Interlayers comprising stabilized tungsten oxide agents
View Patent ↗The present invention includes polymer interlayers that are used in multiple layer glazing panels. Interlayers of the present invention comprise a thermoplastic polymer, a plasticizer, a tungsten oxide agent, and a stabilizing agent that prevents the degradation of the tungsten oxide agent. Interlayers incorporating such components have improved ultraviolet light blocking character, and also maintain optical quality over time.
1. An interlayer for use in a multiple layer glazing, comprising:
poly(vinyl butyral);
a tungsten oxide agent;
a sole ultraviolet absorber selected from the group consisting of: a molecule having the structural formula
a molecule having the structral formula
and combination thereof; and
a multivalent metal salt;
wherein the sole ultraviolet absorber and the multivalent metal salt are added in an effective amount to reduce the interlayer's decrease in visible light transmittance to about six percent or less, after the interlayer has had exposure to ultraviolet radiation in a weatherometer for 500 hours, and to thereby inhibit a blue color shift due to ageing effects of the tungsten oxide agent in said interlayer; and
wherein said interlayer comprises 0.05 to 0.5 weight percent of said tungsten oxide agent.
2. The interlayer of claim 1 , wherein said interlayer comprises 0.05 to less than about 0.1 weight percent of said tungsten oxide agent.
3. The interlayer of claim 1 , wherein said tungsten oxide agent is described by the general formula W y O z , wherein W is tungsten, O is oxygen, and satisfying 2.0<z/y<3.0, and those described by the general formula M x W y O z where M is an element selected from H, He, alkali metals, alkaline-earth metals, rare-earth metals, Mg, Zr, Cr, Mn, Fe, Ru, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, Au, Zn, Cd, Al, Ga, In, Ti, Si, Ge, Sn, Pb, Sb, B, F, P, S, Se, Br, Te, Ti, Nb, V, Mo, Ta, and Re, W is tungsten, O is oxygen, and satisfying 0.001≦x/y≦1.0 and 2.0≦z/y≦3.0.
4. The interlayer of claim 1 , wherein said tungsten oxide is present in an amount sufficient to block 70% to 95% of near infrared light.
5. The interlayer of claim 1 , wherein said tungsten oxide is present in an amount sufficient to block 95% or more of infrared radiation in the 800 nanometer to 2500 nanometer range.
6. The interlayer of claim 1 , wherein the interlayer's decrease in visual light transmittance is effectively reduced to about two percent or less, after the interlayer has had exposure to ultraviolet radiation in a weatherometer for 500 hours.
7. The interlayer of claim 1 , wherein the interlayer's decrease in visual light transmittance is effectively reduced to about 0.2 percent or less, after the interlayer has had exposure to ultraviolet radiation in a weatherometer for 500 hours.
8. A multiple layer glazing panel, comprising:
a sheet of glass; and,
an interlayer in contact with said sheet of glass, where said interlayer comprises:
poly(vinyl butyral);
a tungsten oxide agent;
a sole ultraviolet absorber selected from the group consisting of: a molecule having the structural formula
a molecule having the structral formula
and combination thereof; and
magnesium bis(2-ethylbutyrate);
wherein the sole ultraviolet absorber and magnesium bis(2-ethylbutyrate) are added in an effective amount to reduce the interlayer's decrease in visible light transmittance to about six percent or less, after the interlayer has had exposure to ultraviolet radiation in a weatherometer for 500 hours, and to thereby inhibit a blue color shift due to ageing effects of the tungsten oxide agent in said interlayer; and
wherein said interlayer comprises 0.05 to 0.5 weight percent of said tungsten oxide agent.
9. The panel of claim 8 , wherein said interlayer comprises 0.05 to less than about 0.1 weight percent of said tungsten oxide agent.
