Method for manufacturing composite container with different opening sizes
View Patent ↗The present invention relates to a method for manufacturing a composite container with different opening sizes, which is accomplished by winding with fibers impregnated with resin. First, fibers impregnated with resin are wound on a first substrate for winding a first container, wherein first openings are positioned at both ends of the first container. Then, cut the first container into two shells with a first opening each, and slip one of the shells on a second substrate. Next, fibers impregnated with resin is used for winding the second substrate and the shell such that the fibers impregnated with resin wound on the second substrate and the shell are combined to form a second container, where both ends of the second container are the first opening and a second opening with different opening sizes. Thereby, filament winding can be applied for manufacturing containers with different opening sizes on both ends, and the technique of manufacturing and performance of containers are enhanced.
1. A method for manufacturing a composite container with different opening sizes, comprising:
winding the outer surface of a first substrate with first fibers impregnated with resin, for forming a first container with first openings positioned on both ends thereof, respectively;
cutting the first container into two shells with the first opening positioned on one end of each shell, at least a first shell being separated from the first substrate;
slipping the first shell on a second substrate to cap an end portion thereof, the second substrate extending between axial end openings; and
winding to cover the outer surface of the second substrate from one axial end opening thereof to the other and overlay the first shell in conformed manner with second fibers impregnated with resin, for forming a second container with the first opening and a second opening positioned on both ends thereof, respectively.
2. The method of claim 1 , wherein the diameter of the first opening is smaller or greater than the second opening.
3. The method of claim 1 , wherein the material of the first and the second fibers impregnated with resin are chosen from the group consisting of: inorganic or organic fibers, such as glass fibers or carbon fibers, or a combination of the above.
4. The method of claim 1 , wherein the resin materials of each of the first and the second fibers impregnated with resin is thermoplastic or thermosetting resin.
5. The method of claim 1 , further comprising before the step of winding the outer surface of the first substrate with first fibers impregnated with resin, a step of determining the winding pattern of the first fibers impregnated with resin according to the shape of the first substrate.
6. The method of claim 5 , further comprising before the step of determining the winding pattern of the first fibers impregnated with resin according to the shape of the first substrate, a step of installing the first substrate.
7. The method of claim 1 , further comprising before the step of winding the outer surface of the second substrate with second fibers impregnated with resin, a step of determining the winding pattern of the second fibers impregnated with resin according to the shape of the second substrate.
8. The method of claim 7 , further comprising before the step of determining the winding pattern of the second fibers impregnated with resin according to the shape of the second substrate, a step of installing the second substrate.
9. The method of claim 1 , further comprising before the step of cutting the first container into shells with the first opening positioned on one end of each shell, a step of removing at least one shell off the first substrate.
10. The method of claim 1 , further comprising after the step of winding the outer surface of the first substrate with first fibers impregnated with resin, a step of curing the first container.
11. The method of claim 1 , further comprising after the step of winding the outer surface of the second substrate with second fibers impregnated with resin, a step of curing the second container.
12. The method of claim 11 , further comprising after the step of curing the second container, a step of removing at least one second container off the second substrate.
13. The method of claim 1 , wherein the second substrate is an assemble or a soluble substrate.
14. The method of claim 1 , wherein the diameter of the second substrate is greater or smaller than the diameter of the first substrate.