Aqueous dispersion, its production method, and its use
View Patent ↗An aqueous dispersions including (A) at least one ethylene-based polyolefin forming a dispersed polymer phase; (B) at least one dispersing agent; and (C) water; wherein the dispersion has a pH of less than 12; and wherein the dispersed polymer phase has a volume average particle size of less than about 5 microns. In other aspects, an article or a substrate including a coating, wherein the coating was obtained from an aqueous dispersion comprising (A) at least one of an ethylene-based polyolefin and a propylene-based polyolefin; (B) at least one dispersing agent; and (C) water; wherein the dispersion had a pH of less than 12.
1. An aqueous dispersion comprising (A) at least one or more interpolymers of ethylene with at least one comonomer selected from the group consisting of a C 4 -C 20 linear, branched or cyclic diene, and a compound represented by the formula H 2 C═CHR wherein R is a C 2 -C 20 linear, branched or cyclic alkyl group or a C 6 -C 20 aryl group forming a dispersed polymer phase; (B) at least one dispersing agent; and (C) water; wherein the dispersion has a pH of less than 12; wherein the dispersed polymer phase has a volume average particle size of less than 5 microns.
2. The dispersion according to claim 1 , wherein the dispersing agent comprises at least one carboxylic acid, at least one salt of at least one carboxylic acid, at least one carboxylic acid ester, or at least one salt of at least one carboxylic acid ester.
3. The dispersion of claim 1 , wherein the dispersion has a particle size distribution defined as volume average particle diameter (Dv) divided by number average particle diameter (Dn) of less than or equal to 2.0.
4. A film layer comprising: a substrate having a coating, wherein the coating was obtained from: an aqueous dispersion comprising (A) at least one or more interpolymers of ethylene with at least one comonomer selected from the group consisting of a C 4 -C 20 linear, branched or cyclic diene, and a compound represented by the formula H 2 C═CHR wherein R is a C 2 -C 20 linear, branched or cyclic alkyl group or a C 6 -C 20 aryl group forming a dispersed polymer phase; (B) at least one dispersing agent; and (C) water; wherein the dispersion had a pH of less than 12, and wherein the dispersed polymer phase has a volume average particle size of less than 5 microns.
5. The film layer of claim 4 , wherein the coating is heat sealable.
6. The film layer of claim 4 , wherein the substrate comprises at least one thermoplastic polymer selected from the group consisting of polyethylene terephthalate, polyethylene, polycarbonate, polyimide, polyamide, polyphenylene sulfide, polysulfone, aromatic polyester, polyether ether ketone, polyether sulfone, and polyether imide.
7. The film layer of claim 4 , wherein the substrate comprises at least one of aluminum, glass, copper, brass, and steel.
8. The film layer of claim 4 , wherein the interpolymer of ethylene has a density of less than 0.92 g/cc.
9. The film layer of claim 4 , wherein the dispersing agent comprises at least one carboxylic acid, at least one salt of at least one carboxylic acid, at least one carboxylic acid ester, or at least one salt of at least one carboxylic acid ester.
10. An article comprising: a substrate having a coating, wherein the coating was obtained from: an aqueous dispersion comprising (A) at least one or more interpolymers of ethylene with at least one comonomer selected from the group consisting of a C 4 -C 20 linear, branched or cyclic diene, and a compound represented by the formula H 2 C═CHR wherein R is a C 2 -C 20 linear, branched or cyclic alkyl group or a C 6 -C 20 aryl group forming a dispersed polymer phase of; (B) at least one dispersing agent; and (C) water; wherein the dispersion had a pH of less than 12, and wherein the dispersed polymer phase has a volume average particle size of less than 5 microns.
11. The article of claim 10 , wherein the substrate is selected from the group consisting of glass paper, wall paper, fiber, fabric, carpet, wood, metal, or a plastic molded article.
12. The article of claim 10 , wherein the dispersing agent comprises at least one carboxylic acid, at least one salt of at least one carboxylic acid, at least one carboxylic acid ester, or at least one salt of at least one carboxylic acid ester.
13. The article of claim 10 , wherein the dispersion had a particle size distribution defined as volume average particle diameter (Dv) divided by number average particle diameter (Dn) of less than or equal to 2.0.
14. The article of claim 10 , wherein the dispersion was dried at a temperature in the range of less than a melting temperature of the one or more interpolymers of ethylene with at least one comonomer selected from the group consisting of a C 4 -C 20 linear, branched or cyclic diene, and a compound represented by the formula H 2 C═CHR wherein R is a C 2 -C 20 linear, branched or cyclic alkyl group or a C 6 -C 20 aryl group.
15. The article of claim 10 , wherein the dispersion was dried at a temperature in the range of equal to or greater than a melting temperature of the one or more interpolymers of ethylene with at least one comonomer selected from the group consisting of a C 4 -C 20 linear, branched or cyclic diene, and a compound represented by the formula H 2 C═CHR wherein R is a C 2 -C 20 linear, branched or cyclic alkyl group or a C 6 -C 20 aryl group.
16. The article of claim 10 , wherein the article comprises at least two coating layers obtained from: an aqueous dispersion comprising (A) at least one or more interpolymers of ethylene with at least one comonomer selected from the group consisting of a C 4 -C 20 linear, branched or cyclic diene, and a compound represented by the formula H 2 C═CHR wherein R is a C 2 -C 20 linear, branched or cyclic alkyl group or a C 6 -C 20 aryl group; (B) at least one dispersing agent; and (C) water; wherein the dispersion had a pH of less than 12, and wherein the dispersed polymer phase has a volume average particle size of less than 5 microns.