Cement dispersant and methods of making and using the same
View Patent ↗The present invention relates to cement dispersant that is a copolymerization product of a first monomer (A) comprising a carboxylic acid, a second monomer (B) comprising an alkoxylated allyl alcohol sulfate, and, optionally, a third monomer (C) comprising an alkoxylated allyl alcohol. The cement dispersant according to the invention provides improved slump life properties and water reduction properties in cement admixtures.
1. A dispersant composition for improving the slump properties of a cement admixture, the dispersant composition comprising a terpolymer comprised of a random combination of structural units (A), (B) and (C) remaining after polymerization, wherein:
(A) is one or more monomers having functional groups selected from the group consisting of carboxylic acids, amido carboxylic acids, C1-C6 alkyl esters of carboxylic acids, C1-C6 alkyl ester of amido carboxylic acids, hydroxylated C1-C6 alkyl esters of carboxylic acids, hydroxylated C1-C6 alkyl esters of amido carboxylic acids and sulfonic acids:
(B) is according to Formula (I):
where “R1” is (CH 2 —CH 2 —O)n or (CH 2 —CH(CH 3 )—O)n or a mixture of both and “n” is an integer ranging from about 1 to about 100; and “M” is sodium, potassium, calcium, ammonium or an organic amine; and
(C) is according to Formula (II):
where “R2” is H or a C1-C4 straight or branched alkyl chain; “R3” is CH 2 or C═O; “R4” is (CH 2 -CH 2 —O)m or (CH 2 —CH(CH 3 )—O)m or a mixture of both and “m” is an integer ranging from about 1 to about 150; and “R5” is H or a C1-C18 straight or branched alkyl chain.
2. The dispersant composition of claim 1 , wherein (A) is one or more selected from the group consisting of acrylic acid, methacrylic acid, acrylamide, maleic acid, maleic anhydride, fumaric acid, itaconic acid, 2-acrylamido-2-methylpropanesulfonic acid, and water-soluble salts thereof.
3. The dispersant composition of claim 1 , wherein (B) comprises an allyl alcohol that has been ethoxylated, propoxylated, or both, followed by the addition of sulfamic acid to form an end terminal sulfate group that is covalently bonded through an oxygen atom.
4. The dispersant composition of claim 1 , wherein (B) is an ammonium allylpolyethoxy sulfate alkoxylated with an average of up to about 100 moles of ethylene oxide.
5. The dispersant composition of claim 1 , wherein (B) is an ammonium allylpolyethoxy sulfate alkoxylated with an average of up to about 50 moles of ethylene oxide.
6. The dispersant composition of claim 1 , wherein (C) is one or more selected from the group consisting of polyethylene glycol allyl ether (PEGAE), polypropylene glycol allyl ether (PPGAE), polyethylene glycol/polypropylene glycol allyl ether (PEGPGAE), hydroxyethyene glycol methylmethacrylate (HEME), and methoxyethyene glycol methylnnethacrylate (MEME).
7. The dispersant composition of claim 1 , wherein the molar ratio of (A) to (B) to (C) in the terpolymer is in a range of from about 1 to about 10 for (A), from about 1 to about 4 for (B), and from about 1 to about 10 for (C).
8. The dispersant composition of claim 1 , wherein the molar ratio of (A) to (B) to (C) in the terpolymer is in a range of from about 2.5 to about 6 for (A), from about 1 to about 2 for (B), and from about 1 to about 3 for (C).
9. The dispersant composition of claim 1 , wherein (A) is acrylic acid and (B) is an allyloxypolyethylene glycol sulfate ammonium salt.