula:
Li x Ni 1-y-z Mn y M z O 2
where 0.99≦x≦1.1, 0<y+z≦0.7, 0<y≦0.4 and M is at least one element selected from Mg, Al, Co, Sr, Y, Zr and Mo.