10. The panel of claim 8 , wherein said tungsten oxide agent is described by the general formula W y O z , wherein W is tungsten, O is oxygen, and satisfying 2.0<z/y<3.0, and those described by the general formula M x W y O z where M is an element selected from H, He, alkali metals, alkaline-earth metals, rare-earth metals, Mg, Zr, Cr, Mn, Fe, Ru, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, Au, Zn, Cd, Al, Ga, In, Tl, Si, Ge, Sn, Pb, Sb, B, F, P, S, Se, Br, Te, Ti, Nb, V, Mo, Ta, and Re, W is tungsten, O is oxygen, and satisfying 0.001≦x/y≦1.0 and 2.0≦z/y≦3.0.
11. The panel of claim 8 , wherein said tungsten oxide is present in an amount sufficient to block 70% to 95% of near infrared light.
12. The panel of claim 8 , wherein the interlayer's decrease in visual light transmittance is effectively reduced to about two percent or less, after the interlayer has had exposure to ultraviolet radiation in a weatherometer for 500 hours.
13. An interlayer for use in a multiple layer glazing, comprising:
poly(vinyl butyral);
a tungsten oxide agent;
a sole ultraviolet absorber selected from the group consisting of: a molecule having the structural formula
a molecule having the structural formula
and combination thereof; and
magnesium bis(2-ethylbutyrate);
wherein the sole ultraviolet absorber and magnesium bis(2-ethylbutyrate) are added in an effective amount reduce the interlayer's decrease in visible light transmittance to about six percent to about one tenth of a percent, after the interlayer has had exposure to ultraviolet radiation in a weatherometer for 500 hours, and to thereby inhibit a blue color shift due to ageing effects of the tungsten oxide agent in said interlayer; and
wherein said interlayer comprises 0.05 to 0.5 weight percent of said tungsten oxide agent.
14. An interlayer for use in a multiple layer glazing, comprising:
poly(vinyl butyral);
cesium tungsten oxide;
a sole ultraviolet absorber selected from the group consisting of: a molecule having the structural formula
a molecule having the structural formula
and combination thereof; and
a multivalent metal salt;
wherein the sole ultraviolet absorber and the multivalent metal salt are added in an effective amount to reduce the interlayer's decrease in visible light transmittance to about six percent to about one tenth of a percent, after the interlayer has had exposure to ultraviolet radiation in a weatherometer for 500 hours, and to thereby inhibit a blue color shift due to ageing effects of the cesium tungsten oxide in said interlayer; and
wherein said interlayer comprises 0.05 to 0.5 weight percent of said tungsten oxide agent.
15. An interlayer for use in a multiple layer glazing, comprising:
poly(vinyl butyral);
cesium tungsten oxide;
magnesium bis(2-ethylbutyrate); and
a sole ultraviolet absorber having the structure:
wherein magnesium bis(2-ethylbutyrate) and the sole ultraviolet absorber having the above structure are added in an effective amount to reduce the interlayer's decrease in visible light transmittance to about six percent to about one tenth of a percent, after the interlayer has had exposure to ultraviolet radiation in a weatherometer for 500 hours, and to thereby inhibit a blue color shift due to ageing effects of the cesium tungsten oxide in said interlayer; and
wherein said interlayer comprises 0.05 to 0.5 weight percent of said tungsten oxide agent.
16. An interlayer for use in a multiple layer glazing, comprising:
poly(vinyl butyral);
cesium tungsten oxide;
magnesium bis(2-ethylbutyrate); and
a sole ultraviolet absorber having the structure:
wherein magnesium bis(2-ethylbutyrate) and the sole ultraviolet absorber having the structure above are added in an effective amount to reduce the interlayer's decrease in visible light transmittance to about six percent to about one tenth of a percent, after the interlayer has had exposure to ultraviolet radiation in a weatherometer for 500 hours, and to thereby inhibit a blue color shift due to ageing effects of the cesium tungsten oxide in said interlayer; and
wherein said interlayer comprises 0.05 to 0.5 weight percent of said tungsten oxide agent.