Organic electro-luminescence display device and method for fabricating the same
An organic electro-luminescence display device and a method for fabricating the same are provided. A first substrate and a second substrate are sealed by a sealant. An organic electro-luminescent diode is formed on the first substrate. The sealant contains a frit glass and a light-heat converter. The frit glass can reduce the moisture and oxygen transmission rate by preventing the organic electro-luminescent diode from being thermally decomposed during a curing process. Since the two substrates are encapsulated by the frit glass, the lifetime and reliability of the organic electro-luminescence display device can be increased.
1. An organic electro-luminescence display device comprising:
a first substrate;
a second substrate opposite to the first substrate;
a display element disposed on the first substrate;
a moisture absorbent formed on the second substrate;
a thin film transistor disposed on the first substrate and under the moisture absorbent; and
a sealant formed adjacent the periphery of the first substrate and of the second substrate, wherein the sealant includes a mixture of a powder-type frit glass and at least one of IR dye and carbon black,
wherein the frit glass is disposed between the first substrate and the second substrate and is cured by heat generated by the at least one of the IR dye and the carbon black,
wherein the at least one of the IR dye and the carbon black is uniformly mixed with the powder-type frit glass in the sealant and receives and converts a light energy to heat energy and uniformly supplies the heat energy to the frit glass, thereby reducing a curing time of the frit glass;
wherein the moisture absorbent removes residual moisture and oxygen from a sealed space between the first substrate and the second substrate,
wherein the display element comprises first and second electrodes disposed on the first substrate and having different work functions, an organic layer disposed between the first electrode and the second electrode and having an organic emission layer, and insulating layer patterns having an opening exposing the sub-pixel and disposed on the first electrode,
wherein the insulating layer patterns are formed of photo-resist resin.
2. The organic electro-luminescence display device according to claim 1 , wherein the first electrode is formed by depositing a transparent conductive material and patterned the deposited transparent conductive material in each sub-pixel.
3. The organic electro-luminescence display device according to claim 1 , wherein at least two first electrodes are provided on the first substrate in a matrix form.
4. A method for fabricating an organic electro-luminescence display device, comprising:
preparing a first substrate;
forming a display element on the first substrate;
preparing a second substrate;
forming a moisture absorbent on the second substrate;
forming a thin film transistor on the first substrate and under the moisture absorbent;
uniformly mixing a powder-type frit glass with at least one of IR dye and carbon black to form a mixture of the powder-type frit glass and the at least one of IR dye and the carbon black;
coating the mixture of the powder-type frit glass and the at least one of the IR dye and the carbon black in a periphery of the first or second substrate;
attaching the first substrate to the second substrate;
irradiating light energy to the mixture of the powder-type frit glass and the at least one of the IR dye and the carbon black such that the at least one of the IR dye and the carbon black converts the light energy into heat energy;
curing the powder-type frit glass by using the heat energy generated by the at least one of IR dye and carbon black;
wherein the moisture absorbent removes residual moisture and oxygen from a sealed space between the first substrate and the second substrate;
wherein the display element comprises first and second electrodes disposed on one of the first and second substrates having different work functions and an organic layer disposed between the first electrode and the second electrode and having an organic emission layer.
5. The method according to claim 4 , wherein the display element is formed on the first substrate, the display element further comprises insulating layer patterns having an opening exposing the sub-pixel and disposed on the first electrode connected to the thin film transistor.
6. The method according to claim 4 , wherein the at least one of the IR dye and the carbon black is uniformly mixed with the powder-type frit glass in the sealant and uniformly supplies the heat energy to the frit glass, thereby reducing a curing temperature of the frit glass.
7. The method according to claim 4 , wherein the first substrate and the second substrate are attached to each other by the powder-type frit glass that is cured while being fused by the heat generated by the applied light energy and being cooled.
8. The method according to claim 4 , wherein the light energy is provided only to the mixture of the powder-type frit glass and the at least one of the IR dye and the carbon black.
9. The method according to claim 8 , wherein the light energy is provided only to the mixture of the powder-type frit glass and the at least one of the IR dye and the carbon black, thereby avoiding the display element thermally decomposed.
10. The method according to claim 8 , wherein a beam heater is used to provide light energy only to the region where the mixture of the powder-type frit glass and the at least one of the IR dye and the carbon black is formed, and
wherein the beam heater is a line type or a rectangular type.