Method for synthesis of carbon nanotubes
View Patent ↗The present invention relates to a process for preparing CNTs by bringing a carbon source into contact with a multivalent metal and/or metal-oxide-based catalyst deposited on an inorganic substrate having a BET specific surface area of greater than 50 m 2 /g. The CNTs obtained may be used as agents for improving the mechanical and electrical conductivity properties in polymeric compositions.
1. Process for synthesizing CNTs by decomposition of a carbon source that is brought into contact in a fluidized-bed reactor, at a temperature of between 500 and 1,500° C., with one or more multivalent transition metals with a zero and/or positive oxidation state and recovery of the said CNTs, characterized in that:
said one or more multivalent transition metals is supported on a substrate with a BET specific surface area of between 70 m 2 /g and 300 m 2 /g, and
the quantity of said one or more multivalent transition metals represents from 15 to 50% of the weight of the final catalyst.
2. Process according to claim 1 , characterized in that the quantity of transition metals represents from 30 to 40% of the weight of the final catalyst.
3. Process according to claim 1 , characterized in that the catalyst comprises particles have a diameter between about 20 μm and 500 μm.
4. Process according to claim 1 , characterized in that the catalyst is prepared by impregnating the substrate with an impregnation solution containing at least one salt of said one or more transition metals.
5. Process according to claim 4 , characterized in that the said catalyst is prepared by impregnating the substrate by means of an aqueous iron nitrate solution, and in that the quantity of liquid, at any moment, in contact with the substrate is just sufficient to ensure formation of a surface film on the substrate.
6. Process according to claim 4 , characterized in that the catalyst is reduced in situ and the catalyst and is not exposed to air.
7. Process according to claim 6 , characterized in that it is continuous.
8. Process according to claim 4 , characterized in that the catalyst is based on one or more metal oxides.
9. Process according to claim 8 , characterized in that it is continuous.
10. Process of claim 1 , characterized in that said substrate is an inorganic support.
11. Process of claim 1 , characterized in that said substrate is selected from gamma-type aluminas or theta-type aluminas.
12. Process of claim 5 , characterized in that said nitrate solution is at a temperature between room temperature and the boiling point of the impregnation solution.
13. Process according to claim 6 , characterized in that the catalyst is based on iron.
14. Process according to claim 8 , characterized in that the one or more metal oxides is iron oxide.