Method for preparing an improved bitumen by addition of polyphosphoric acid and a cross-linkable polymer
View Patent ↗Methods are provided for preparing a bitumen product having improved properties for use in asphalt road paving. In a preferred embodiment, polyphosphoric acid is added to heated bitumen and stirred for a period of time. After addition of the polyphosphoric acid, one or more sulfur-crosslinkable elastomers and one or more sulfur donor coupling agents is added to the heated bitumen and mixed. The polyphosphoric acid, sulfur-crosslinkable elastomers and sulfur donor coupling agents may also be added to separate quantities of bitumen, and the bitumens may be combined prior to use to obtain a final bitumen product having the desired characteristics.
1. A method for producing an improved bitumen comprising the steps of:
(a) providing a first quantity of bitumen or mixture of bitumens heated to a temperature of between about 100° C. to about 230° C.;
(b) adding to the first quantity of bitumen or mixture of bitumens polyphosphoric acid and maintaining the resulting mixture at a temperature of between about 100° C. to about 230° C. while stirring for a period of at least about 10 minutes;
(c) providing a second quantity of bitumen or mixture of bitumens heated to a temperature of between about 100° C. to about 230° C.;
(d) adding to the second quantity of bitumen or mixture of bitumens at least one sulfur cross-linkable elastomer and at least one sulfur-donor coupling agent in an amount capable of providing an amount of free sulfur representing between 0.1% and 20% of the weight of the sulfur cross-linkable elastomer while maintaining the temperature of the bitumen at between 100° C. and 230° C. with stirring for a period of at least about 10 minutes
(e) combining a sufficient amount of the first quantity of bitumen with a sufficient quantity of the second quantity of bitumen to obtain a final bitumen product having polyphosphoric acid in an amount of between about 0.005% to 5% by weight of the weight of the final bitumen product and at least one sulfur cross-linkable elastomer in an amount of between 0.5% to 20% by weight of the weight of the final bitumen product, and wherein the amount of polyphosphoric acid added to the first quantity of bitumen and the amount of the at least one sulfur cross-linkable elastomer added to the second quantity of bitumen are selected to achieve the desired concentrations of polyphosphoric acid and sulfur-crosslinkable elastomer in the final bitumen product.
2. A method for producing an improved bitumen comprising the steps of:
(a) providing a first quantity of bitumen or mixture of bitumens heated to a temperature of between about 100° C. to about 230° C.;
(b) adding to the first quantity of bitumen or mixture of bitumens polyphosphoric acid and at least one sulfur cross-linkable elastomer and maintaining the resulting mixture at a temperature of between about 100° C. to about 230° C. while stirring for a period of at least about 10 minutes;
(c) providing a second quantity of bitumen or mixture of bitumens heated to a temperature of between about 100° C. to about 230° C.;
(d) adding to the second quantity of bitumen or mixture of bitumens at least one sulfur-donor coupling agent in an amount capable of providing an amount of free sulfur representing between 0.1% and 20% of the weight of the sulfur cross-linkable elastomer while maintaining the temperature of the bitumen at between 100° C. and 230° C. with stirring for a period of at least about 10 minutes
(e) combining a sufficient amount of the first quantity of bitumen with a sufficient quantity of the second quantity of bitumen to obtain a final bitumen product having polyphosphoric acid in an amount of between about 0.005% to 5% by weight of the weight of the final bitumen product, at least one sulfur cross-linkable elastomer in an amount of between 0.5% to 20% by weight of the weight of the final bitumen product, and at least one sulfur-donor coupling agent in an amount capable of providing an amount of free sulfur representing between 0.1% and 20% of the weight of the sulfur cross-linkable elastomer and wherein the amount of polyphosphoric acid and sulfur-crosslinkable elastomer added to the first quantity of bitumen and the amount of the at least one sulfur-donor coupling agent added to the second quantity of bitumen are selected to achieve the desired concentrations of polyphosphoric acid, sulfur-crosslinkable elastomers and sulfur-donor coupling agents in the final bitumen product.
3. The method of claim 1 , wherein the cross-linkable elastomer is selected from the group consisting of polyisoprene, polynorbornene, polybutadiene, butyl rubber, random ethylene/propylene (EP) copolymers, random ethylene/propylene/diene (EPDM) terpolymers, a random or block copolymer of styrene and a conjugated diene, and mixtures thereof.
4. The method of claim 1 , wherein the sulfur-donor coupling agent is selected from the group consisting of elemental sulfur, hydrocarbyl polysulfides, sulfur-donor vulcanization accelerators, and mixtures thereof.
5. The method of claim 2 , wherein the cross-linkable elastomer is selected from the group consisting of polyisoprene, polynorbornene, polybutadiene, butyl rubber, random ethylene/propylene (EP) copolymers, random ethylene/propylene/diene (EPDM) terpolymers, a random or block copolymer of styrene and a conjugated diene, and mixtures thereof.
6. The method of claim 2 , wherein the sulfur-donor coupling agent is selected from the group consisting of elemental sulfur, hydrocarbyl polysulfides, sulfur-donor vulcanization accelerators, and mixtures thereof.