High performance kaolin pigment, paper coating paint and method for producing such paint
An improvement in high performance kaolin pigment, paper coating paint comprised of high performance kaolin pigment and a method for producing high performance kaolin pigment, wherein only coarse kaolin is used, said pigment exhibiting an ISO whiteness preferably higher than 88.5; a grain size distribution of at least 96% lower than 2 μm and at most 15% lower than 0.2 μm; a Hercules viscosity at 18 dines of at least 200 RPM in pulps with a concentration of solids of 70-71%, thus producing a coating paint that has an ISO whiteness higher than 88.5 and lower than 91.0; a grain size distribution of at least 96% lower than 2 μm and at most 15% lower than 0.2 μm and a Hercvules viscosity at 18 dines of at least 200 RPM in pulps with a solids concentration of 70-71%, said manufacturing process providing an overall recovery of 49%.
1 . An improvement in high performance kaolin pigment set forth in U.S. Pat. No. 6,660,076 wherein the pigment is comprised only of coarse kaolin, said coarse kaolin being composed of large particles in the shape of single plates, a high degree of crystallization, with a Hinckley index higher than 0.6, a size distribution in the sand-free fraction of 55% to 75% lower than 2 μm and at most 15% lower than 0.2 μm.
2 . The improvement in high performance kaolin pigment according to claim 1 , wherein the coarse fraction of coarse kaolin is discarded by using only the fine fraction, and comprises a grain size distribution of at least 96% lower than 2 μm and at most 15% lower than 0.2 μm and an average shape factor of at most 15 in the fine end and of at most 30 in the coarse end.
3 . The improvement in high performance kaolin pigment according to claim 1 , wherein the pigment has an ISO whiteness ranging from 88.5 to 91.0, preferably higher than 88.5; a grain size distribution of at least 96% lower than 2 μm and at most 15% lower than 0.2 μm; a Hercules viscosity at 18 dines of at the least 200 RPM in pulps with a solids concentration of 70-71%.