View Patent ↗Methods of oxidizing multiwalled carbon nanotubes are provided. The multiwalled carbon nanotubes are oxidized by contacting the carbon nanotubes with gas-phase oxidizing agents such as CO 2 , O 2 , steam, N 2 O, NO, NO 2 , O 3 , and ClO 2 . Near critical and supercritical water can also be used as oxidizing agents. The multiwalled carbon nanotubes oxidized according to methods of the invention can be used to prepare rigid porous structures which can be utilized to form electrodes for fabrication of improved electrochemical capacitors.
1. An electrode prepared according to a method comprising:
contacting multiwalled carbon nanotubes with a gas-phase oxidizing agent under conditions sufficient to form oxidized carbon nanotubes;
wherein said multiwalled carbon nanotubes are grown on a supported catalyst, and said electrode includes said supported catalyst.
2. The electrode of claim 1 , wherein said carbon nanotubes comprise multiwalled carbon nanotubes with a diameter no greater than 1 micron.
3. The electrode of claim 1 , wherein said gas-phase oxidizing agent is selected from the group consisting of CO 2 , O 2 , steam, H 2 O, N 2 O, NO, NO 2 , O 3 , ClO 2 and mixtures thereof.
4. The electrode of claim 1 , wherein said oxidized carbon nanotubes exhibit an acid titer of from about 0.05 meq/g to about 0.6 meq/g.
5. The electrode of claim 1 , wherein said oxidized carbon nanotubes comprise moieties selected from the group consisting of carbonyl, carboxyl, hydroxy, aldehydes, ketones, phenols, esters, lactones, derivatives thereof, and mixtures thereof.
6. An electrochemical capacitor comprising the electrode of claim 1 .
7. An electrode prepared according to the method of claim 1 , further comprising:
dispersing said oxidized carbon nanotubes in a liquid medium to form a slurry;
filtering and drying said slurry to form a mat of oxidized carbon nanotubes; and
subjecting said mat to conditions sufficient to cause crosslinking of said oxidized carbon nanotubes.
8. The electrode of claim 7 , wherein said carbon nanotubes comprise aggregates of carbon nanotubes.
9. The electrode of claim 7 , wherein said conditions of the subjecting said mat to conditions sufficient to cause crosslinking of said oxidized carbon nanotubes step includes heating said mat from 180° C. to 350° C.
10. The electrode of claim 7 , wherein said gas-phase oxidizing agent is selected from the group consisting of CO 2 , O 2 , steam, H 2 O, N 2 O, NO, NO 2 , O 3 , ClO 2 and mixtures thereof.
11. The electrode of claim 7 , wherein said contacting in the contacting carbon nanotubes with gas-phase oxidizing step results in oxidized carbon nanotubes exhibiting an acid titer of from about 0.05 meq/g to about 0.6 meq/g.
12. An electrochemical capacitor comprising the electrode of claim 7 .
13. An electrode formed according to the method of claim 1 , further comprising:
dispersing carbon nanotubes prepared in a liquid medium to form a slurry; and
filtering and drying said slurry to form a mat of carbon nanotubes; wherein the step of contacting carbon nanotubes with a gas-phase oxidizing agent under conditions sufficient to form oxidized carbon nanotubes comprises treating said mat with a gas-phase oxidizing agent under conditions sufficient to form oxidized carbon nanotubes.
14. The electrode of claim 13 , wherein said carbon nanotubes comprise aggregates of carbon nanotubes.
15. The electrode of claim 13 , wherein said gas-phase oxidizing agent is selected from the group consisting of CO 2 , O 2 , steam, H 2 O, N 2 O, NO, NO 2 , O 3 , ClO 2 and mixtures thereof.
16. The electrode of claim 13 , wherein said treating in the filtering and drying said slurry to form a mat of oxidized carbon nanotubes step results in oxidized carbon nanotubes exhibiting an acid titer of from about 0.05 meq/g to about 0.6 meq/g.
17. An electrochemical capacitor comprising the electrode of claim 13 .
18. A mat prepared according to a method comprising:
contacting multiwalled carbon nanotubes with a gas-phase oxidizing agent under conditions sufficient to form oxidized carbon nanotubes;
wherein said multiwalled carbon nanotubes are grown on a supported catalyst, and said mat includes said supported catalyst.
19. An assemblage prepared according to a method comprising:
contacting multiwalled carbon nanotubes with a gas-phase oxidizing agent under conditions sufficient to form oxidized carbon nanotubes;
wherein said multiwalled carbon nanotubes are grown on a supported catalyst, and said assemblage includes said supported catalyst.
20. A rigid porous structure prepared according to a method comprising:
contacting multiwalled carbon nanotubes with a gas-phase oxidizing agent under conditions sufficient to form oxidized carbon nanotubes;
wherein said multiwalled carbon nanotubes are grown on a supported catalyst, and said rigid porous structure includes said supported catalyst.