Heat-sealing compound for sealing aluminium foil and polyethylene terephthalate film to polypropylene, polyvinyl chloride and polystyrene containers
View Patent ↗The invention relates to a heat-sealing system consisting of an olefin polymer or olefin copolymer A, a methacrylate copolymer B, a graft polymer AB that is composed of the aforementioned components, a polyester C and an optional polymer D or an optional polymer blend D A , in addition to a solvent or solvent mixture L. The heat-sealing system is characterised by a high heat resistance, excellent barrier properties and short sealing times in relation to various plastics and aluminium foil or PET film.
1. A heat-sealable coating system in the form of a film-forming dispersion and suitable for sealing different kinds of substrates, comprising:
polymer types, A, B, AB, and C
optionally the polymer types D or D A , and
an organic solvent system L,
wherein
polymer type A is an olefin polymer or olefin copolymer,
polymer type B is a (meth)acrylate copolymer containing standard (meth)acrylates and in total up to 15% by weight of methacrylic acid and/or acrylic acid and/or another polymerizable acid, relative to polymer type B,
polymer type AB is a graft polymer of polymer type A and polymer type B, and
polymer type C is a polyester or a polyester mixture;
optionally there is also an addition of polymer type D which is polyvinyl chloride or polymer type D A which is a polyamide, and
the amount of polymer type A is between 15% and 65% by weight,
the amount of polymer type B is between 15% and 65% by weight,
the amount of polymer type AB is between 15% and 70% by weight,
the amount of polymer type C is between 5% and 50% by weight,
the amount of polymer type D is between 0% and 10% by weight,
the amount of polymer type D A is between 0% and 10% by weight, based on the total mass of the polymer types A, B, AB, C, D, and D A ,
and the mass ratio of the total of polymer types A, B, AB, C, D and D A to the mass of the solvent or solvent mixture L is between 5:1 and 1:5.
2. The heat-sealable coating system suitable for sealing different kinds of substrates, according to claim 1 ,
wherein
the amount of polymer type A is between 20% and 60% by weight,
the amount of polymer type B is between 20% and 60% by weight,
the amount of polymer type AB is between 20% and 65% by weight,
the amount of polymer type C is between 5% and 30% by weight,
the amount of polymer type D is between 0% and 5% by weight, and
the amount of polymer type D A is between 0% and 5% by weight,
based on the total mass of polymer types A, B, AB, C, D and D A .
3. The heat-sealable coating system suitable for sealing different kinds of substrates, according to claim 1 ,
wherein
the amount of polymer type A is between 25% and 55% by weight,
the amount of polymer type B is between 25% and 55% by weight,
the amount of polymer type AB is between 25% and 55% by weight,
the amount of polymer type C is between 10% and 25% by weight,
the amount of polymer type D is between 0% and 5% by weight, and
the amount of polymer type D A is between 0% and 5% by weight,
based on the total mass of polymer types A, B, AB, C, D and D A .
4. The heat-sealing system according to claim 1 ,
Wherein the solvent system is a solvent mixture comprising components
L1.) esters of aliphatic carboxylic acids with aliphatic alcohols and
L2.) aliphatic hydrocarbons,
wherein the weight ratio of L1.) to L2.) being between 1 and 200 and the boiling point of the solvent system under standard conditions being not more than 105 degrees Celsius.
5. The heat-sealing system according to claim 4 ,
wherein
the solvent system comprises a mixture of aliphatic hydrocarbons having 5-12 carbon atoms in the chain, and the chain may also be branched.
6. The heat-sealing system according to claim 4 ,
wherein the solvent system comprises a mixture of esters of aliphatic carboxylic acids having 2-4 carbon atoms in the chain, with aliphatic alcohols having 2-4 carbon atoms in the chain, and the chains may also be branched.
7. The heat-sealing system according to claim 4 ,
wherein the solvent system comprises a mixture of aliphatic hydrocarbons having 5-12 carbon atoms in the chain, and the chain may also be branched, and of a mixture of esters of aliphatic carboxylic acids having 2-4 carbon atoms in the chain with aliphatic alcohols having 2-4 carbon atoms in the chain, and the chain may also be branched.
8. The heat-sealing system according to claim 4 ,
wherein
the volume ratio between esters and aliphatic hydrocarbons is between 1 and 200.
9. The heat-sealing system according to claim 4 ,
wherein
the boiling temperature of the solvent system is between 70 degrees Celsius and 105 degrees Celsius.
10. The heat-sealing system according to claim 4 ,
wherein
the boiling temperature of the solvent system is between 85 degrees Celsius and 100 degrees Celsius.
11. A method of sealing heat-sealable substrates, comprising
applying a coating system of claim 1 to the substrates and heat-sealing the substrates.
12. The method according to claim 11 ,
wherein
an aluminium foil or a polyester film is coated with the coating system and sealed to a plastic selected from the group consisting of the plastics polypropylene, polyethylene, polystyrene, polyester and polyvinyl chloride.
13. The method according to claim 10 ,
wherein
the solvent system comprises a mixture of propyl acetate (40% to 70% by volume), ethyl acetate (24% to 45% by volume) and isooctane (5% to 15% by volume).
14. A packaging system,
wherein
said packaging system is sealed with a heat-sealing system according to claim 1 .
15. A food packaging system,
wherein
said food packaging system is sealed with a heat-sealing system according to claim 1 .