Nanocrystal-containing filtration media
View Patent ↗The invention relates to filtration media having nanocrystals of metal oxides, encapsulated in or impregnated into a binder matrix, which binds together particles of activated carbon. The filtration media can be compressed into a filtration block, has low pressure drop, and has excellent microbial removal properties.
1. A filtration media for water, comprising:
a cylindrical block filtration media, comprising:
a polymeric binder matrix;
a plurality of metal oxide nanoparticles, selected from the group consisting of titanium oxide zinc oxide, aluminum oxide, zirconium oxide, and mixtures thereof, dispersed and encapsulated in the polymeric binder, and
a plurality of activated carbon particles bound together by the polymeric binder.
2. The filtration media of claim 1 , wherein the nanoparticles are present in an amount ranging from about 0.1 wt % to about 10 wt %, based upon the total weight of the filtration media.
3. The filtration media of claim 2 , wherein the nanoparticles are present in an amount of about 0.5 wt %, based on the total weight of the filtration media.
4. The filtration media of claim 1 , wherein the nanoparticles have an average particle size ranging from about 20 nm to about 1000 nm.
5. The filtration media of claim 1 , wherein the activated carbon particles have particle sizes ranging between about 30 μm and about 500 μm.
6. The filtration media of claim 5 , wherein the activated carbon particles have particle sizes ranging between about 30 μm and about 200 μm.
7. The filtration media of claim 1 , wherein the polymeric binder is selected from the group consisting of polyolefins, acrylic resins, nylons, carboxymethylcelluloses, polyvinyl acetates, and blends and copolymers thereof.
8. The filtration media of claim 7 , wherein the polymeric binder is a high-density polyethylene.
9. The filtration media of claim 1 , wherein the weight ratio of nanoparticles to polymeric binder ranges between about 30:1 and about 5:1.
10. The filtration media of claim 9 , wherein the weight ratio of nanoparticles to polymeric binder ranges between about 20:1 and about 10:1.
11. A method of making a filtration media for water, wherein said filtration media comprises a cylindrical block filtration media, comprising: a polymeric binder matrix; a plurality of metal oxide nanoparticles, selected from the group consisting of titanium oxide zinc oxide, aluminum oxide, zirconium oxide, and mixtures thereof, dispersed and encapsulated in the polymeric binder, and a plurality of activated carbon particles bound together by the polymeric binder, comprising:
combining about 0.1 wt % to about 10 wt % metal oxide nanoparticles with about 10 wt % to about 25 wt % particles of polymeric binder and the balance particles of activated carbon;
heating the mixture to a temperature above the melting temperature of the polymeric binder;
compressing the heated mixture at said temperature for a period of time sufficient to allow formation of the cylindrical block filtration media; and
cooling the cylindrical block filtration media to ambient temperature.
12. The method of claim 11 , wherein the metal oxide nanoparticles have particle sizes ranging from about 10 nm to about 1000 nm.
13. The method of claim 11 , wherein the polymeric binder particles have particle sizes ranging from about 5 μm to about 60 μm.
14. The method of claim 11 , wherein the activated carbon particles have particle sizes ranging between about 30 μm and about 500 μm.
15. The method of claim 11 , wherein said combining comprises first mixing the metal oxide nanoparticles and polymeric binder particles using rapid shear mixing, followed by addition of activated carbon particles and additional mixing.
16. A method of making a filtration media for water, wherein said filtration media comprises a cylindrical block filtration media, comprising: a polymeric binder matrix; a plurality of metal oxide nanoparticles, selected from the group consisting of titanium oxide zinc oxide, aluminum oxide, zirconium oxide, and mixtures thereof, dispersed and encapsulated in the polymeric binder, and a plurality of activated carbon particles bound together by the polymeric binder, comprising:
combining about 0.1 wt % to about 10 wt % metal oxide nanoparticles with about 10 wt % to about 25 wt % particles of polymeric binder and the balance particles of activated carbon;
extruding the mixture into a cylindrical block filtration media; and
cooling the cylindrical block filtration media to ambient temperature.