Methods for production of zinc oxide electrodes for alkaline batteries
View Patent ↗A zinc electrode for use in alkaline batteries comprises a mixture of 0.425 to 1.55 volume parts of zinc oxide with a volume part of a metallic oxide chosen from the group consisting of: calcium oxide, barium oxide, and mixtures thereof, together with hydroxy-ethyl cellulose, an oxide dispersant chosen from the group consisting of: soap derivatives, anionic polyelectrolytes, anionic surfactants, and mixtures thereof, and a binder. The electrode is prepared by mixing zinc oxide with the chosen metallic oxide in an aqueous medium such as water or potassium hydroxide, stirring overnight, filtering and drying the mixture, optionally adding a further small amount of zinc oxide, optionally adding other metallic oxides, and adding hydroxy-ethyl cellulose, an oxide dispersant, and a binder. The aqueous paste os slurry thus formed is placed on a conductive substrate, drawn through a sizing gap, cut and dried, to form low cost pasted zinc oxide electrodes.
1. A zinc electrode plate for use in alkaline batteries, comprising:
a conductive substrate;
a slurry or paste comprising:
a mixture comprising zinc oxide and calcium oxide;
a cellulose compound;
an oxide dispersant; and
a binder.
2. The zinc electrode of claim 1 , wherein the mixture further comprises magnesium oxide or barium oxide.
3. The zinc electrode of claim 1 , wherein the cellulose compound is hydroxyl-ethyl cellulose.
4. The zinc electrode of claim 1 , wherein the oxide dispersant is chosen from the group consisting of: soap derivatives, anionic polyelectrolytes, anionic surfactants, and mixtures thereof.
5. The zinc electrode of claim 1 , wherein the binder is dispersed PTFE.
6. The zinc electrode of claim 1 , further comprising a further metallic oxide of 0.01 to 0.04 volume parts of the mixture of claim 1 , said further metallic oxide selected from the group consisting of: bismuth oxide, indium oxide, tin oxide, and mixtures thereof.
7. The zinc electrode of claim 1 , wherein the mixture comprises 0.425 to 1.55 volume parts of zinc oxide and one volume part of calcium oxide.
8. The zinc electrode of claim 1 , wherein the mixture further comprises calcium zincate.
9. A stable zinc-based slurry or paste for use in the production of a zinc negative electrode, comprising a mixture of zinc oxide with calcium oxide, together with a cellulose compound, an oxide dispersant and a binder.
10. The slurry or paste of claim 9 , wherein the mixture further comprises magnesium oxide or barium oxide.
11. The slurry or paste of claim 9 , wherein the cellulose compound is hydroxyl-ethyl cellulose.
12. The slurry or paste of claim 9 , wherein the oxide dispersant is chosen from the group consisting of: soap derivatives, anionic polyelectrolytes, anionic surfactants, and mixtures thereof.
13. The slurry or paste of claim 9 , wherein the binder is dispersed PTFE.
14. The slurry or paste of claim 9 , further comprising a further metallic oxide of 0.01 to 0.04 volume parts of the mixture of claim 1 , said further metallic oxide selected from the group consisting of: bismuth oxide, indium oxide, tin oxide, and mixtures thereof.
15. The slurry or paste of claim 9 , wherein the mixture comprises 0.425 to 1.55 volume parts of zinc oxide and one volume part of calcium oxide.
16. The slurry or paste of claim 9 , wherein the mixture further comprises calcium zincate.
17. The slurry or paste of claim 9 , wherein the slurry or paste is a slurry which is adapted for an electrode coating operation carried out at room temperature.