Non-fibrous high modulus ultra high molecular weight polyethylene tape for ballistic applications
View Patent ↗A non-fibrous ultra high molecular weight polyethylene tape having a width of 1-inch or greater and a modulus of 1,400 grams per denier or greater. The non-fibrous UHMWPE tape is obtained by compression molding ultrahigh molecular weight polyethylene powder at a temperature below its melting point and then drawing and stretching the entire resultant compression molded UHMWPE sheet, with no slitting or splitting of the sheet, at a draw ratio of at least 100:1. The UHMWPE tape can be produced in weights of 6,000 to 90,000 denier or greater. The UHMWPE tape of the present invention minimizes the effect of stress concentrators that are prevalent with fibers and thereby enables the tape to be drawn at much higher draw ratios than is possible with fibrous UHMWPE. When used in ballistics panels, the high modulus high molecular weight polyethylene tape of the present invention improves ballistic performance by providing enhanced dissipation of the impact energy of a projectile.
1. A monolithic non-fibrous ultra high molecular weight polyethylene tape usable in ballistic resistant panels comprising:
ultra high molecular weight polyethylene (UHMWPE) having a viscosity-average molecular weight of 2,000,000 or greater;
a width of from 1.0 to 8.1 inches;
a modulus of 1,400 to 1,600 grams per denier; and
a thickness of between 0.0015 and 0.004 inch.
2. The UHMWPE tape of claim 1 wherein said ultra high molecular weight polyethylene is drawn to a total draw ratio of from 100:1 to 120:1.
3. The UHMWPE tape of claim 1 wherein said tape includes a width to thickness ratio of between 400:1 and 648:1.
4. The UHMWPE tape of claim 1 wherein said tape has a denier of from 6,000 to 19,000.
5. The UHMWPE tape of claim 1 wherein said tape is formed from ultra high molecular weight polyethylene powder having
a crystallinity of at least 76%; and
a heat of fusion of 220 joules/gram or greater.
6. A non-fibrous and monolithic ultra high molecular weight polyethylene tape usable in ballistic resistant panels comprising:
ultra high molecular weight polyethylene (UHMWPE) having a viscosity-average molecular weight of 2,000,000 or greater;
a width of 1.0 to 8.1 inches;
a modulus of 1,400 to 1,600 grams per denier;
a thickness of between 0.0015 and 0.004 inch; and
a denier of 6,000 to 90,000.
7. The UHMWPE tape of claim 6 wherein said tape is formed from UHMWPE powder having
a crystallinity of at least 76%; and
a heat of fusion of 220 joules/gram or greater.