Gypsum composition
View Patent ↗A gypsum composition comprising water, stucco, clay, an amine compound, a polyoxyalkylene, and a comb-branched copolymer is disclosed. The gypsum composition has improved fluidity. A method for preparing the gypsum composition is also disclosed. The method comprises mixing the components to form a slurry, casting the slurry into a product, and drying the product.
1. A method of making the gypsum composition, said method comprising mixing water, stucco, clay, a polyoxyalkylene, an amine compound, and a comb-branched copolymer to form a slurry.
2. The method of claim 1 , further comprising casting a product from the slurry, heating and drying the product.
3. The method of claim 2 , wherein the product is a wallboard.
4. The method of claim 3 , wherein the wallboard contains no other agent added for generating foam or for reducing the density of the wallboard.
5. The method of claim 1 , wherein the clay is present in an amount within the range of about 0.01% to about 10% of the total weight of the gypsum composition.
6. The method of claim 1 , wherein the clay is present in an amount within the range of about 0.05% to about 5% of the total weight of the gypsum composition.
7. The method of claim 1 , wherein the polyoxyalkylene is present in an amount within the range of about 0.01% to about 4% of the total weight of the gypsum composition.
8. The method of claim 1 , wherein the polyoxyalkylene is present in an amount within the range of about 0.1% to about 1% of the total weight of the gypsum composition.
9. The method of claim 1 , wherein the amine compound is present in an amount within the range of about 0.01% to about 4% of the total weight of the gypsum composition.
10. The method of claim 1 , wherein the amine compound is present in an amount within the range of about 0.1% to about 1% of the total weight of the gypsum composition.
11. The method of claim 1 , wherein the amine compound is selected from the group consisting of aliphatic amines, quaternary amines, alkoxylated amines, amine oxides, and mixtures thereof.
12. The method of claim 1 , wherein the comb-branched copolymer is present in an amount within the range of about 0.005% to about 1% of the total weight of the gypsum composition.
13. The method of claim 1 , wherein the comb-branched copolymer is present in an amount within the range of about 0.025% to about 0.5% of the total weight of the gypsum composition.
14. The method of claim 1 , wherein the polyether macromonomer is an acrylate or methacrylate of a propylene oxide and ethylene oxide copolymer.
15. The method of claim 1 , wherein the comb-branched copolymer is at least partially neutralized.