Method of manufacturing a bent pipe
View Patent ↗A bent pipe corresponding to at least API X100 grade and having a base metal with high strength and toughness and a weld metal with high toughness is provided. A steel plate prepared by cooling after hot rolling at a cooling rate at the central portion in the plate thickness direction of at most 5° C. per second at 700-500° C. is formed into a bend mother pipe, which is then heated to 900-1100° C. and subjected to bending, then it is cooled to a temperature of at most 300° C. at a cooling rate in the central portion of the thickness direction of at least 5° C. per second at 700-500° C., after which it is tempered at 300-500° C.
1. A method of manufacturing a bent pipe comprising preparing a steel plate by air cooling at a cooling rate in the central portion of the thickness direction of the plate of less than 5° C. per second in a temperature range of 700-500° C. after hot rolling, preparing a bend mother pipe in the form of a welded steel pipe from the steel plate, performing hot bending of the bend mother pipe, and then cooling at a cooling rate in the central portion of the thickness direction of at least 5° C. per second in a temperature range of 700-500° C. to manufacture a bent pipe having a base metal with a tensile strength which is higher than the tensile strength of the base metal of the bend mother pipe, wherein the bent pipe has a base metal having a steel composition comprising, in mass %, C:0.03%-0.12%, Si: 0.05%-0.50%, Mn: 1.4%-2.2%, S: at most 0.01%, Mo: 0.05%-1.0%, Al: 0.005%-0.06%, N: at most 0.008%, at least one of Cu: 0.05%-1.0%, Ni: 0.05%-2.0%, and Cr: 0.05%-1.0%, at least one of Nb: 0.005%-0.1%, V: 0.005%-0.1%, and Ti: 0.005%-0.03%, and a remainder of Fe and impurities, with the carbon equivalent Ceq given by the following equation being at least 0.45%:
Ceq =C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15.
2. A method of manufacturing a bent pipe as set forth in claim 1 wherein the base metal of the bent pipe further contains at most 0.030 mass % of B.
3. A method of manufacturing a bent pipe as set forth in claim 1 wherein the base metal of the bent pipe contains at most 0.005 mass % of Ca.
4. A method of manufacturing a bent pipe comprising preparing a steel plate by cooling after hot rolling at a cooling rate in the central portion of the thickness direction of the plate of less than 5° C. per second in the temperature range of 700-500° C., preparing a bend mother pipe in the form of a welded steel pipe from the steel plate, heating the bend mother pipe to a temperature range of at least 900° C. to at most 1100° C. and performing bending, then cooling the pipe to a temperature range of at most 300° C. at a cooling rate in the central portion of the thickness direction of at least 5° C. per second in a temperature range of 700-500° C., and subjecting the pipe to tempering in a temperature range from at least 300° C. to at most 500° C., wherein the bent pipe has a base metal having a steel composition comprising, in mass %, C:0.03%-0.12%, Si: 0.05%-0.50%, Mn: 1.4%-2.2%, S: at most 0.01%, Mo: 0.05%-1.0%, Al: 0.005%-0.06%, N: at most 0.008%, at least one of Cu: 0.05%-1.0%, Ni: 0.05%-2.0%, and Cr: 0.05%-1.0%, at least one of Nb: 0.005%-0.1%, V: 0.005%-0.1%, and Ti: 0.005%-0.03%, and a remainder of Fe and impurities, with the carbon equivalent Ceq given by the following equation being at least 0.45%:
Ceq =C+Mn/6+(Cr+Mo+V)/5+(Cu+Ni)/15.
5. A method of manufacturing a bent pipe as set forth in claim 2 wherein the base metal of the bent pipe contains at most 0.005 mass % of Ca.
6. A method of manufacturing a bent pipe as set forth in claim 4 wherein the base metal of the bent pipe further contains at most 0.030 mass % of B.
7. A method of manufacturing a bent pipe as set forth in claim 4 wherein the base metal of the bent pipe contains at most 0.005 mass % of Ca.
8. A method of manufacturing a bent pipe as set forth in claim 6 wherein the base metal of the bent pipe contains at most 0.005 mass % of Ca.