Fiber-reinforced composite material and process for producing the same
View Patent ↗Disclosed is a highly transparent fiber-reinforced composite material including an assembly of cellulose fibers of 4 to 200 nm average fiber diameter impregnated with a matrix material so as to not only remedy the moisture absorbency attributed to cellulose fibers but also further improve transparency. There is provided a fiber-reinforced composite material including an assembly of cellulose fibers impregnated with a matrix material. In the fiber-reinforced composite material, hydroxyl groups of cellulose fibers are chemically modified through a reaction with one or more chemical modifiers selected from the group consisting of an acid, an alcohol, a halogenating reagent, an acid anhydride, and an isocyanate so that the ratio of a functional group introduced by the chemical modification is 5 to 40 percent by mole based on the hydroxyl groups of cellulose fibers before the chemical modification. The chemical modification of hydroxyl groups of cellulose fibers can reduce the hydrophilicity of cellulose fibers to thereby reduce the moisture absorbency of fiber-reinforced composite material. Further, the affinity between cellulose fibers and matrix material can be enhanced to thereby further improve transparency.
1. A fiber-reinforced composite material comprising a matrix material and an assembly of cellulose fibers impregnated with the matrix material,
wherein the cellulose fibers are microfibrils of cellulose, which form base skeletons of plant cell walls, or fibers constituting the microfibrils, and
wherein hydroxy groups of the cellulose fibers are chemically modified through a reaction with one or more chemical modifiers selected from the group consisting of an acid, an alcohol, a halogenating reagent, an acid anhydride, and an isocyanate, so that the ratio of a functional group introduced by the chemical modification is 5 to 40 percent by mole based on the hydroxyl groups of cellulose fibers before the chemical modification.
2. The fiber-reinforced composite material according to claim 1 , wherein the functional group is one or more functional groups selected from the group consisting of acetyl group, methacryloyl group, propanoyl group, butanoyl group, iso-butanoyl group, pentanoyl group, hexanoyl group, heptanoyl group, octanoyl group, nonanoyl group, decanoyl group, undecanoyl group, dodecanoyl group, myristoyl group, palmitoyl group, stearoyl group, pivaloyl group, 2-methacryloyloxyethyl isocyanoyl group, methyl group, ethyl group, propyl group, iso-propyl group, butyl group, iso-butyl group, tert-butyl group, pentyl group, hexyl group, heptyl group, octyl group, nonyl group, decyl group, undecyl group, dodecyl group, myristyl group, palmityl group, and stearyl group.
3. The fiber-reinforced composite material according to claim 2 , wherein the functional group is acetyl group and/or methacryloyl group.
4. The fiber-reinforced composite material according to claim 1 , wherein the ratio of the introduced functional group is 10 to 25 percent by mole based on the hydroxy groups of cellulose fibers.
5. The fiber-reinforced composite material according to claim 1 , wherein the assembly of cellulose fibers is an assembly of cellulose fibers having an average fiber diameter of 4 to 200 nm.
6. The fiber-reinforced composite material according to claim 1 , wherein the cellulose fibers are bacterial cellulose.
7. The fiber-reinforced composite material according to claim 1 , wherein the cellulose fibers are isolated from plant fibers.
8. The fiber-reinforced composite material according to claim 7 , wherein the cellulose fibers are prepared by further grinding microfibrillated cellulose fibers.
9. The fiber-reinforced composite material according to claim 1 , wherein the fiber-reinforced composite material has a fiber content of 10 percent by weight or more.
10. The fiber-reinforced composite material according to claim 1 , wherein the matrix material is a synthetic polymer.
11. The fiber-reinforced composite material according to claim 1 , wherein the fiber-reinforced composite material has a moisture regain of 3% or less, and wherein the moisture regain is measured according to the following method of measuring moisture regain:
A sample is left stand at 50° C. in a dry atmosphere for 24 hours, followed by weighing (dry weight W o );
next, the sample is left stand in an atmosphere at a temperature of 20° C. and humidity of 60% until the weight becomes constant, followed by weighing (humid weight W 1 ); and
the moisture regain is determined by calculation based on the dry weight W 0 and the humid weight W 1 according to the following equation:
Moisture regain (%)=( W 1 −W 0 )/ W 0 ×100.
12. A method for manufacturing the fiber-reinforced composite material of claim 1 , the method comprising:
bringing an assembly of cellulose fibers into contact with a reaction liquid comprising the chemical modifier to cause chemical modification as a result of a reaction between hydroxyl groups of the cellulose fibers and the chemical modifier to thereby yield an assembly of modified cellulose fibers;
impregnating the assembly of modified cellulose fibers with an impregnating liquid capable of forming the matrix material; and curing the impregnating liquid.
13. The method of manufacturing a fiber-reinforced composite material, according to claim 12 , the method comprising:
impregnating the assembly of cellulose fibers with water to yield an assembly of hydrated cellulose fibers;
replacing water in the assembly of hydrated cellulose fibers with a first organic solvent; and
replacing the first organic solvent in the assembly of cellulose fibers with the reaction liquid and maintaining the reaction liquid therein.
14. The method of manufacturing a fiber-reinforced composite material, according to claim 13 , further comprising:
replacing the reaction liquid in the assembly of cellulose fibers with a second organic solvent; and
replacing the second organic solvent in the assembly of cellulose fibers with an impregnating liquid capable of forming the matrix material and curing the impregnating liquid.
15. A fiber-reinforced composite material comprising a matrix material and an assembly of cellulose fibers impregnated with the matrix material, wherein the fiber-reinforced composite material has a moisture regain of 3% or less, and wherein the moisture regain is measured according to the method as specified in claim 11 .
16. An organic electroluminescent device using a transparent substrate comprising the fiber-reinforced composite material of claim 1 .
17. A photoreceptor device using a transparent substrate comprising the fiber-reinforced composite material of claim 1 .
18. A fiber-reinforced composite material comprising a matrix material and an assembly of cellulose fibers impregnated with the matrix material, wherein the fiber-reinforced composite material has a moisture regain of 3% or less, and wherein the moisture regain is measured to the following method of measuring moisture regain:
A sample is left stand at 50° C. in a dry atmosphere for 24 hours, followed by weighing (dry weight W 0 );
next, the sample is left stand in an atmosphere at a temperature of 20° C. and humidity of 60% until the weight becomes constant, followed by weighing (humid weight W 1 ); and
the moisture regain is determined by calculation based on the dry weight W 0 and the humid weight W 1 according to the following equation:
Moisture regain (%)=( W 1 −W 0 )/ W 0 ×100.
19. An organic electroluminescent device using a transparent substrate comprising a fiber-reinforced composite material comprising a matrix material and an assembly of cellulose fibers impregnated with the matrix material,
wherein hydroxy groups of the cellulose fibers are chemically modified through a reaction with one or more chemical modifiers selected from the group consisting of an acid, an alcohol, a halogenating reagent, an acid anhydride, and an isocyanate, so that the ratio of a functional group introduced by the chemical modification is 5 to 40 percent by mole based on the hydroxyl groups of cellulose fibers before the chemical modification.
20. A photoreceptor device using a transparent substrate comprising a fiber-reinforced composite material comprising a matrix material and an assembly of cellulose fibers impregnated with the matrix material,
wherein hydroxy groups of the cellulose fibers are chemically modified through a reaction with one or more chemical modifiers selected from the group consisting of an acid, an alcohol, a halogenating reagent, an acid anhydride, and an isocyanate, so that the ratio of a functional group introduced by the chemical modification is 5 to 40 percent by mole based on the hydroxyl groups of cellulose fibers before the chemical modification.