View Patent ↗A rosin based intermediate softening point (ISPR) tackifier has a ring and ball softening point of from 35 to 60° C. A hot-melt pressure-sensitive adhesive (HMPSA) composition contains an elastomeric component, such as a blend of SIS and SB block copolymers, and a tackifying component comprising one or more rosin based ISPRs having a ring and ball softening point of from 35 to 60° C.
1. An intermediate softening point resin (ISPR) comprising:
about 40% to about 80% by weight of a main component comprising at least one rosin based resin having a ring and ball softening point of about 85 to about 125° C.; and
about 20% to about 60% by weight of a modifier component comprising at least one rosin based resin having a low softening point, such that when combined with the main component, the overall ring and ball softening point of the ISPR is within the range of about 35 to about 60° C.
2. The ISPR of claim 1 wherein the main component comprises at least one resin selected from pentaerythritol ester of rosin, or glycol ester of rosin, or polyterpene resin, or mixtures thereof.
3. The ISPR of claim 1 wherein the modifier component comprised at least on resin selected from a polyterpene, a terpene phenolic, a styrenated terpene, or a glycerol ester, or mixtures of two or more thereof.
4. A rosin based intermediate softening point resin (ISPR) having a ring and ball softening point within the range of about 35 to about 60° C.
5. A hot melt pressure-sensitive adhesive (HMPSA) composition, comprising:
(a) one or more styrene-butadiene (SB) block copolymers;
(b) one or more styrene-isoprene-styrene (SIS) block copolymers, or a mixture of SIS and styrene-isoprene (SI) block copolymers; and
(c) a tackifying component comprising a rosin derived resin having a ring and ball softening point of from about 35 to 60° C.
6. The HMPSA composition of claim 5 , wherein (a) and (b) together comprise about 20 to 50% by weight of the HMPSA composition.
7. The HMPSA composition of claim 5 , wherein (a) and (b) together comprise about 25 to 40% by weight of the HMPSA composition.
8. The HMPSA composition of claim 5 , wherein the tackifying component comprises about 50 to 80% by weight of the composition.
9. The HMPSA composition of claim 5 , wherein the tackifying component comprises 60 to 75% by weight of the HMPSA composition.
10. The HMPSA composition of claim 5 , further comprising a positive amount up to 7% by weight of a plasticizer.
11. An adhesive article, comprising:
a facestock; and
a HMPSA composition coated on or laminated to the facestock, the HMPSA composition comprising (a) one or more SB block copolymers, (b) one or more SI and/or SIS block copolymers, and (c) a tackifying component comprising a rosin derived resin having a ring and ball softening point of from 35 to 60° C.