Low bulk density proppant and methods for producing the same
View Patent ↗Materials and methods for making low bulk density proppant capable of providing permeability at subterranean pressures. The low bulk density proppant is made from kaolin clay and at least one of calcined diatomaceous earth and burned kaolin clay.
1. A method for forming a low bulk density proppant comprising:
co-milling raw materials to form substantially round and spherical green pellets, wherein the raw materials comprise water, non-burned kaolin clay and burned kaolin clay, wherein the non-burned kaolin clay consists essentially of kaolin clay that does not include mullite and wherein the burned kaolin clay comprises cristobalite and at least 5 weight percent mullite; and
sintering the pellets to form a proppant having a bulk density of less than about 1.60 g/cc;
wherein the proppant has a short term permeability greater than that of a proppant having a bulk density of less than about 1.60 g/cc made from pellets consisting of water and non-burned kaolin clay.
2. The method of claim 1 wherein the short term permeability of the proppant is 10% to 50% greater than the short term permeability of a proppant having a bulk density less than about 1.60 g/cc made from pellets consisting of water and non-burned kaolin clay.
3. A method for producing a low bulk density proppant comprising:
heating kaolin clay at a temperature above 800° C. sufficient to produce a burned kaolin clay comprising cristobalite and at least 5 weight percent of mullite;
co-milling a non-burned kaolin clay and the burned kaolin clay to form a co-milled mixture, wherein the non-burned kaolin clay consists essentially of kaolin clay that does not include mullite;
forming substantially round and spherical green pellets from the co-milled mixture and water; and
sintering the pellets to form a proppant having a bulk density of less than about 1.60 g/cc; wherein the proppant has a short term permeability greater than that of proppant having a bulk density of less than about 1.60 g/cc made from pellets consisting of water and non-burned kaolin clay.
4. The method of claim 3 wherein the burned kaolin clay comprises at least 50 weight percent of mullite.
5. The method of claim 3 wherein the burned kaolin clay comprises at least 65 weight percent of mullite and at least 15 weight percent of cristobalite.
6. The method of claim 1 wherein the raw materials further comprise calcined diatomaceous earth.