Pretreated aggregate for hotmix asphalt concrete applications and other related applications
A process of producing an asphalt concrete with enhanced performance is provided by utilizing a primer comprising uintahite and an augmenter. The primer is added to a hot aggregate with a surface temperature of at least 250 deg. F. prior to addition of an asphalt-derived base binder. The primer forms a primer interlayer between the hot aggregate and the base binder. As a result, the asphalt concrete has enhanced performance when compared with other asphalt concretes produced without a primer being added.
1. A process for producing an aggregate and base binder combination with enhanced performance utilizing a primer, comprising:
(a) supplying a hot aggregate with a surface temperature of at least 380 deg. F.;
(b) mixing the hot aggregate with a primer comprising a natural asphalt from the American Gilsonite Company with a trademarked name of Gilsonite, whose non-trademark name is uintahite and an augmenter, the augmenter comprising a processing agent, for a period of time sufficient to melt the primer onto at least a portion of the aggregate surface, the melted primer forming a primer layer over at least the portion of the aggregate surface; and
(c) mixing an asphalt base binder with the hot aggregate at least partially covered with the primer layer such that the primer layer forms a primer interlayer between the hot aggregate and the base binder, the resulting combination having enhanced performance when compared with an aggregate and base binder combination in the absence of the prime.
2. The process of claim 1 , wherein said aggregate and base binder combination comprises a material selected from the group consisting of: an asphalt concrete, a roofing chips, and chips for chip seal applications.
3. The process of claim 1 , wherein the enhanced performance comprises enhanced fatigue life, enhanced rut and shoving resistance, and better retaining of low temperature properties of the base binder.
4. The process of claim 1 , wherein the processing agent is selected from the group consisting of an oligiomeric wax, a derivative if an oligiomeric wax, low molecular weight polyolefins, and combinations thereof.
5. The process according claim 4 , wherein the derivative of an oligiomeric wax comprises a carboxylated derivative of the oligiomeric wax.
6. The process according claim 1 , wherein the primer comprises between about 3% to about 10% by weight of the total binder.
7. The process according claim 1 , wherein the period of time sufficient to melt the primer onto at least a portion of the aggregate surface is about 3 to 10 seconds.
8. The process according claim 1 , wherein said mixing the primer includes utilizing a method selected from the group consisting of utilizing a bulk silo, utilizing a supersack, utilizing a meltable bag, and utilizing an auger.
9. The process according claim 1 , wherein the aggregate comprises recycled asphalt pavement.
10. An aggregate and base binder combination having enhanced performance, comprising:
(a) a hot aggregate with a surface temperature of at least 380 deg. F;
(b) a primer that has been added to the hot aggregate prior to addition of an asphalt base binder, the primer being melted on to at least a portion of the hot aggregate and subsequently forming a primer interlayer between the hot aggregate and the base binder; and
(c) the asphalt base binder, the resulting combination having enhanced performance when compared with an aggregate and base binder combination without a primer being added, wherein the primer comprises an asphalt component and an augmenter, the augmenter comprising a processing agent, and wherein the asphalt component comprises a natural asphalt from the American Gilsonite Company with a trademarked name of Gilsonite, whose non-trademark name is uintahite.
11. The combination of claim 10 , wherein the processing agent is selected from the group consisting of an oligiomeric wax, a derivative of an oligiomeric wax, a low molecular weight polyolefins, and combinations thereof.
12. The combination of claim 11 , wherein the derivative of an oligiomeric wax comprises a carboxylated derivative of the oligiomeric wax.
13. The combination of claim 10 , wherein the primer comprises between about 3% to about 10% by weight of the total binder.
14. The combination of claim 10 , wherein the aggregate comprises recycled asphalt pavement.
15. The combination of claim 10 , wherein the asphalt component further comprises Trinidad Lake Asphalt.
16. The combination of claim 10 , wherein said combination comprises a material selected from the group consisting of: an asphalt concrete, a roofing chips, and chips for chip seal applications.
17. A process for producing an aggregate and base binder combination with enhanced performance utilizing a primer, comprising:
(a) supplying a hot aggregate with a surface temperature of at least 250 deg. F.;
(b) mixing a primer and a hot aggregate for a period of time sufficient to melt the primer onto at least a portion of the aggregate surface, the melted primer forming a primer over at least the portion of the aggregate surface; and
(c) mixing an asphalt base binder with the hot aggregate at least partially covered with the primer layer such that the primer layer forms a primer interlayer between the hot aggregate and the base binder, the resulting combination having enhanced performance when compared with an aggregate and base binder combination in the absence of the primer, wherein the primer comprises an asphalt component and an augmenter, the augmenter comprising a processing agent, and wherein the asphalt component comprises Trinidad Lake Asphalt.
18. The process of claim 17 , wherein said aggregate and base binder combination comprises a material selected from the group consisting of: an asphalt concrete, a roofing chips, and chips for chip seal applications.
19. The process of claim 17 , wherein the primer further comprises a processing agent, the Trinidad Lake Asphalt being added in a four-to-one to twenty-to-one ratio to the processing agent.
20. The process of claim 17 , wherein the asphalt component further comprises a natural asphalt from the American Gilsonite Company with a trademarked name of Gilsonite, whose non-trademark name is uintahite.
21. An aggregate and base binder combination having enhanced performance comprising:
(a) a hot aggregate with a surface temperature of at least 250 deg. F.;
(b) a primer that has been added to the hot aggregate prior to addition of an asphalt base binder, the primer being melted on to at least a portion of the hot aggregate and subsequently forming a primer interlayer between the hot aggregate and the base binder; and
(c) the asphalt base binder, the resulting combination having enhanced performance when compared with an aggregate and base binder combination without a primer being added, wherein the primer comprises and asphalt component and an augmenter, the augmenter comprising a processing agent, and wherein the asphalt component comprises Trinidad Lake Asphalt.
22. The combination of claim 21 , wherein the hot aggregate has a surface temperature of at least 340 deg. F.
23. The combination of claim 21 , wherein the hot aggregate has a surface temperature of at least 380 deg. F.
24. The combination of claim 21 , wherein the processing agent is selected from the group consisting of an oligiomeric wax, a derivative of an oligiomeric wax, a low molecular weight polyolefins, and combinations thereof.
25. The combination of claim 24 , wherein the derivative of an oligiomeric wax comprises a carboxylated derivative of the oligiomeric wax.
26. The combination of claim 21 , wherein the primer further comprises a processing agent, the Trinidad Lake Asphalt being in a four-to-one to twenty-to-one ratio to the processing agent.
27. The combination of claim 21 , wherein the primer comprises between about 3% to about 10% by weight of the total binder.
28. The combination of claim 21 , wherein the aggregate comprises recycled asphalt pavement.
29. The combination of claim 21 , wherein the asphalt component further comprises a natural asphalt from the American Gilsonite Company with a trademarked name of Gilsonite, whose non-trademarked name is uintahite.
30. The combination of claim 21 , wherein said combination comprises a material selected from the group consisting of: an asphalt concrete, a roofing chips, and chips for chip seal applications.