Low density ethylenic polymer composition and method of making the same
View Patent ↗The instant invention is an improved low-density ethylenic polymer composition and method of making the same. The polymer composition according to instant invention includes a major component, and a minor component. The major component is an LDPE resin having a melt index (I 2 ) in the range of about 0.01 dg/min to about 100 dg/min, a M W(abs) /M W(GPC) ratio of about 2.6 or less, and a melt strength of less than (14.0 e (−1.05 * log 10(MI)) )cN Jj16 mmor component is an LDPE resin having a melt index (I 2 ) of less than about 5 dg/min, a molecular weight distribution of greater than about 7, and a M W(abs) /M W(GPC) ratio of at least 2.7. The polymer composition of the instant invention may further include additional components.
1. A composition comprising:
a major component, wherein said major component comprising a high pressure highly branched LDPE resin having a melt index (MI) tested at 190° C. ASTM D1238: 2.16 kg weight dg/minute in the range of about 0.01 dg/min to about 100 dg/min, a M w(abs) /M w(GPC) ratio of about 2.6 or less, and a melt strength of less than (14.0 e (−1.05 * log 10(MI)) )) cN; and
a minor component, wherein said minor component comprising a high pressure highly branched LDPE resin having a melt index (MI) tested at 190° C. ASTM D1238: 2.16 kg weight dg/minute of less than about 5 dg/min, a molecular weight distribution of greater than about 7, and a M w(abs) /M w(GPC) ratio of at least 2.7.
2. The composition according to claim 1 , wherein said minor component having a melt index (MI) tested at 190° C. ASTM D1238: 2.16 kg weight dg/minute in the range of about 0.1 dg/min to about 2.5 dg/min, and a M w(abs) /M w(GPC) ratio of greater than about 3.0.
3. The composition according to claim 1 , wherein said minor component having a melt index in the range of about 0.2 dg/min to about 1.0 dg/min, and a M w(abs) /M w(GPC) ratio of greater than about 3.5.
4. The composition according to claim 1 , wherein said composition comprising from about 1 to about 49 percent by weight of the minor component, based on the total weight of said major and minor components.
5. The composition according to claim 4 , wherein said composition comprising from about 5 to about 30 percent by weight of the minor component, based on the total weight of said major and minor components.
6. The composition according to claim 4 , wherein said composition comprising from about 10 to about 25 percent by weight of the minor component, based on the total weight of said major and minor components.
7. The composition according to claim 1 , wherein said composition comprising from about at least 1 to about 100 percent by weight of both said major and minor components, based on the total weight of said composition.
8. The composition according to claim 1 , wherein the melt strength of said composition being greater than (1.1) (14.0e (−1.05 * log 10(MI)) )cN.
9. The composition according to claim 1 , wherein the melt strength of said composition being greater than (1.2) (14.0 e (−1.05 * log 10(MI)) ) cN.
10. The composition according to claim 1 , wherein said composition further comprising a linear polyethylene.
11. An article comprising:
a polymer composition comprising;
a major component, wherein said first component being a high pressure highly branched LDPE resin having a melt index (MI) tested at 190° C. ASTM D1238: 2.16 kg weight dg/minute in the range of about 0.01 dg/min to about 100 dg/min, a M w(abs) /M w(GPC) ratio of about 2.6 or less, and a melt strength of less than (14.0 e (−1.05 * log 10(MI)) ) cN; and
a minor component, wherein said second component being a high pressure highly branched LDPE resin having a melt index (MI) tested at 190° C. ASTM D1238: 2.16 kg weight dg/minute of less than about 5 dg/min, a molecular weight distribution of greater than about 7, and a M w(abs) /M w(GPC) ratio of at least 2.7.