Method of producing exfoliated graphite, flexible graphite, and nano-scaled graphene platelets
View Patent ↗The present invention provides a method of exfoliating a layered material (e.g., graphite and graphite oxide) to produce nano-scaled platelets having a thickness smaller than 100 nm, typically smaller than 10 nm. The method comprises (a) dispersing particles of graphite, graphite oxide, or a non-graphite laminar compound in a liquid medium containing therein a surfactant or dispersing agent to obtain a stable suspension or slurry; and (b) exposing the suspension or slurry to ultrasonic waves at an energy level for a sufficient length of time to produce separated nano-scaled platelets. The nano-scaled platelets are candidate reinforcement fillers for polymer nanocomposites. Nano-scaled graphene platelets are much lower-cost alternatives to carbon nano-tubes or carbon nano-fibers.
1. A method of exfoliating a layered graphite material to produce separated nano-scaled graphene platelets having a thickness smaller than 100 nm, said method comprising:
a) dispersing particles of a graphite material in a liquid medium containing therein a surfactant or dispersing agent to produce a suspension or slurry, wherein said graphite material has never been subjected to intercalation, chemical oxidation, or exfoliation; and
b) exposing said suspension or slurry to ultrasonication at an energy level for a sufficient length of time to produce said separated nano-scaled platelets.
2. The method of claim 1 wherein said ultrasonication step is conducted at a temperature lower than 100° C.
3. The method of claim 1 wherein said energy level is greater than 80 watts.
4. The method of claim 1 wherein said ultrasonication step is followed by a mechanical shearing treatment selected from air milling, ball milling, rotating blade shearing, or a combination thereof.
5. The method of claim 1 wherein said liquid medium comprises water, organic solvent, alcohol, a monomer, an oligomer, or a resin.
6. The method of claim 1 wherein said platelets have a thickness smaller than 10 nm.
7. The method of claim 1 wherein said surfactant or dispersing agent is selected from the group consisting of anionic surfactants, nonionic surfactants, cationic surfactants, amphoteric surfactants, silicone surfactants, fluoro-surfactants, polymeric surfactants, sodium hexametaphosphate, sodium lignosulphonate, poly (sodium 4 -styrene sulfonate), sodium dodecylsulfate, sodium sulfate, sodium phosphate, sodium sulfonate, and combinations thereof.
8. The method of claim 1 wherein said layered graphite material comprises natural graphite, synthetic graphite, highly oriented pyrolytic graphite, graphite fiber, graphitic nano-fiber, or a combination thereof.
9. The method of claim 1 wherein said liquid medium contains a monomer or a polymer dissolved or dispersed therein to form a nanocomposite precursor suspension.
10. The method of claim 9 further including a step of converting said suspension to a mat or paper, or converting said nanocomposite precursor suspension to a nanocomposite solid.
11. The method of claim 1 further comprising a step of re-compressing said platelets to obtain flexible graphite sheets.