Injection molded article and composition for the preparation thereof
View Patent ↗A composition containing particular amounts of a poly(arylene ether), a poly(arylene sulfide), an electrically conductive carbon black, and glass fibers is particularly useful for molding heat-resistant articles suitable for electrostatic painting. Compared to a corresponding composition without the poly(arylene ether), the composition exhibits improved paint attraction and markedly improved paint adhesion, and it allows the use of a lower level of conductive carbon black to achieve the same electrical conductivity. The composition thus provides an excellent balance of impact strength, electrical conductivity, and paint attraction and adhesion.
1. A composition comprising:
5 to 25 weight percent of a poly(arylene ether),
35 to 63 weight percent of a poly(arylene sulfide),
1.7 to 5 weight percent of an electrically conductive carbon black, and
20 to 50 weight percent of glass fibers;
wherein all weight percents are based on the total weight of the composition;
wherein the weight ratio of electrically conductive carbon black to poly(arylene sulfide) is at least 0.048; and
wherein the composition exhibits
a volume resistivity less than or equal to 1,000,000 ohm-centimeters, measured at 23° C. according to ASTM D6095,
a paint adhesion rating of at least 3 B measured according to ASTM D3359, Method B, and
an unnotched Izod impact strength of at least 150 Joules/meter, measured at 23° C. according to ASTM D256.
2. The composition of claim 1 , wherein the composition exhibits
a volume resistivity of 100 to 1,000,000 ohm-centimeters, measured at 23° C. according to ASTM D6095,
a paint adhesion rating of 3 B or 4 B or 5 B measured according to ASTM D3359, Method B, and
an unnotched Izod impact strength of 150 to 250 Joules/meter, measured at 23° C. according to ASTM D256.
3. The composition of claim 1 , wherein the composition further comprises 2 to 5 weight percent of a processing aid that is a liquid at 25° C. and one atmosphere and that is selected from the group consisting of triaryl phosphates, polyolefins, polytetrafluoroethylenes, mineral oil, and mixtures thereof.
4. The composition of claim 1 , wherein the composition is free of a compatibilizing agent for the poly(arylene ether) and the poly(arylene sulfide).
5. The composition of claim 1 ,
wherein the composition comprises
8 to 15 weight percent of the poly(arylene ether),
40 to 50 weight percent of the poly(arylene sulfide),
2 to 3 weight percent of the electrically conductive carbon black, and
20 to 45 weight percent of the glass fibers;
wherein the weight ratio of electrically conductive carbon black to poly(arylene sulfide) is 0.048 to 0.07; and
wherein the composition exhibits
a volume resistivity of 100 to 100,000 ohm-centimeters, measured at 23° C. according to ASTM D6095,
a paint adhesion rating of 3 B or 4 B or 5 B measured according to ASTM D3359, Method B, and
an unnotched Izod impact strength of 150 to 250 Joules/meter, measured at 23° C. according to ASTM D256.
6. The composition of claim 5 , wherein the composition further comprises 2 to 5 weight percent of a processing aid that is a liquid at 25° C. and one atmosphere and that is selected from the group consisting of triaryl phosphates, polyolefins, polytetrafluoroethylenes, mineral oil, and mixtures thereof.
7. The composition of claim 5 , wherein the composition is free of a compatibilizing agent for the poly(arylene ether) and the poly(arylene sulfide).
8. An injection molded article, comprising:
a product of injection molding a composition comprising
5 to 25 weight percent of a poly(arylene ether),
35 to 63 weight percent of a poly(arylene sulfide),
1.7 to 5 weight percent of an electrically conductive carbon black, and
20 to 50 weight percent of glass fibers;
wherein all weight percents are based on the total weight of the composition;
wherein the weight ratio of electrically conductive carbon black to poly(arylene sulfide) is at least 0.048; and
wherein the composition exhibits
a volume resistivity less than or equal to 1,000,000 ohm-centimeters, measured at 23° C. according to ASTM D6095,
a paint adhesion rating of at least 3 B measured according to ASTM D3359, Method B, and
an unnotched Izod impact strength of at least 150 Joules/meter, measured at 23° C. according to ASTM D256.
9. The injection molded article of claim 8 , wherein the composition exhibits
a volume resistivity of 100 to 1,000,000 ohm-centimeters, measured at 23° C. according to ASTM D6095,
a paint adhesion rating of 3 B or 4 B or 5 B measured according to ASTM D3359, Method B, and
an unnotched Izod impact strength of 150 to 250 Joules/meter, measured at 23° C. according to ASTM D256.
10. The injection molded article of claim 8 , wherein the weight ratio of electrically conductive carbon black to poly(arylene sulfide) is 0.048 to 0.07.
11. The injection molded article of claim 8 , wherein the electrically conductive carbon black has a BET surface area of at least 1,000 meter 2 /gram.
12. The injection molded article of claim 8 , wherein the composition further comprises 0.2 to 5 weight percent of a compatibilizer for the poly(arylene ether) and the poly(arylene sulfide).
13. The injection molded article of claim 12 , wherein the compatibilizer is citric acid.
14. The injection molded article of claim 8 , wherein the composition further comprises 2 to 5 weight percent of a processing aid that is a liquid at 25° C. and one atmosphere and that is selected from the group consisting of triaryl phosphates, polyolefins, polytetrafluoroethylenes, mineral oil, and mixtures thereof.
15. The injection molded article of claim 8 , wherein the composition is free of a compatibilizing agent for the poly(arylene ether) and the poly(arylene sulfide).
16. The injection molded article of claim 8 , comprising a continuous phase comprising the poly(arylene sulfide) and a dispersed phase comprising the poly(arylene ether); wherein the dispersed phase has an equivalent circular diameter of 2 to 10 micrometers.
17. The injection molded article of claim 8 , further comprising a paint layer in contact with a surface of the product of injection molding.
18. The injection molded article of claim 17 , wherein the paint layer is applied to the product of injection molding by electrostatic painting.
19. A painted injection molded article, comprising:
a product of injection molding a composition comprising
8 to 15 weight percent of a poly(arylene ether),
40 to 50 weight percent of a poly(arylene sulfide),
2 to 3 weight percent of an electrically conductive carbon black, and
35 to 45 weight percent of glass fibers;
wherein all weight percents are based on the total weight of the composition; wherein the weight ratio of electrically conductive carbon black to poly(arylene sulfide) is 0.048 to 0.07; and wherein the composition exhibits
a volume resistivity of 100 to 100,000 ohm-centimeters, measured at 23° C. according to ASTM D6095,
a paint adhesion rating of 3 B or 4 B or 5 B measured according to ASTM D3359, Method B, and
an unnotched Izod impact strength of 150 to 250 Joules/meter, measured at 23° C. according to ASTM D256; and
a paint layer in contact with a surface of the product of injection molding;
wherein the paint layer is applied to the product of injection molding by electrostatic painting.
20. The painted injection molded article of claim 19 , wherein the composition further comprises 2 to 5 weight percent of a processing aid that is a liquid at 25° C. and one atmosphere and that is selected from the group consisting of triaryl phosphates, polyolefins, polytetrafluoroethylenes, mineral oil, and mixtures thereof.
21. The painted injection molded article of claim 19 , wherein the composition is free of a compatibilizing agent for the poly(arylene ether) and the poly(arylene sulfide).