Compositions comprising a mixture of a BAM phosphor and at least one other hexaaluminate
View Patent ↗Disclosed herein are phosphor compositions comprising a BAM phosphor BaMgAl 10 O 17 :Eu 2+ and at least one other hexaaluminate that may also be europium activated. The BAM may be mixed with any number of different kinds of heaxaaluminates having a similar crystal structure. The aluminum ratio may also be adjusted to alter the defect structure or to produce a second phase. Addition of another hexaaluminate to BAM enhances emission intensity and resistance to degradation, which is beneficial to applications such as plasma display panels.
1. A phosphor composition comprising a europium activated BAM phosphor and a hexaaluminate other than the BAM phosphor, the composition represented by the formula:
( x )hexaaluminate+(1 −x )BaMgAl 10 O 17 :Eu 2+
where the hexaaluminate is selected from the group consisting of a β-alumina, a β′-alumina, and a magnetoplumbite, and wherein x ranges from about 0.001 to about 0.999, subject to the proviso that the hexaaluminate is not Ba 0.75 Al 11 O 17.25 :Eu 2+ .
2. A phosphor composition comprising a europium activated BAM phosphor and a hexaaluminate other than the BAM phosphor, the composition represented by the formula:
( x )LnMAl 11 O 19 +(1 −x )BaMgAl 10 O 17 :Eu 2+ ,
where Ln is a trivalent lanthanide, M is a divalent cation, and x ranges from about 0.001 to about 0.5.
3. The phosphor composition of claim 2 , wherein M is an alkaline earth metal selected from the group consisting of Mg, Ca, Sr, and Ba.
4. A phosphor composition comprising a europium activated BAM phosphor and a hexaaluminate other than the BAM phosphor, the composition represented by the formula:
( x )Ln u Al v O w +(1 −x )BaMgAl 10 O 17 :Eu 2+ ,
where Ln is a trivalent lanthanide, x ranges from about 0.001 to about 0.5, u ranges from about 0.67 to about 1, v ranges from about 11 to about 12, and w ranges from about 18 to about 19.
5. A phosphor composition comprising a europium activated BAM phosphor and a hexaaluminate other than the BAM phosphor, the composition represented by the formula:
( x )M′Al 11 O 17 +(1 −x )BaMgAl 10 O 17 :Eu 2+ ,
where M′ is a monovalent cation, and x ranges from about 0.001 to about 0.5.
6. The phosphor composition of claim 5 , wherein the M′ cation is selected from the group consisting of Li, Na, K, Rb, and Cs.
7. A phosphor composition comprising a europium activated BAM phosphor and a hexaaluminate other than the BAM phosphor, the composition represented by the formula:
( x )M′ 1.5 Al 10.5 O 16.5 +(1 −x )BaMgAl 10 O 17 :Eu 2+ ,
where M′ is a monovalent cation, and x ranges from about 0.001 to about 0.5.
8. The phosphor composition of claim 7 , wherein the M′ cation is selected from the group consisting of Li, Na, K, Rb, and Cs.
9. A phosphor composition comprising a europium activated BAM phosphor and a hexaaluminate other than the BAM phosphor, the composition represented by the formula:
x ( y MO.6Al 2 O 3 )+(1 −x )BaMgAl 10 O 17 :Eu 2+ ,
where M is a divalent cation, and x ranges from about 0.001 to about 0.5, and y ranges from about 1.28 to about 1.32.
10. A method of synthesizing a phosphor composition comprising a europium activated BAM phosphor and a hexaaluminate other than the BAM phosphor, the composition represented by the formula:
( x )hexaaluminate+(1 −x )BaMgAl 10 O 17 :Eu 2+ ,
wherein x ranges from about 0.001 to about 0.999, and wherein the synthesis method is selected from the group consisting of liquid processing methods, co-precipitation methods, and sol-gel methods, subject to the proviso that the hexaaluminate is not Ba 0.75 Al 11 O 17.25 :Eu 2+ .
11. A method of synthesizing a phosphor composition comprising a europium activated BAM phosphor and a hexaaluminate other than the BAM phosphor, the composition represented by the formula:
( x )hexaaluminate+(1 −x )BaMgAl 10 O 17 :Eu 2+ ,
wherein x ranges from about 0.001 to about 0.999, and wherein the synthesis method comprises:
(a) dissolving the precursor metal salts in an aqueous based solution;
(b) co-precipitating an intermediate product;
(c) removing at least a portion of the water from step (b);
(d) calcining the product of step (c); and
(e) sintering the product of step (d).